Low-smell composition of automobile seat electric slide rail lubricating grease and preparation method thereof

A car seat and composition technology, applied in the field of lubricating grease, can solve the problems of VOC, slow lifting speed, excessive content of toxic and harmful substances, etc., and achieve good antirust performance, good long life, and excellent high and low temperature resistance.

Inactive Publication Date: 2018-12-21
CHINA PETROLEUM & CHEM CORP
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are the following problems: 1. Noise problems occur during the operation of the electric slide rail of the car seat; In a low temperature environment (-25°C to -40°C), the liftin

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-smell composition of automobile seat electric slide rail lubricating grease and preparation method thereof
  • Low-smell composition of automobile seat electric slide rail lubricating grease and preparation method thereof
  • Low-smell composition of automobile seat electric slide rail lubricating grease and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0035] Example 1

[0036] Base oil 60%,

[0037] Thickener 40%,

[0038] According to the total amount of the above two components, add the following additives by mass percentage:

[0039] Structure improver 0.5%,

[0040] Antioxidant 0.5%,

[0041] Anti-rust agent 0.5%;

[0042] Add 1200g of poly-a-olefin synthetic oil, 160g of dodecanoic acid and 10g of glycerin into the reactor, turn on the stirring, heat to 85°C, add 22.2g of lithium hydroxide aqueous solution, and react for 120 minutes under these conditions; the reaction is over Afterwards, add 640g of polytetrafluoroethylene, heat to 160°C for a second reaction, the reaction time is controlled at 30 minutes; after the reaction, the temperature is raised to 202°C, the temperature is kept at a constant temperature for 2 minutes and then cooled naturally, so that the material temperature is controlled at 165°C In between, the temperature is kept constant for 30 minutes; after the constant temperature is over, the heat medium is stop...

Example Embodiment

[0046] Example 2

[0047] Base oil 65%,

[0048] Thickener 35%,

[0049] According to the total amount of the above two components, add the following additives by mass percentage:

[0050] Structure improver 0.5%,

[0051] Antioxidant 0.5%,

[0052] Anti-rust agent 0.5%;

[0053] Add 1300g poly-a-olefin synthetic oil, 140g dodecahydroxystearic acid and 10g glycerin into the reactor, turn on the stirring, heat to 85°C, add 20g lithium hydroxide aqueous solution, and react for 120 minutes under these conditions; after the reaction is complete , Add 560g polytetrafluoroethylene, heat to 160°C for a second reaction, the reaction time is controlled at 30 minutes; after the reaction is over, the temperature is raised to 202°C, the temperature is kept at a constant temperature for 2 minutes and then naturally cooled, so that the material temperature is controlled at 165°C At the end of the constant temperature for 30 minutes; after the end of the constant temperature, stop the heating medium, ...

Example Embodiment

[0057] Example 3

[0058] Base oil 62%,

[0059] Thickener 38%,

[0060] According to the total amount of the above two components, add the following additives by mass percentage:

[0061] Structure improver 0.5%,

[0062] Antioxidant 0.5%,

[0063] Anti-rust agent 0.5%;

[0064] Add 1240g of poly-a-olefin synthetic oil, 152g of dodecanoic acid and 10g of glycerin into the reaction kettle, turn on the stirring, heat to 85°C, add 21g of lithium hydroxide aqueous solution, and react under these conditions for 120 minutes; after the reaction is complete , Add 608g polytetrafluoroethylene, heat to 160℃ for secondary reaction, the reaction time is controlled at 30 minutes; after the reaction is over, raise the temperature to 202℃, keep it at a constant temperature for 2 minutes and then cool naturally, so that the material temperature is controlled at 165℃ At the end of the constant temperature for 30 minutes; after the end of the constant temperature, stop the heating medium, naturally cool...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a low-smell composition of automobile seat electric sliderail lubricating grease and a preparation method thereof. The composition comprises the raw materials in percentage byweight: 60-65% of basic oil, 35-40% of a densifier, 0.5% of a structure modifier, 0.5% of an antioxidant and 0.5% of an antirust agent. The prepared environment-friendly automobile seat electric seatsliderail lubricating grease can effectively solve the problems that the noise generated by the slide rail in the operation process is high, the slide rail operates slowly at the low temperature, theoriginal equipment manufacturer smell and toxic and harmful substances exceed the standard by strictly controlling the variety selection of raw materials in the original formula of the product, the investigation of the adding amount and the technology in the preparation process. The lubricating grease has the excellent high and low temperature resistance, mechanical stability, colloid stability,the good antirust performance and long service life, meanwhile meets the environment-friendly and non-toxic requirements, and belongs to the low-smell lubricating material.

Description

technical field [0001] The invention relates to the technical field of lubricating grease, in particular to the lubricating grease for an electric slide rail of an automobile seat and a preparation method thereof. Background technique [0002] With the rapid development of my country's automobile industry, the demand for automobiles has changed from first-time purchase to renewal. Automobiles no longer exist only as means of transportation. People have given automobiles more expectations and requirements: safety, environmental protection, energy saving, space Spacious and comfortable etc. The car seat is no longer a simple seat, such as adding electric heating function, automatic massage function, etc., reflecting people's pursuit of a higher quality of life. In the future, the car seat slide rail will develop in the direction of light weight, high strength, integration and platformization. Structures will also continue to be generated and applied. While constantly pursuin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C10M169/00C10M177/00C10N50/10C10N30/08C10N30/12
CPCC10M169/00C10M177/00C10M2205/0206C10M2207/026C10M2207/1285C10M2207/282C10M2213/0626C10N2010/02C10N2030/08C10N2030/12C10N2050/10C10N2030/76
Inventor 曾俊张军张广辽孙毅吴宝杰
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap