Silane cross-linked polyethylene insulation material for 10 kV and below silver-gray wires and cables, and preparation method thereof

A polyethylene insulation, wire and cable technology, used in insulators, organic insulators, plastic/resin/wax insulators, etc., can solve problems such as large gaps, and achieve high insulation resistance, improved mechanical properties, and good thermal denaturation.

Inactive Publication Date: 2016-11-09
浙江太湖远大新材料股份有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As we all know, in the industry, the temperature grade of 105°C and below can meet the requirements no matter whether XLPE, XLPVC or PVC is used. Above 150°C, the application of silicone rubber, fluoroplastics, polyimide and other varieties has also matured, but in the middle temperature grade (such as 125°C, 150°C) application development, there is a big gap with foreign countries

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Silane cross-linked polyethylene insulation material for 10 kV and below silver-gray wires and cables, and preparation method thereof
  • Silane cross-linked polyethylene insulation material for 10 kV and below silver-gray wires and cables, and preparation method thereof
  • Silane cross-linked polyethylene insulation material for 10 kV and below silver-gray wires and cables, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] Silane cross-linked polyethylene insulating material for 10kV and below silver-gray wire and cable, which is prepared from the following components by weight percentage:

[0044]

[0045]

[0046] The two-step method for preparing silane cross-linked polyethylene insulating materials for 10kV and below silver-gray wires and cables is mainly composed of two parts, one is the preparation of catalyst masterbatch, and the other is the preparation of finished products.

[0047] 1. Preparation of catalyst masterbatch: The catalyst masterbatch accounts for 5% of the total material composition, and the specific formula is as follows:

[0048]

[0049] Stir the above materials in the mixer, first stir at low speed for 1 minute and then at high speed for 3 minutes, then release and pour into the hopper of the extruder (extruder temperature: 140-180°C), extrude through the twin-screw, and then pass through the cooling water tank for cooling , and then blown dry by a fan b...

Embodiment 2

[0059] Silane cross-linked polyethylene insulating material for 10kV and below silver-gray wire and cable, which is prepared from the following components by weight percentage:

[0060]

[0061]

[0062] The insulating material mentioned above was prepared by the two-step method of Example 1.

Embodiment 3

[0064] Silane cross-linked polyethylene insulating material for 10kV and below silver-gray wire and cable, which is prepared from the following components by weight percentage:

[0065]

[0066] A method for preparing silane cross-linked polyethylene insulating materials for 10kV and below silver-gray wires and cables in one step. It mainly consists of two parts, one is the preparation of catalyst masterbatch, and the other is the preparation of finished products.

[0067] 1. Preparation of catalyst masterbatch: The catalyst masterbatch accounts for 5% of the total material composition, and the specific formula is as follows:

[0068]

[0069] Stir the above materials in the mixer, first stir at low speed for 1 minute and then at high speed for 3 minutes, then release and pour into the hopper of the extruder (extruder temperature: 140-180°C), extrude through the twin-screw, and then pass through the cooling water tank for cooling , and then blown dry by a fan before cut...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of insulation materials, in particular to a silane cross-linked polyethylene insulation material for 10 kV and below silver-gray wires and cables, and a preparation method thereof. The insulation material is prepared by the following components: LLDPE-7042, LLDPE-8320, LDPE, EVA, PP, a silane coupling agent, a crosslinking agent DCP, an antioxidant 300, an antioxidant 1010, an antioxidant DLTP, an antioxidant 1024, organic tin, a fluorine rubber master batch, a UV absorber and a silver-gray master batch. The material is mainly used in an insulation layer of the cable to replace the current main PVC materials, and is better than PVC in insulation property, PVC emits toxic and harmful gases when the wires fire due to aging, while the silane insulation material is non-toxic and harmless.

Description

technical field [0001] The invention relates to the field of insulating materials, in particular to a silane crosslinked polyethylene insulating material for 10kV and below silver-gray electric wires and cables and a preparation method thereof. Background technique [0002] The types of polyolefins used in the cable industry mainly include PE, PP, EVA and EEA, etc. Among them, the relatively large amount and long application history are mainly PE, which include HDPE, MDPE, LDPE, LLDPE and cross-linked XLPE. Their application Needless to say. The current application and development trends of polyolefins in the industry mainly focus on the following aspects: [0003] (1) Serialization and perfection of halogen-free and low-smoke materials [0004] Halogen-free, low-smoke, flame-retardant cable materials have been developing rapidly in recent years, and thermoplastic materials that meet the requirements of the IEC92-359 standard have been more and more widely used. With the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/08C08L23/06C08L23/12C08K5/00C08K5/54C08K5/14C08K5/134C08J3/22H01B3/44
CPCC08L23/0815C08J3/226C08J2323/08C08J2423/08C08L2201/08C08L2203/202C08L2205/02C08L2205/025C08L2205/035C08L2207/066C08L2312/08H01B3/441C08L23/06C08L23/0853C08L23/12C08K5/00C08K5/54C08K5/14C08K5/1345
Inventor 赵勇李顺利俞丽琴蔡煜明郑颜
Owner 浙江太湖远大新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More