A kind of 540mpa grade hot-rolled pickled steel plate and its manufacturing method

A hot-rolled pickling and steel plate technology, applied in the field of metal materials, can solve problems such as non-conformance, and achieve the effects of reducing load, refining structure, and improving hardenability

Active Publication Date: 2019-09-20
ANGANG STEEL CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the tensile strength of the steel plate produced by it is up to 475MPa, which does not meet the requirements of high-strength formed auto parts

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of 540mpa grade hot-rolled pickled steel plate and its manufacturing method
  • A kind of 540mpa grade hot-rolled pickled steel plate and its manufacturing method
  • A kind of 540mpa grade hot-rolled pickled steel plate and its manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] The present invention is a 540MPa grade hot-rolled pickled steel plate. The chemical composition of the hot-rolled pickled steel plate is calculated by mass percentage: C 0.15%-0.25%, Si 0.01%-0.06%, Mn 0.80%-1.30%, Al 0.01%-0.06%, and 0.015%-0.050% Nb and / or 0.30%-0.40% Cr, and limit P<0.010%, S<0.005%, and the balance is Fe and unavoidable impurities.

[0026] The final structure of the hot-rolled pickled steel plate is composed of ferrite, pearlite and a small amount of bainite, and its structure composition is 55% to 65% of ferrite, 30% to 40% of pearlite and bainite by volume percentage. Tensile body 5% to 15%, yield strength > 440MPa, tensile strength > 540MPa, longitudinal elongation > 26%.

[0027] The effect of main chemical composition in a kind of 540MPa grade hot-rolled pickled steel plate of the present invention is:

[0028] C: Carbon is the most important solid solution strengthening element in steel, which is the guarantee of steel strength; considering...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a 540MPa grade hot-rolled pickled steel plate and a manufacturing method thereof. The hot-rolled pickled steel plate comprises the following chemical components in percentageby mass: 0.15-0.25% of C, 0.01-0.06% of Si, 0.80-1.30% of Mn, 0.01-0.06% of Al, 0.015-0.050% of Nb, and / or 0.30-0.40% of Cr, less than 0.010% of P, less than 0.005% of S, and the balance Fe and inevitable impurities; and the final structure of the hot-rolled pickled steel plate comprises 55-65% by volume of ferrite, 30-40% by volume of pearlite, and 5-15% by volume of bainite. According to the 540MPa grade hot-rolled pickled steel plate, the components are optimized on the basis of the chemical components of a C-Mn series steel; the technical parameters of the rolling process, the cooling process and the pickling process are controlled, and thus the hot-rolled pickled steel plate of which the yield intensity is 440MPa or more, the tensile strength is at540MPa grade or more, and the longitudinal elongation A is not less than 26% can be obtained.

Description

technical field [0001] The invention relates to the technical field of metal materials, in particular to a 540MPa hot-rolled pickled steel plate suitable for manufacturing auto parts and a manufacturing method thereof. Background technique [0002] In recent years, with the development of the automobile industry, automobile manufacturers have increasingly higher requirements for the individualization of steel materials. Hot-rolled pickled steel plate is made of high-quality hot-rolled steel plate as raw material. After the iron scale is removed by the pickling unit, the surface quality and service performance are intermediate products between hot-rolled steel plate and cold-rolled steel plate. It is part of hot-rolled steel plate and cold-rolled steel plate. An ideal substitute for cold-rolled steel sheets. In the severe situation of the steel market, hot-rolled pickled steel plates have the advantage of better surface quality compared with hot-rolled steel plates. Compared...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/06C22C38/12C22C38/18C22C38/26B21C37/02C21D8/02
Inventor 孙成钱时晓光韩斌董毅张宇刘仁东徐荣杰张建军杨卫管成平
Owner ANGANG STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com