Waterborne scroll-steel coating and preparation method thereof

A coiled steel, water-based technology, applied in anti-corrosion coatings, polyester coatings, epoxy resin coatings, etc., can solve the problems of water-based coatings that do not meet the T-bending performance standards, affect the post-processing performance of coils, and achieve excellent post-processing performance. Good weather resistance

Active Publication Date: 2019-03-22
ZHUHAI CBB CHEM
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to solve the problem that the T-bend performance of the water-based coating is not up to the standard, which affects the post-processing performance of the coil, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterborne scroll-steel coating and preparation method thereof
  • Waterborne scroll-steel coating and preparation method thereof
  • Waterborne scroll-steel coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0048] The preparation method of the coating of embodiment 1-6, comprises the following steps:

[0049] (1) Prepare the primer: mix the water, dispersant, and wetting agent in the primer components according to the number of parts, then add epoxy modified acrylic resin, hexamethoxymethylmelamine resin and mix evenly, then add Acid catalysts, pigments, leveling agents, pH regulators, and cosolvents are uniformly mixed to obtain the primer;

[0050] (2) Preparation of topcoat: Mix the water, dispersant, and wetting agent in the topcoat components according to the number of parts, then add polyester modified acrylic resin, hexamethoxymethylmelamine resin and mix evenly, then add Acid catalysts, pigments, leveling agents, pH regulators, and co-solvents are uniformly mixed to prepare the top coat.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a waterborne scroll-steel coating and a preparation method thereof. The waterborne scroll-steel coating is prepared from primer and finish paint, wherein the primer is preparedfrom the following components: water, a dispersant, a wetting agent, epoxy modified acrylic resin, hexamethoxymethyl melamine resin, an acid catalyst, a pigment, a leveling agent, a pH (Potential of Hydrogen) regulator and a co-solvent; the finish paint is prepared from the following components: the water, the dispersant, the wetting agent, polyester modified acrylic resin, the hexamethoxymethyl melamine resin, the acid catalyst, the pigment, the leveling agent, the pH regulator and the co-solvent. The coating provided by the invention has the advantages of high T bending performance, punchingresistance, good post-processing performance, high rigidity, acid and alkali resistance, salt mist resistance, good weather resistance, low VOC (Volatile Organic Compounds), high economic benefits, no toxicity and environment protection.

Description

technical field [0001] The invention belongs to the field of coatings, and in particular relates to a water-based coil coating and a preparation method thereof. Background technique [0002] Coil coatings have been developed since the 1980s. By 2010, the output of coil coatings in my country was 243,300 tons, in 2013 it was 371,800 tons, and in 2015 it was about 480,000 tons. However, these coatings are all oil-based coatings, with a VOC content of about 30%. It is estimated that more than 150,000 tons of VOC (volatile organic compounds) are discharged from coil coatings every year, seriously polluting the environment. So people focus on water-based coil coatings, but due to the water-based process of coil coatings, the flexibility of the coating (that is, the T-bend performance, used to measure the ability of the coating film to resist cracking and damage during the forming process) The project index) is very poor (such as 3T, 4T, and the better performance can only reach 2...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/10C09D167/06C09D5/08C09D7/61C09D7/63C09D7/65
CPCC08K2003/0806C09D5/08C09D7/61C09D7/63C09D7/65C09D163/10C09D167/06C08L61/32C08K3/08
Inventor 胡军余艳锋
Owner ZHUHAI CBB CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com