Preparation method of porous calcium alginate gel spheres for treating heavy metal sewage

A calcium alginate gel ball and sewage treatment technology, applied in the field of preparation of polymer porous materials, can solve the problems of large pore size uniformity, small specific surface area, affecting the adsorption effect of heavy metal ions, etc., and achieve the effect of improving the adsorption effect

Inactive Publication Date: 2019-02-22
ANQING NORMAL UNIV
View PDF7 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] 4. The calcium alginate pellets currently used for heavy metal sewage treatment are all solid balls with relatively small specific surface area, which affects their adsorption effect on heavy metal ions
Although the preparation of porous ca

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of porous calcium alginate gel spheres for treating heavy metal sewage
  • Preparation method of porous calcium alginate gel spheres for treating heavy metal sewage
  • Preparation method of porous calcium alginate gel spheres for treating heavy metal sewage

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0043] Example 1

[0044] 20g of deionized water and 0.2g of sodium alginate were added to a 100ml beaker and placed on a stirrer to stir for 6 hours to prepare a 1% sodium alginate solution.

[0045] Add 0.05 g of 2% polystyrene microsphere emulsion to the above sodium alginate solution to form a mixed solution with a particle size of about 600 nm, and place the mixed solution on a stirrer and stir for 6 hours.

[0046] The above-mentioned homogeneous mixed solution was added dropwise to 0.2M calcium chloride solution with a dropper, and the formed gel ball was washed with deionized water three times and then placed in a low-temperature refrigerator for 12 hours.

[0047] The frozen samples were put into a vacuum freeze dryer for vacuum freeze-drying for 48 hours. After the completion, the porous calcium alginate gel balls were obtained. The obtained sample is denoted as 2#.

Example Embodiment

[0048] Example 2

[0049] Add 0.1g of 2% polystyrene microsphere emulsion to the 1% sodium alginate solution prepared in Example 1 to form a mixed solution with a particle size of about 600nm, and place the mixed solution on a stirrer to stir 6h.

[0050] The above-mentioned homogeneous mixed solution was added dropwise to 0.2M calcium chloride solution with a dropper, and the formed gel ball was washed with deionized water three times and then placed in a low-temperature refrigerator for 12 hours.

[0051] The frozen samples were put into a vacuum freeze dryer for vacuum freeze-drying for 48 hours. After the completion, the porous calcium alginate gel balls were obtained. The sample obtained is designated as 3#.

Example Embodiment

[0052] Example 3

[0053] To the 1% sodium alginate solution prepared in Example 1, 0.5g of 2% polystyrene microsphere emulsion was added to form a mixed solution with a particle size of about 600nm, and the mixed solution was placed on a stirrer and stirred for 6 hours .

[0054] The above-mentioned homogeneous mixed solution was added dropwise to 0.2M calcium chloride solution with a dropper, and the formed gel ball was washed with deionized water three times and then placed in a low-temperature refrigerator for 12 hours.

[0055] The frozen samples were put into a vacuum freeze dryer for vacuum freeze-drying for 48 hours. After the completion, the porous calcium alginate gel balls were obtained. The sample obtained is designated as 4#.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of porous calcium alginate gel spheres for treating heavy metal sewage. The method comprises the following steps: firstly, preparing a sodium alginate water solution with a certain concentration and adding a micron/nano microsphere solution into the sodium alginate water solution; continuously stirring to sufficiently mix the water solutions; then dropwise adding an obtained mixed solution into a calcium chloride solution to obtain calcium alginate gel spheres containing template microspheres; then washing the obtained gel spheres with water and carrying out vacuum freezing and drying; and finally, putting the obtained gel spheres into an organic reagent and carrying out ultrasonic immersion for a period of time to remove a micron/nano microsphere template, so as to obtain micron/nano porous calcium alginate gel spheres. The porous calcium alginate gel spheres with the pore diameter range of 100nm to 10mu m can be obtained. The specific surface area of the calcium alginate gel spheres is changed through adjusting the pore diameter, so that the exchange speed of ions in an adsorption process is increased and the adsorption effect on heavymetal ions is improved.

Description

technical field [0001] The invention relates to a preparation method of a polymer porous material, in particular to a preparation method of porous calcium alginate composite gel balls with controllable apertures. Background technique [0002] 1. Sodium alginate is a natural and environmentally friendly polymer material, which has the ability to concentrate solutions, form gels, and form films. Because it contains a large number of free carboxyl groups, it is easy to combine with heavy metal ions, so it has a strong chelating effect on heavy metal ions. [0003] 2. Studies have shown that the gel balls formed by sodium alginate and calcium ions (calcium alginate gel balls) have good adsorption capacity for heavy metal ions such as lead, copper, and cadmium, and can be used for the treatment of heavy metal sewage. [0004] 3. For the mechanism of calcium alginate gel ball adsorption of heavy metals, please refer to the attached figure 1 . [0005] 4. The calcium alginate pe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J20/26B01J20/28B01J20/30C02F1/28C02F101/20
CPCB01J20/103B01J20/24B01J20/26B01J20/28019B01J20/28047C02F1/286C02F2101/20
Inventor 董彦杰桑大申白国梁潘林海何承东
Owner ANQING NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap