Argil and preparation method thereof

A technology of clay and heavy calcium powder, which is applied in the field of clay, can solve the problems of poor plasticity of clay and unfavorable product promotion and use, and achieve the effect of delicate touch, good plasticity and strong crack resistance

Inactive Publication Date: 2018-12-21
得时宝(广州)科技有限公司
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, at present, the plasticity of clay is not good, and the requirements for heating tools and conditions are relatively strict, which is not conducive to the promotion and use of products.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Embodiment 1: A kind of pottery clay and its preparation method are prepared from the following raw materials in weight ratio: heavy calcium powder 40%, epoxy resin 15%, amine curing agent 12%, diluent 1%, lubricant 8%, 24% plasticizer, 1% thixotropic agent, 1% colorant, 2% color powder, 1% color fixing agent, and appropriate amount of water.

[0020] The production process of the heavy calcium: first, calcite, limestone, chalk, and shells are transported from the quarry; then the limestone is roughly crushed with a crusher, and then crushed with a Raymond pendulum mill to obtain fine limestone powder, and finally classified The machine classifies the mill powder, and the heavy calcium powder is 800 mesh for standby.

[0021] The amine curing agent is an aromatic amine curing agent.

[0022] The preparation method of this pottery clay comprises the following steps:

[0023] (1) Mix heavy calcium powder, epoxy resin and plasticizer in proportion and stir evenly, stir f...

Embodiment 2

[0028] Embodiment 2: A kind of pottery clay and its preparation method are prepared from the following raw materials in weight ratio: heavy calcium powder 45%, epoxy resin 20%, amine curing agent 15%, diluent 1.5%, lubricant 9%, 10% plasticizer, 1.5% thixotropic agent, 1.5% colorant, 3% color powder, 1.5% color fixing agent, and appropriate amount of water.

[0029] The production process of the heavy calcium: first, calcite, limestone, chalk, and shells are transported from the quarry; then the limestone is roughly crushed with a crusher, and then crushed with a Raymond pendulum mill to obtain fine limestone powder, and finally classified The machine classifies the mill powder, and the heavy calcium powder is 900 mesh for standby.

[0030] The amine curing agent is an aromatic amine curing agent.

[0031] The preparation method of this pottery clay comprises the following steps:

[0032] (1) Mix heavy calcium powder, epoxy resin and plasticizer in proportion and stir evenly...

Embodiment 3

[0037] Embodiment 3: A kind of pottery clay and its preparation method are prepared from the following raw materials in weight ratio: heavy calcium powder 50%, epoxy resin 25%, amine curing agent 18%, diluent 3%, lubricant 12%, 30% plasticizer, 3% thixotropic agent, 3% colorant, 4% color powder, 3% color fixing agent, and appropriate amount of water.

[0038] The production process of the heavy calcium: first, calcite, limestone, chalk, and shells are transported from the quarry; then the limestone is roughly crushed with a crusher, and then crushed with a Raymond pendulum mill to obtain fine limestone powder, and finally classified The machine classifies the mill powder, and the heavy calcium powder is 1000 mesh for standby.

[0039] The amine curing agent is an aromatic amine curing agent.

[0040] The preparation method of this pottery clay comprises the following steps:

[0041] (1) Mix heavy calcium powder, epoxy resin and plasticizer in proportion and stir evenly, stir...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides argil and a preparation method thereof. The argil is prepared through the following raw materials in parts by weight: 40-50% of triple superphosphate powder, 15-25% of epoxy resin, 12-18% of an amine curing agent, 1-3% of a diluent, 6-12% of a lubricating agent, 20-30% of a plasticizer, 1-3% of a thixotropic agent, 1-3% of a coloring agent, 2-4% of pigment powder, 1-3% of acolor fixing agent, and a proper amount of water. The argil is simple to prepare; the color is vivid and long lasting; the argil can be stored for a long term and cannot be changed with time, water and fire.

Description

technical field [0001] The invention relates to the field of clay, in particular to a clay and a preparation method thereof. Background technique [0002] Clay is a kind of aggregated clay. This material is rich in color and has good flexibility. It is a handicraft creation material that combines the characteristics of clay, paper clay, sculpture clay, and plasticine. This material has a wide audience. After being sculpted by hand, creatively produced, and heated at high temperature, it can become exquisite ornaments and handicrafts with bright colors, ever-changing patterns, and as hard as pottery. [0003] However, at present, the plasticity of clay is not good, and the requirements for heating tools and conditions are relatively strict, which is not conducive to the promotion and use of products. Therefore, using my country's abundant clay raw material resources to develop a kind of clay with good plasticity, bright and long-lasting color, which can be heated and formed ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/14C04B111/82
CPCC04B26/14C04B2111/82C04B14/28C04B24/121C04B2103/54
Inventor 吴志章吴振章吴永曜吴永滔
Owner 得时宝(广州)科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap