One-way permeable concrete structure and preparation method thereof

A technology of permeable concrete and concrete structure, applied in the field of building materials, can solve the problems of loss of permeable function of permeable structure, impermeability of rainwater, etc., and achieve the effect of improving permeable operation efficiency, increasing urban groundwater resources, and the method is simple and controllable

Active Publication Date: 2019-09-06
惠州富盈新材料科技有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a one-way permeable concrete structure with one-way water permeability, large water permeability coefficient, and high compressive strength and its preparation method, aiming to solve the problem of the existing one-way permeable concrete structure running for a period of time. The permeable function of the permeable structure is lost, and the problem that rainwater cannot penetrate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • One-way permeable concrete structure and preparation method thereof
  • One-way permeable concrete structure and preparation method thereof
  • One-way permeable concrete structure and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0069] And, the embodiment of the present invention also provides a method for preparing the above-mentioned one-way permeable concrete structure, including the following steps:

[0070] Step 1. Weigh each raw material component according to the mixing ratio of the water-permeable filter layer, pre-stir all the aggregates, fibers and 40% by weight of water for 60-90 seconds, then add all the cement, stir for 60-90 seconds, and then Add all the water reducing agent and the remaining 60% by weight of water, fully stir for 90-120 seconds, finally add the hydrophilic polymer, and stir for 30-60 seconds to obtain the concrete mixture of the permeable filter layer;

[0071] Step 2. Calculate the raw material components according to the mixing ratio of the one-way water-permeable layer. First, pre-stir all the aggregate and 40% by weight of water for 60-90 seconds, then add all the cement, stir for 60-90 seconds, and then add The whole water reducer and the remaining 60% by weight of...

Embodiment 1

[0080] A one-way permeable concrete structure, which is composed of a permeable base layer, a one-way permeable layer and a permeable filter layer sequentially combined from bottom to top, wherein the permeable filter layer is made of the first permeable concrete doped with a hydrophilic polymer Made, the aggregate particle size of the first permeable concrete is ≤0.63mm, and the compressive strength of the permeable filter layer is >30 MPa, the permeable hole diameter is 1.2mm / s; The one-way permeable layer is made of the second permeable concrete doped with hydrophobic polymer, and the aggregate particle size of the second permeable concrete is ≤1.25mm, and the compressive strength of the one-way permeable layer is >30 MPa , the aperture of the permeable hole 5mm / s; the permeable base is made of the third permeable concrete, the aggregate particle size of the third permeable concrete is 5-15mm, and the permeable base is resistant to Compressive strength > 40 MPa, permeable h...

Embodiment 2

[0095] A one-way permeable concrete structure, which is composed of a permeable base layer, a one-way permeable layer and a permeable filter layer sequentially combined from bottom to top, wherein the permeable filter layer is made of the first permeable concrete doped with a hydrophilic polymer Made, the aggregate particle size of the first permeable concrete is ≤0.63mm, and the compressive strength of the permeable filter layer is >30 MPa, the permeable hole diameter is 1.2mm / s; The one-way permeable layer is made of the second permeable concrete doped with hydrophobic polymer, and the aggregate particle size of the second permeable concrete is ≤1.25mm, and the compressive strength of the one-way permeable layer is >30 MPa , the aperture of the permeable hole 5mm / s; the permeable base is made of the third permeable concrete, the aggregate particle size of the third permeable concrete is 5-15mm, and the permeable base is resistant to Compressive strength > 40 MPa, permeable h...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a unidirectional permeable concrete structure composed of a permeable base layer, a unidirectional permeable layer and a permeable filtration layer which are sequentially combined from bottom to top. The permeable filtration layer is made of first permeable concrete doped with a hydrophilic polymer, the aggregate size of the first permeable concrete is smaller than or equal to 0.63 mm, the compressive strength of the permeable filtration layer is larger than 30 Mpa, the hole diameter of a permeable hole is smaller than 0.02 mm, and the permeable coefficient is larger than 1.2 mm / s. The unidirectional permeable layer is made of second permeable concrete doped with a hydrophobic polymer, the aggregate size of the second permeable concrete is smaller than or equal to 1.25 mm, the compressive strength of unidirectional permeable layer is larger than 30 Mpa, the hole diameter of a permeable hole is smaller than 0.05 mm, and the permeable coefficient is larger than 5 mm / s. The permeable base layer is made of third permeable concrete, the aggregate size of the third permeable concrete is 5-15 mm, the compressive strength of the permeable base layer is larger than 40 MPa, the hole diameter of a permeable hole is smaller than 1.0 mm, and the permeable coefficient is larger than 10 mm / s.

Description

technical field [0001] The invention belongs to the technical field of building materials, in particular to a one-way permeable concrete structure and a preparation method thereof. Background technique [0002] With the continuous development of urban green ecological development and sponge city construction, the demand for permeable concrete projects is increasing. The existing sidewalk with fully permeable structure includes a base layer and a permeable concrete surface layer sequentially arranged on the roadbed, wherein the permeable concrete surface layer contains permeable holes. However, in the existing permeable pavement, because the permeable holes in the permeable concrete surface are easily blocked by garbage or dust, after a period of operation, the permeable function of the permeable structure will be lost, and rainwater will not be able to penetrate. Various tools are required to clean the permeable concrete pores on the pavement. Even so, it cannot effectively...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): E01C11/22C04B28/00C04B38/00
Inventor 刘福财肖敏黄贺明王贻远张信祯
Owner 惠州富盈新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com