Printing ink for offset lithography and preparation method thereof

A technology of offset printing ink and flat plate, applied in ink, household utensils, applications, etc., can solve the problems of light printing color, pigment dispersion defects, and affecting printing uniformity, and achieve good dispersion, fast drying speed, safety and non-toxicity cost effect

Inactive Publication Date: 2017-06-13
广东绿之彩科技股份有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the daily use of varnishes, there are obvious defects in the dispersibility of pigments, w

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Printing ink for offset lithography and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0019] Example 1

[0020] A flat offset printing ink prepared in parts by weight of the following components: 30 parts of polyurethane, 20 parts of phenolic epoxy acrylate, 4 parts of epoxidized oil propionate, 5 parts of drier, 17 parts of pigment, 1 part of coupling agent, 0.6 part of antioxidant, 1.5 part of dispersant and 6 parts of graphene.

[0021] In this embodiment, the graphene is at least one of spherical, sheet, tubular, fibrous, spiral, and three-dimensional, and its particle size ranges from 0.005 μm to 10,000 μm. The novolac epoxy acrylate is a bisphenol A modified novolac epoxy acrylate. The polyurethane is an epoxy modified waterborne polyurethane hybrid emulsion. The coupling agent is a silane coupling agent or an aluminate coupling agent. The antioxidant is nano-copper / PTFE composite material. The drier is a mixed crystal or solid solution of the reaction product of ligand 3,7-diazabicyclo[3.3.1]nonane and metal chloride. The dispersant is dispersant HY-304....

Example Embodiment

[0023] Example 2

[0024] A flat offset printing ink prepared by weight of the following components: 25 parts of polyurethane, 10 parts of phenolic epoxy acrylate, 6 parts of epoxidized oil propionate, 4 parts of drier, 15 parts of pigment, 3 parts of coupling agent, 0.45 parts of antioxidant, 1 part of dispersant and 8 parts of graphene.

[0025] Furthermore, it is prepared from the following components in parts by weight: 20-30 parts of polyurethane, 20-25 parts of phenolic epoxy acrylate, 5 parts of epoxidized oil propionate, 4 parts of drier, 15-parts of pigment 20 parts, 2-3 parts coupling agent, 0.3-0.6 parts antioxidant, 1-2 parts dispersant, and 7 parts graphene.

[0026] In this embodiment, the graphene is at least one of spherical, sheet, tubular, fibrous, spiral, and three-dimensional, and its particle size ranges from 0.005 μm to 10,000 μm. The novolac epoxy acrylate is a bisphenol A modified novolac epoxy acrylate. The polyurethane is an epoxy modified waterborne poly...

Example Embodiment

[0028] Example 3

[0029] A flat offset printing ink prepared by weight parts of the following components: 20 parts of polyurethane, 30 parts of phenolic epoxy acrylate, 5 parts of epoxidized oil propionate, 3 parts of drier, 20 parts of pigment, 2 parts of coupling agent, 0.3 parts of antioxidant, 2 parts of dispersant and 7 parts of graphene.

[0030] In this embodiment, the graphene is at least one of spherical, sheet, tubular, fibrous, spiral, and three-dimensional, and its particle size ranges from 0.005 μm to 10,000 μm. The novolac epoxy acrylate is a bisphenol A modified novolac epoxy acrylate. The polyurethane is an epoxy modified waterborne polyurethane hybrid emulsion. The coupling agent is a silane coupling agent or an aluminate coupling agent. The antioxidant is nano-copper / PTFE composite material. The drier is a mixed crystal or solid solution of the reaction product of ligand 3,7-diazabicyclo[3.3.1]nonane and metal chloride. The dispersant is dispersant HY-304.

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Login to view more

Abstract

The invention relates to printing ink for offset lithography and a preparation method thereof. The printing ink is prepared from the following components in parts by weight: 20-30 parts of polyurethane, 10-30 parts of phenolic epoxy acrylate, 4-6 parts of epoxidized oil propionate, 3-5 parts of a drier, 15-20 parts of a pigment, 1-3 parts of a coupling reagent, 0.3-0.6 part of an antioxidant, 1-2 parts of a dispersing agent and 6-8 parts of graphene. The printing ink has the characteristics of high tinting strength, good dispersibility, high drying speed, safety and no toxicity and low cost.

Description

technical field [0001] The invention relates to the technical field of packaging, in particular to a flat offset printing ink and a preparation method thereof. Background technique [0002] The manufacture of ink is a complex chemical engineering, and its materials involve chemical changes such as organic polymer synthesis and redox, diazotization, displacement reaction, and complexation reaction. At the same time, it involves mechanics, optics, color science, surface chemistry and other subjects. The first is the manufacture of various pigments and the manufacture of fillers. The second is the manufacture of various synthetic resins and the production of various types of linking materials, dissolving solid resins in vegetable oil, mineral oil, and solvent media. The third is the manufacture of ink. These three processes are interrelated, affect each other, and are indispensable. In the process of offset printing, the quality requirements of the ink are also high, not on...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D11/102C09D11/037
CPCC09D11/037C09D11/102
Inventor 曾家明曾志平吴志雄钟永红
Owner 广东绿之彩科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap