Wide and thin specification NM450 wear-resistant steel plate and fabrication method
A manufacturing method and thin gauge technology, applied in the field of metallurgy, can solve the problems of difficulty in meeting large-scale, lightweight and long-life, not wide width, not thin thickness, etc., and achieve good development value and market prospects, good unevenness. , the effect of high wear resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0021] Example 1
[0022] In this embodiment, a wide and thin wear-resistant steel plate with a thickness of 6mm, a width of 2600-3100mm and a Brinell hardness of 450HB is used as an example. The chemical composition and mass percentage are as follows: C: 0.19%, Si: 0.33%, Mn: 1.10%, P : 0.011%, S: 0.0020%, Cr: 0.34%, Ti: 0.015%, B: 0.0016%, the rest is Fe and unavoidable impurities.
[0023] The manufacturing method includes hot metal desulfurization pretreatment-converter smelting-LF + RH refining-continuous casting-billet heating-dephosphorization-rolling-air cooling-flaw detection-shot blasting-quenching-tempering-powerful straightening-cutting-sampling-spraying Print identification-inspection-warehousing.
[0024] The molten steel smelted according to the above ratio is subjected to continuous casting after vacuum degassing treatment. The thickness of the continuous casting billet is 150mm. The billet is heated to a furnace temperature of 1220°C, held for 180 minutes, and then ...
Example Embodiment
[0025] Example 2
[0026] In this embodiment, a wide and thin wear-resistant steel plate with a thickness of 6mm, a width of 2600-3100mm and a Brinell hardness of 450HB is taken as an example. The chemical composition and mass percentage are as follows: C: 0.20%, Si: 0.34%, Mn: 1.08%, P : 0.010%, S: 0.0015%, Cr: 0.35%, Ti: 0.018%, B: 0.0015%, the rest is Fe and unavoidable impurities.
[0027] The manufacturing method includes hot metal desulfurization pretreatment-converter smelting-LF + RH refining-continuous casting-billet heating-dephosphorization-rolling-air cooling-flaw detection-shot blasting-quenching-tempering-powerful straightening-cutting-sampling-spraying Print identification-inspection-warehousing.
[0028] The molten steel smelted according to the above ratio is subjected to continuous casting after vacuum degassing. The thickness of the continuous casting billet is 150mm. The billet is heated to a furnace temperature of 1230°C, kept for 200 minutes, and then rolled ou...
Example Embodiment
[0029] Example 3
[0030] In this embodiment, a wide and thin wear-resistant steel plate with a thickness of 6mm, a width of 2600-3100mm and a Brinell hardness of 450HB is taken as an example. The chemical composition and mass percentage are as follows: C: 0.19%, Si: 0.34%, Mn: 1.09%, P : 0.010%, S: 0.0020%, Cr: 0.33%, Ti: 0.017%, B: 0.0017%, the rest is Fe and unavoidable impurities.
[0031] The manufacturing method includes hot metal desulfurization pretreatment-converter smelting-LF + RH refining-continuous casting-billet heating-dephosphorization-rolling-air cooling-flaw detection-shot blasting-quenching-tempering-powerful straightening-cutting-sampling-spraying Print identification-inspection-warehousing.
[0032] The molten steel smelted according to the above proportion is subjected to continuous casting after vacuum degassing treatment. The thickness of the continuous casting billet is 150mm. The billet is heated to a furnace temperature of 1220°C, held for 190 minutes, and...
PUM
Property | Measurement | Unit |
---|---|---|
Width | aaaaa | aaaaa |
Tensile strength | aaaaa | aaaaa |
Impact energy | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap