A method for making a transparent car cover with heat insulation and superhydrophobic functions

A production method, super-hydrophobic technology, applied in the direction of biocide-containing paints, antifouling/underwater coatings, coatings, etc., which can solve the problem of inability to make adjustments to different requirements, the protection film cannot provide heat insulation, the temperature rise in the car, etc. problem, to achieve the effect of low adhesion, long-lasting super-hydrophobic effect, and good aging resistance

Active Publication Date: 2020-11-03
成都德科立高分子材料有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Another disadvantage of membrane materials is that they have a single function and cannot be adjusted for different requirements.
For example, dark car paint is easy to absorb heat, and the temperature inside the car tends to rise when the sun is directly shining. Cooling down and dissipating heat requires a lot of energy consumption, but general protective films cannot provide heat insulation. Cars are also inevitably stained during storage and driving. It takes money and time to wash the car every time, but there is no suitable car cover for such problems on the market

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The present invention provides a transparent car cover with thermal insulation and super-hydrophobic functions. The transparent car cover is prepared by spraying component A and component B on the car paint and drying them respectively. The weight ratio is 4:1. When using, first spray the A component evenly on the car paint and dry it at 25°C. Repeat this spraying and drying for 3 times, then spray the B component. ℃ for 10 minutes to get the finished product; wherein,

[0028] Component A is water-based polyurethane-nano antimony tin oxide composite emulsion;

[0029] Component B is a fluorine-containing silane solution.

[0030] The preparation of the above-mentioned component A water-based polyurethane-nano antimony tin oxide composite emulsion goes through the following steps successively:

[0031] Add 100 parts of polycarbonate diol with a relative molecular mass of 3000 into a sealed dispersion kettle with heating, temperature control and dispersion device, add ...

Embodiment 2

[0037] The present invention provides a transparent car cover with thermal insulation and super-hydrophobic functions. The transparent car cover is prepared by spraying component A and component B on the car paint and drying them respectively. The weight ratio is 100:1. When using, first spray the A component evenly on the car paint and dry it at 70°C. Repeat this spraying and drying for 8 times, then spray the B component, after spraying the B component The finished product is obtained by heating at 150°C for 1 minute; wherein,

[0038] Component A is water-based polyurethane-nano antimony tin oxide composite emulsion;

[0039] Component B is a fluorine-containing silane solution.

[0040] The preparation of the above-mentioned component A water-based polyurethane-nano antimony tin oxide composite emulsion goes through the following steps successively:

[0041] Add 100 parts of polycarbonate diol with a relative mass fraction of 3000 into a sealed dispersion kettle with hea...

Embodiment 3

[0046] The present invention provides a transparent car cover with thermal insulation and super-hydrophobic functions. The transparent car cover is prepared by spraying component A and component B on the car paint and drying them respectively. The weight ratio is 20:1. When using, first spray the A component evenly on the car paint and dry it at 60°C. Repeat this spraying and drying for 4 times, then spray the B component, after spraying the B component The finished product is obtained by heating at 100°C for 3 minutes; wherein,

[0047] Component A is water-based polyurethane-nano antimony tin oxide composite emulsion;

[0048] Component B is a fluorine-containing silane solution.

[0049] The preparation of the above-mentioned component A water-based polyurethane-nano antimony tin oxide composite emulsion goes through the following steps successively:

[0050] Add 100 parts of polycarbonate diol with a relative mass fraction of 2000 into a sealed dispersion kettle with hea...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for making a transparent car cover with heat-insulating and super-hydrophobic functions. The transparent car cover with heat-insulating and super-hydrophobic functions is sprayed and dried on the car paint by component A and component B respectively. And prepared, the weight ratio of A component and B component is 4-100:1; wherein, A component is a water-based polyurethane-nano-tin-antimony composite emulsion, and B component is a fluorine-containing silane solution. When using, first spray component A evenly on the surface of the car paint and dry it, then spray component B and heat at 80-150°C for 1-10 minutes to obtain an invisible car cover with both heat insulation and super-hydrophobic effects.

Description

technical field [0001] The invention relates to the technical field of car paint protection films, in particular to a method for making a transparent car cover with heat insulation and super-hydrophobic functions. Background technique [0002] It is inevitable that vehicles will be scratched and collided during use, which will cause damage to the paint. Long-term exposure to wind and sun will also cause the paint to age and change color. In order to protect the paint and improve the appearance, various invisible car covers have also emerged as the times require. At present, the mainstream invisible car cover in the market is a TPU protective film, such as a kind of automobile protective film disclosed by the patent of CN 206030690U. The process of applying this kind of protective film is cumbersome, time-consuming and labor-intensive, because the bottom layer of the protective film attached to the car paint is generally hot-melt adhesive or pressure-sensitive adhesive, which...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D175/04C09D5/16C09D7/61C09D7/63C08G18/32C08G18/34C08G18/44C08G18/73C08G18/75C08G18/66
CPCC08G18/0823C08G18/0828C08G18/3206C08G18/3212C08G18/3228C08G18/348C08G18/44C08G18/6651C08G18/6659C08G18/73C08G18/755C08G18/758C08K3/2279C08K2003/2231C08K2201/011C09D5/1625C09D5/1687C09D175/04C08K3/22C08K5/5406
Inventor 刘世勇盖静戴江臻
Owner 成都德科立高分子材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products