Fabric blended with pearl fiber and polyester fiber and preparation method thereof

A pearl fiber and polyester fiber technology, applied in the field of textile fabrics, can solve the problems of poor wear resistance and easy wrinkling, and achieve the effects of high breaking strength, fast evaporation rate and strong moisture conduction effect.

Inactive Publication Date: 2018-09-04
HAIYAN SHUOCHUANG CLOTHING RES INST
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The object of the present invention is to provide a preparation method of a pearl fiber and polyester fiber blended fabric, the preparation method is simple to operate, suitable for large-scale industrial production, and the prepared fabric overcomes the wrinkling of existing fabrics and is wear-resistant The problem of poor durability, while the fabric has high breaking strength and good hydrophilicity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Embodiment 1: a kind of preparation method of lining:

[0013] 1) Preparation of pearl fiber: take protamine sulfate, nano-pearl powder and polyester chips and mix them in a mass ratio of 2:7:80, then extrude the melt from the spinneret hole of the spinneret at 265° C. Cool in water and solidify into silk to obtain pearl fiber; the prepared fiber has a variety of amino acids contained in nano-pearls, and has the effect of pearl beauty and skin care. When in contact with the skin for a long time, it has the properties of pearl beauty care, clearing fire and detoxification, whitening skin, and at the same time Has anti-ultraviolet effect;

[0014] 2) Preparation of polyester fiber: polyester chips are melt-spun to obtain polyester fiber, wherein the spinning temperature is 280°C, the spinning speed is 900m / min, the stretching temperature is 65°C, and the pre-stretching ratio It is 1.04, the draw ratio of the first pass is 2.8, and the draw ratio of the second pass is 1.0...

Embodiment 2

[0016] Embodiment 2: a kind of preparation method of lining:

[0017] 1) Preparation of pearl fiber: take protamine sulfate, nano-pearl powder and polyester chips and mix them in a mass ratio of 5:12:80, then extrude the melt from the spinneret hole of the spinneret at 275° C. Cool in water and solidify into silk to obtain pearl fiber; the prepared fiber has a variety of amino acids contained in nano-pearls, and has the effect of pearl beauty and skin care. When in contact with the skin for a long time, it has the properties of pearl beauty care, clearing fire and detoxification, whitening skin, and at the same time Has anti-ultraviolet effect;

[0018] 2) Preparation of polyester fiber: melt-spin polyester chips to obtain polyester fiber, wherein the spinning temperature is 290°C, the spinning speed is 1200m / min, the stretching temperature is 75°C, and the pre-stretching ratio It is 1.08, the draw ratio of the first pass is 3.2, and the draw ratio of the second pass is 1.15;...

Embodiment 3

[0020] Embodiment 3: a kind of preparation method of lining:

[0021] 1) Preparation of pearl fiber: take protamine sulfate, nano-pearl powder and polyester chips and mix them in a mass ratio of 3:8:80, then extrude the melt from the spinneret hole of the spinneret at 266° C. Cool in water and solidify into silk to obtain pearl fiber; the prepared fiber has a variety of amino acids contained in nano-pearls, and has the effect of pearl beauty and skin care. When in contact with the skin for a long time, it has the properties of pearl beauty care, clearing fire and detoxification, whitening skin, and at the same time Has anti-ultraviolet effect;

[0022] 2) Preparation of polyester fiber: melt-spin polyester chips to obtain polyester fiber, wherein the spinning temperature is 281°C, the spinning speed is 950m / min, the stretching temperature is 66°C, and the pre-stretching ratio It is 1.05, the draw ratio of the first pass is 2.9, and the draw ratio of the second pass is 1.06; u...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a fabric blended with pearl fiber and polyester fiber, which comprises the preparation of pearl fiber, the preparation of polyester fibers and the preparation of the fabric. The preparation method has the advantages that the preparation method is simple to operate, and is suitable for large-scale industrial production, and the prepared fabric overcomes the problems of easy wrinkling and poor abrasion resistance in the prior art, and meanwhile, the fabric has high anti-breaking strength, strong moisture-conducting effect and high evaporation rateof water molecules.

Description

technical field [0001] The invention relates to the field of textile fabrics, in particular to pearl fiber and polyester fiber blended fabrics and a preparation method thereof. Background technique [0002] With the continuous improvement of material living standards, people's pursuits are also constantly changing. Basic needs such as food and clothing have gradually become a thing of the past, and health and comfort have become the current standard. People put forward higher requirements for the quality of clothing fabrics. Fashionable, healthy, comfortable and casual clothing is more and more favored by consumers, and clothing fabrics are developing in the direction of high-end, diversification and functionalization. Contents of the invention [0003] The object of the present invention is to provide a preparation method of a pearl fiber and polyester fiber blended fabric, the preparation method is simple to operate, suitable for large-scale industrial production, and th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01D5/08D01D5/098D01F1/10D01F6/62D01F6/92D03D15/00D03D15/283D03D15/292D03D15/50
CPCD01D5/08D01D5/098D01F1/10D01F1/106D01F6/62D01F6/92D03D15/00D10B2401/22D10B2331/04
Inventor 王硕
Owner HAIYAN SHUOCHUANG CLOTHING RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com