Glaze gloss wear-resistant glaze formula and preparation technology thereof
A glaze and luster technology, which is applied in the field of glaze formulation and preparation technology for glossy and wear-resistant glaze, can solve the problems of complex production process, lack of luster, high production cost, etc., achieve high artistic and market value, and promote common technology , good gloss effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0015] Embodiment 1: The glaze formula of glossy and wear-resistant glaze, which is prepared from the following raw materials in parts by weight: 50 parts of potassium feldspar, 22 parts of quartz, 10 parts of bovine bone ash, 9 parts of glass, and 8 parts of frit 57 parts of copper ore, 6 parts of iron ore, 4 parts of Ruyao, 4 parts of zinc oxide, 1.5 parts of tin oxide, and 0.8 part of talcum powder.
[0016] The preparation process of the glaze gloss and wear-resistant glaze comprises the following steps:
[0017] S1: Weigh the potassium feldspar, quartz, glass, frit, copper ore, iron ore, Ru medicine, zinc oxide, and tin oxide in the above weight parts, put them into a ball mill and pulverize them, mix them evenly and sieve them to get the mixture powder ;
[0018] S2: Put the mixture powder in S1 in a crucible for smelting. When the mixture powder is melted into a fluid melt, the balls are floated, and the melt flows into the water tank below to quench, so that the melt ...
Embodiment 2
[0023] Embodiment 2: the glaze formula of glossy and wear-resistant glaze, which is prepared from the following raw materials in parts by weight: 40 parts of potassium feldspar, 20 parts of quartz, 8 parts of bovine bone ash, 8 parts of glass, and 7 parts of frit 5 parts of copper ore, 5 parts of iron ore, 3 parts of Ruyao, 3 parts of zinc oxide, 1 part of tin oxide, and 0.5 part of talcum powder.
[0024] The preparation process of the glaze gloss and wear-resistant glaze comprises the following steps:
[0025] S1: Weigh the potassium feldspar, quartz, glass, frit, copper ore, iron ore, Ru medicine, zinc oxide, and tin oxide in the above weight parts, put them into a ball mill and pulverize them, mix them evenly and sieve them to get the mixture powder ;
[0026] S2: Put the mixture powder in S1 in a crucible for smelting. When the mixture powder is melted into a fluid melt, the balls are floated, and the melt flows into the water tank below to quench, so that the melt split...
Embodiment 3
[0031] Embodiment 3: the glaze formula of glaze surface luster wear-resisting, it is prepared by the raw material of following parts by weight: potassium feldspar 55 parts, quartz 25 parts, bovine bone ash 15 parts, glass 10 parts, frit 10 parts 8 parts of copper ore, 8 parts of iron ore, 5 parts of Ruyao, 5 parts of zinc oxide, 2 parts of tin oxide, and 1 part of talcum powder.
[0032] The preparation process of the glaze gloss and wear-resistant glaze comprises the following steps:
[0033] S1: Weigh the potassium feldspar, quartz, glass, frit, copper ore, iron ore, Ru medicine, zinc oxide, and tin oxide in the above weight parts, put them into a ball mill and pulverize them, mix them evenly and sieve them to get the mixture powder ;
[0034] S2: Put the mixture powder in S1 in a crucible for smelting. When the mixture powder is melted into a fluid melt, the balls are floated, and the melt flows into the water tank below to quench, so that the melt splits into brittle and ...
PUM
| Property | Measurement | Unit |
|---|---|---|
| melting point | aaaaa | aaaaa |