Biocompatible ancient tree hole restoration silicon rubber

A biocompatible and silicone rubber technology, applied in the field of silicone rubber for the repair of ancient tree holes, can solve the problems of poor weather resistance and poor biocompatibility of polyurethane, and achieve the effect of not being easy to crack, promoting wound healing, and good effect

Inactive Publication Date: 2018-01-12
颜健
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It can also be repaired with polyurethane foam, but polyurethane foam has poor weather resistance and poor biocompatibility, which is still not ideal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Biocompatible ancient tree hole restoration silicon rubber

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment

[0018] 1. The preparation of the first component A of the biocompatible old tree hole repair silicone rubber according to the present invention: Weigh the hydroxyl-terminated polydimethylsiloxane with a viscosity (25°C) of 2500 mPa.s 650g, 300g of hydrophobic white carbon black, 50g of polydimethylsiloxane with a viscosity (25°C) of 500mPa.s, mixed evenly with a high-speed disperser, and vacuum defoaming to obtain the first component A.

[0019] 2. A biocompatible old tree hole repair silicone rubber of the present invention, the preparation of the second component A: Weigh 850g of hydroxyl-terminated polydimethylsiloxane with a viscosity (25°C) of 25000 mPa.s, 100g of hydrophobic white carbon black, 100g of polydimethylsiloxane with a viscosity (25°C) of 500mPa.s, mixed evenly with a high-speed disperser, and vacuum defoaming to prepare the second component A.

[0020] 3. A biocompatible old tree hole repair silicone rubber according to the present invention, the preparation ...

Embodiment 1

[0022] Example 1, biocompatible ancient tree hole repair silicone rubber, weighing 90g of the first component A: 10g of the first component B, mixed evenly and degassing.

Embodiment 2

[0023] Example 2, biocompatible old tree hole repair silicone rubber: Weigh out 100 g of the second component A and 20 g of the second component B, and mix them evenly for air defoaming.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses biocompatible ancient tree hole restoration silicon rubber, which is prepared from an ingredient A and an ingredient B, wherein the ingredient A is prepared from 65 to 85 weight percent of hydroxyl-terminated polydimethylsiloxane, 10 to 30 weight percent of white carbon black and 5 to 10 weight percent of polydimethylsiloxane; the ingredient B is prepared from 20 to 40 weight percent of partial hydrolystates of tetramethoxysilane , 5 to 15 weight percent of methyltriacetoxysilane partial hydrolystates, 30 to 40 weight percent of white oil, 1 to 3 weight percent of organic tin, 5 to 15 weight percent of 8-oxine copper and 5 to 15 weight percent of white black carbon. In the use process, the ingredient B is added into the ingredient A to be stirred and mixed accordingto the weight parts of ratio of (8 to 10):(1 to 2). A silicon rubber protection layer is formed in the restoration position; the protection layer can effectively kill and inhibit tree body fungi, moths, white ants and the like; the rain water is prevented from invading into the tree body; the ancient tree wound heeling is promoted; the tree appearance is improved; the life of the ancient tree isprolonged; the growth of the ancient tree is enhanced.

Description

technical field [0001] The invention relates to a silicone rubber for repairing tree holes in ancient trees, in particular, it not only has anti-aging and good biocompatibility, but also has a hydrophobic and rain-proof surface, and can also be mildew-proof, anti-corrosion, and insect-proof. Improve the appearance of trees, prolong the life of old trees, and strengthen the growth of old trees to repair the old tree holes with silicone rubber. technical background [0002] Ancient trees are treasures in forest resources. Existing large trees, especially ancient and famous trees, due to various reasons, the phloem or xylem of ancient trees are injured, and various tree holes are easy to form on the trunks of ancient trees. Carry out anti-corrosion treatment in time. When the wounded part is harmed by bacteria caused by rainwater erosion, tree holes will be formed over time. The tree hole restoration of ancient trees is a technical measure for the protection of ancient trees. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L83/06C08L83/04C08L91/06C08K13/02C08K3/36C08K5/57C08K5/3437C08K5/5415
Inventor 颜健
Owner 颜健
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap