Titanium dioxide masterbatch and preparation method thereof
A technology of titanium dioxide and color masterbatch, which is applied in the field of plastic coloring, can solve problems such as poor compatibility, and achieve the effects of good compatibility, good dispersibility, and strong coloring ability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0024] The method for preparing titanium dioxide masterbatch provided by the present invention includes the following steps:
[0025] (1) Preparation of raw materials: 20-60% carrier resin, 30-70% titanium dioxide, 1-6% dispersant, and 1-4% antioxidant;
[0026] (2) Mixing: Mix the dispersant and antioxidant evenly in proportion using a high-speed mixer to obtain a mixed powder;
[0027] (3) Extrusion and granulation: the carrier resin, titanium dioxide and the mixed powder obtained in step (2) are mixed according to the proportion through a weightlessness scale using an extruder, and then extruded and granulated. The screw speed of the extruder is 280-300 revolutions per minute, and the temperature of the extruder is set to 200℃-295℃.
[0028] The antioxidant used in the embodiment is a mixture of antioxidant 1010 and antioxidant 168, wherein the weight ratio of antioxidant 1010 to antioxidant 168 is 1:1.
Example Embodiment
[0030] Example 1
[0031] The titanium white pink masterbatch provided by the present invention and the preparation method thereof. The titanium white pink masterbatch comprises the following ingredients: 40% PET carrier resin, 50% rutile titanium dioxide, polyethylene wax 6%, and antioxidant 4% . The preparation method of titanium white pink masterbatch is automatic feeding by weight loss scale according to the proportion, the total feeding amount is 500kg / h, the screw speed of the extruder is 280 revolutions / min, and the temperature of the extruder is set at 220℃-275℃ The extruded strips are water-cooled, dried, pelletized, and packaged to obtain titanium white pink masterbatch.
Example Embodiment
[0032] Example 2
[0033] The titanium white pink masterbatch provided by the present invention and the preparation method thereof. The titanium white masterbatch comprises the following components: 30% PET carrier resin, 60% rutile titanium dioxide, 6% polyethylene wax, and 4% antioxidant. The preparation method of the titanium white pink masterbatch is to automatically cut the material according to the proportion through a weightlessness scale. The total material is 500kg / h, the screw speed of the extruder is 290 rpm, and the temperature of the extruder is set at 220℃-275℃. The discharged strips are water-cooled, dried, pelletized, and packaged to obtain titanium white pink masterbatch.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap