A kind of maintenance method of silk
A silk and maintenance fluid technology, applied in the direction of improved hand-feeling fibers, animal fibers, and light-resistant fibers, etc., can solve the problem of reducing the durability and washability of silk fabrics, affecting the feel and appearance of textiles, and weakening the anti-ultraviolet effect of silk fabrics To achieve the effect of improving light fastness, long performance retention time, improving dry wrinkle recovery angle and wet wrinkle recovery angle
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0037] A maintenance method for silk, comprising the steps of:
[0038] (1) Soak the silk in clean water, soak it at room temperature for 4 minutes, pick it up and hang it in the air until there is no water dripping;
[0039] (2) Soak the silk obtained in step (1) in the maintenance solution, the bath ratio is 1:35, the soaking temperature is 32°C, the soaking time is 25min, and dehydrated. The water content of the silk after dehydration is 45%;
[0040] The maintenance solution is made of the following components in weight percent: 7% anti-wrinkle agent, 1% aluminum sulfate, 4% softener, 1% anti-ultraviolet finishing agent, 0.6% dicumyl hydrogen peroxide, ethyl pyruvate 0.3% ester, 0.4% triethanolamine, 0.4% tartaric acid, 0.3% lemon juice, and the balance is water;
[0041] The preparation method of described anti-wrinkle agent comprises the steps:
[0042] A, get reeling leftovers, use sodium carbonate to carry out degumming;
[0043] B, adding the reeling scraps after deg...
Embodiment 2
[0053] A maintenance method for silk, comprising the steps of:
[0054] (1) Soak the silk in clean water, soak at room temperature for 3 minutes, pick it up and hang it in the air until there is no water dripping;
[0055] (2) Soak the silk obtained in step (1) in the maintenance solution, the bath ratio is 1:30, the soaking temperature is 35° C., the soaking time is 20 minutes, and dehydrated. The water content of the silk after dehydration is 50%;
[0056] The maintenance solution is made of the following components in percentage by weight: 8% anti-wrinkle agent, 0.8% aluminum sulfate, 5% softener, 2.0% anti-ultraviolet finishing agent, 0.5% dicumyl hydrogen peroxide, ethyl pyruvate 0.5% ester, 0.3% triethanolamine, 0.5% tartaric acid, 0.5% lemon juice, and the balance is water;
[0057] The preparation method of described anti-wrinkle agent comprises the steps:
[0058] A, get reeling leftovers, use sodium carbonate to carry out degumming;
[0059] B, adding the silk ree...
Embodiment 3
[0069] A maintenance method for silk, comprising the steps of:
[0070] (1) Soak the silk in clean water, soak at room temperature for 5 minutes, pick it up and hang it in the air until there is no water dripping;
[0071] (2) Soak the silk obtained in step (1) in the maintenance solution, the bath ratio is 1:40, the soaking temperature is 35°C, the soaking time is 30min, and dehydrated. The water content of the silk after dehydration is 40%;
[0072] The maintenance solution is made of the following components in percentage by weight: anti-wrinkle agent 6%, aluminum sulfate 1.2%, softener 3%, anti-ultraviolet finishing agent 3%, dicumyl hydrogen peroxide 0.8%, ethyl pyruvate 0.2% ester, 0.6% triethanolamine, 0.3% tartaric acid, 0.1% lemon juice, and the balance is water;
[0073] The preparation method of described anti-wrinkle agent comprises the steps:
[0074] A, get reeling leftovers, use sodium carbonate to carry out degumming;
[0075] B, adding the silk reeling wast...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com