Ru porcelain ecological porcelain clay

An ecological and Ru porcelain technology, applied in the field of ceramic clay, can solve the problem of not meeting the needs of consumers, and achieve the effect of excellent porcelain quality, smooth and soft taste, and sweet taste.

CN106007660BActive Publication Date: 2018-06-19李晓涓 +1
4 Cites 0 Cited by

Patent Information

Authority / Receiving Office
CN · China
Patent Type
Patents(China)
Current Assignee / Owner
Publication Date
2018-06-19

Smart Images

  • Figure 1
    Figure 1
  • Figure 2
    Figure 2
  • Figure 3
    Figure 3
Patent Text Reader

Abstract

Ecological Ru porcelain petuntse is prepared from the following raw materials in parts by weight: 4-8 parts of charcoal dust, 8-12 parts of Fengxue soil, 55-80 parts of Banpo soil, 8-12 parts of kaolin, 4-8 parts of potash feldspar and 0.3-0.6 part of white alkali. The ecological Ru porcelain petuntse is calcined into a porcelain in a reducing atmosphere at the temperature of 1,220-1,225 DEG C, the porcelain quality is excellent, the charcoal dust is combusted and volatilized so that holes are formed in a blank and become crack sources of crackles of a glaze surface, the holes are connected with the crackles of the glaze surface, flow of air between the body and glaze of the Ru porcelain is improved, and peculiar effects of adsorbing smell in Ru porcelain utensil and improving taste are achieved, after tea water and wine are injected in an ecological Ru porcelain tea set and an ecological Ru porcelain wine set, the flavor of the tea water and the flavor of the wine are changed, and the tea water and the wine taste sweet and are smooth and soft. If cigarettes are placed in an ecological Ru porcelain smoke tank, part of harmful odor in the cigarettes can be sucked away after five days, and the cigarettes are not cruel or fierce when a user smokes, and are sweet, smooth and soft. Compared with Ru porcelain made of common pug, the porcelain made of the ecological Ru porcelain petuntse has high health maintenance and collection value.
Need to check novelty before this filing date? Find Prior Art

Description

Technical field:

[0001] The invention relates to a ceramic clay, in particular to a Ru porcelain ecological porcelain clay. Background technique:

[0002] Ru porcelain is a high-end artwork and collection. With the improvement of people's living standards, people's demand for Ru porcelain is becoming more and more diverse. Ru porcelain has become daily-use porcelain, and the quality requirements are getting higher and higher. Some existing products can no longer meet the needs of consumers today. Invention content:

[0003] In order to solve the deficiencies in the above-mentioned background technology, the present invention provides a kind of Ru porcelain ecological porcelain clay.

[0004] The technical solution adopted by the present invention to solve its technical problems:

[0005] A Ru porcelain ecological porcelain clay is made from the following raw materials in parts by weight: 4-8 parts by weight of charcoal powder, 8-12 parts by weight of wind cave soil, 55-8...

Examples

Embodiment Construction

[0018] The present invention can be explained in more detail by the following examples, and the purpose of disclosing the present invention is intended to protect all changes and improvements within the scope of the present invention, and the present invention is not limited to the following examples:

[0019] A Ru porcelain ecological porcelain clay is made from the following raw materials in parts by weight: charcoal powder 5, wind cave soil 10, banpo soil 69.6, kaolin 10, potassium feldspar 5, white alkali 0.4.

[0020] The firing method of Ru porcelain ecological porcelain clay comprises the following steps:

[0021] 1. Preparation: Select wind cave soil, banpo soil and kaolin raw materials that have been weathered for more than five years, and then put them into the wet ball mill together with charcoal powder, potassium feldspar and white alkali. Inside, add water according to the weight ratio of mud raw material: ball: water 1: 1.5: 0.5, and ball mill for 19 hours. When ...