Oral composition added with bioactive glass and strontium chloride and its application

A bioactive glass and oral composition technology, applied in the field of oral care, can solve the problems of limited effect of tooth restoration, entering the blood, not recommended for pregnant women, etc., to achieve the effect of repairing small defects and resisting tooth hypersensitivity

Active Publication Date: 2021-11-09
YANGZHOU PERFECT DAILY CHEM
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, its safety has always been a hidden concern for consumers: fluoride is a toxic substance, excessive use will cause dental fluorosis, and fluorine will enter the blood, generally not recommended for pregnant women. The repair effect is very limited
[0005] So far, no cases have been found of adding bioactive glass and strontium chloride to oral care cleaning products at the same time, and no synergistic effect between the two has been found

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Oral composition added with bioactive glass and strontium chloride and its application
  • Oral composition added with bioactive glass and strontium chloride and its application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] The embodiments of the technical solutions of the present invention will be described in detail below. The following examples are only used to illustrate the technical solutions of the present invention more clearly, and are therefore only used as examples, and cannot be used to limit the protection scope of the present invention.

[0021] It should be noted that, unless otherwise specified, the technical or scientific terms used in this application should have the usual meanings understood by those skilled in the art to which the present invention belongs.

[0022] The technical solution of the present invention provides an oral composition added with bioactive glass and strontium chloride, and the oral composition has bioactive glass and strontium chloride. Specifically, the contents of the bioactive glass and strontium chloride are both 0.5wt%-15wt%.

[0023] Wherein, the oral composition also includes any number of solvents, humectants, sweeteners, flavors, preserv...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of oral care and provides an oral composition added with bioactive glass and strontium chloride and an application thereof. The oral composition contains bioactive glass and strontium chloride. The bioactive glass used in the present invention has a good repairing effect on slight tooth defects, and strontium chloride has a good anti-allergic effect on tooth allergies, and the two are added to the product at the same time, and the combination of the two will produce synergy. It has the function of resisting tooth sensitivity while repairing minor defects of teeth.

Description

technical field [0001] The invention relates to the technical field of oral care, in particular to an oral composition added with bioactive glass and strontium chloride and application thereof. Background technique [0002] The chemical name of bioactive glass is sodium calcium phosphosilicate, which is a kind of material that can repair, replace and regenerate body tissues, and has the ability to form bonds between tissues and materials. First successfully researched by American scientists, the "bioactive material - bioactive vitreous body, which can repair and bond soft tissue and bone tissue at the same time. Its repair effect on teeth has been documented in many literatures. For example: "Chinese Tissue Engineering" In the paper "Effects of two toothpastes on enamel remineralization and resistance to acid etching at different times after acid etching" in Volume 22, Volume 34, pages 5490-5495, remineralization experiments were performed on isolated teeth, biological activ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61K8/20A61K8/25A61Q11/00A61P1/02
CPCA61K8/20A61K8/25A61Q11/00A61P1/02
Inventor 区志宏
Owner YANGZHOU PERFECT DAILY CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com