Oxygen candle starting mix and preparation method thereof

A technology for transferring gunpowder and quality, applied in the field of oxygen candles, can solve the problems that the oxidant barium nitrate is easy to absorb moisture and deteriorate, the product cannot be stored for a long time, and the ignition performance is unstable, and achieves the effects of low toxicity, convenient production and processing, and easy ignition

Active Publication Date: 2018-05-29
SHAANXI STAR EXPLOSION SAFETY POLYTRON TECH INC
View PDF8 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the propellants in domestic solid oxygen generators generally use zirconium powder as the main raw material, and barium nitrate or barium peroxide is used as the oxidant. Due to the limitation o

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Oxygen candle starting mix and preparation method thereof
  • Oxygen candle starting mix and preparation method thereof
  • Oxygen candle starting mix and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

5

[0017] Experimental results:

[0018] The developed solid oxygen-making propellant powder is easy to ignite, has a stable reaction, reduces the content of harmful gases, and can ignite an oxygen candle in 2 seconds.

[0019]

[0020]

Embodiment 2

2

[0023] Experimental results:

[0024] The developed solid oxygen-producing powder is easy to ignite, has a stable reaction, reduces the content of harmful gases, and can ignite an oxygen candle in 2.5 seconds.

[0025] detection item

Embodiment 3

[0027]

[0028]

[0029] Experimental results:

[0030] The developed solid oxygen-making propellant powder is easy to ignite, has a stable reaction, reduces the content of harmful gases, and can ignite the oxygen candle in 2.6s.

[0031] detection item

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses oxygen candle starting mix and a preparation method thereof. The oxygen candle starting mix is prepared from the following components in parts by mass: 70-90 parts of barium chromate, 5-15 parts of a metal monomer, 3-10 parts of an adhesive and 0-5 parts of chlorate. The preparation method disclosed by the invention comprises the following step: pressing the barium chromate, the metal monomer, the adhesive and the chlorate according to the formula proportions, thereby obtaining the oxygen candle starting mix. As zirconium powder is replaced by magnesium powder or aluminum powder, magnesium oxide on the surface of the magnesium powder is a catalyst for decomposing chlorate, the decomposition temperature of the chlorate is reduced, harmful gas nitrogen oxides generated from detonating caps of actuators can be rapidly combusted and absorbed, and meanwhile combustion residues are loosened without swelling, thus being safe and reliable.

Description

technical field [0001] The invention relates to oxygen candle technology, in particular to a propagating powder for oxygen candles. Background technique [0002] At present, the propellants in domestic solid oxygen generators generally use zirconium powder as the main raw material, and barium nitrate or barium peroxide is used as the oxidant. Barium is easy to absorb moisture and deteriorate, and barium peroxide is easy to decompose, so the product cannot be stored for a long time. Contents of the invention [0003] Aiming at the defects or deficiencies of the prior art, the object of the present invention is to provide a kind of propellant for oxygen candle. [0004] The fire transfer agent for oxygen candle provided by the invention is made of 70-90 parts by mass of barium chromate, 5-15 parts by mass of simple metal, 3-10 parts by mass of binder and 0-5 parts by mass of chlorate . [0005] The elemental metal of the present invention is one or a mixture of two or mor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C01B13/02
CPCC01B13/0218C01B13/02
Inventor 文新国马爱平
Owner SHAANXI STAR EXPLOSION SAFETY POLYTRON TECH INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap