Ink anti-settling agent for identifying and code spraying before steel pipe delivery
An anti-settling agent and marking technology, which is used in the field of steel pipe marking to achieve excellent anti-settling performance, avoid settlement, and promote uniform and stable dispersion.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0020] (1) Preparation of hydrogenated castor oil intercalated zeolite powder: the natural zeolite is crushed by a jet mill and passed through a 100-mesh sieve, and calcined at 500-550° C. to constant weight, and naturally cooled to room temperature to obtain calcined zeolite powder; Add 20g of calcined zeolite powder and 5g of hydrogenated castor oil into 100g of water, and stir to form a slurry. The resulting slurry is treated with microwave reflux for 5 minutes using a microwave processor with a microwave frequency of 2450MHz and an output power of 700W. After stirring for 15 minutes, continue the microwave reflux treatment for 5 minutes, and stir After 15 minutes, microwave reflux treatment for 5 minutes again, and repeat until the viscosity of the obtained slurry does not change, and then send the obtained slurry into a spray dryer, and dry the obtained particles into a micropowder through an ultrafine pulverizer to obtain hydrogenated castor oil intercalation Zeolite powd...
Embodiment 2
[0024] (1) Preparation of hydrogenated castor oil intercalated zeolite powder: the natural zeolite is crushed by a jet mill and passed through a 100-mesh sieve, and calcined at 500-550° C. to constant weight, and naturally cooled to room temperature to obtain calcined zeolite powder; Add 25g of calcined zeolite powder and 8g of hydrogenated castor oil into 100g of water, stir to form a slurry, and use a microwave processor with a microwave frequency of 2450MHz and an output power of 700W to treat the resulting slurry under microwave reflux for 5 minutes. After stirring for 15 minutes, continue the microwave reflux treatment for 5 minutes. After 15 minutes, microwave reflux treatment for 5 minutes again, and repeat until the viscosity of the obtained slurry does not change, and then send the obtained slurry into a spray dryer, and dry the obtained particles into a micropowder through an ultrafine pulverizer to obtain hydrogenated castor oil intercalation Zeolite powder;
[0025...
Embodiment 3
[0039] The anti-sedimentation agents prepared in Examples 1-2 and Comparative Examples 1-3 were prepared into water-based steel pipe inkjet inks according to the ratio of raw materials shown in Table 1, and the performance of the prepared water-based steel pipe inkjet inks was measured, and the results As shown in table 2.
[0040] Table 1 Raw material ratio of water-based steel pipe inkjet ink
[0041] raw material
[0042] Table 2 Performance of water-based steel pipe inkjet ink
[0043] group
[0044] Abrasion test conditions: Use a rubber wheel at 60r / min with a load of 750g at a relative humidity of 50±5% and a temperature of 23±2°C to polish the marks formed after ink curing for 5 minutes.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com