Sandwich structure of fiber tape toughened honeycomb core

A technology of sandwich structure and honeycomb core, which is applied in the direction of synthetic resin layered products, chemical instruments and methods, and layered products. Compressive strength and shear strength, increase the contact surface core, and improve the effect of bonding strength

Active Publication Date: 2021-05-07
DALIAN UNIV OF TECH +1
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, for the traditional honeycomb core sandwich structure, due to the small contact area of ​​the face-core interface, the surface-core interface of the sandwich structure will still be debonded if only aramid short fiber film is used to toughen the face-core interface.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sandwich structure of fiber tape toughened honeycomb core
  • Sandwich structure of fiber tape toughened honeycomb core
  • Sandwich structure of fiber tape toughened honeycomb core

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0034] Specific example 1: Sandwich panel with carbon fiber tape toughened aluminum honeycomb, its upper and lower skins are made of 6 layers of unidirectional carbon fiber cloth and LY5288 / HY5289 epoxy resin, wherein the 6 layers of carbon fiber cloth are all orthogonal Laying, the skin height (thickness) is 1.2mm; the aluminum honeycomb aperture is 6mm, the hole wall thickness is 0.06mm, and the height is 10mm; the fiber reinforced tape is formed by shearing unidirectional carbon fiber prepreg along the fiber direction, and the width of the carbon fiber tape is about 3mm; Aramid staple fiber film is made of Kevlar49 with an area density of 12g / m 2 , The short fiber length is about 10mm.

[0035] In a Z-shaped unit in which carbon fiber strips are interspersed with aluminum honeycomb cores, the fiber strips cover two honeycomb units on the surface of a core, and the distance between the two fiber strips is one honeycomb unit cell, such as Figure 4 shown.

[0036] The afore...

specific Embodiment 2

[0043] Specific embodiment 2: have the sandwich panel of carbon fiber band toughened aluminum honeycomb, in a Z-shaped unit that carbon fiber band penetrates aluminum honeycomb core body, fiber band covers three honeycomb unit cells on a core body surface, two fiber bands The distance is one honeycomb unit cell. The sandwich panel preparation process and sample size are the same as in Example 1, and the displacement loading rate of the three-point bending test is 2mm / min.

[0044] Figure 8 The load-displacement curves of sandwich beams with or without fiber tape-toughened aluminum honeycomb core are given when the displacement loading rate is 2mm / min, in which the fiber tape-toughened aluminum honeycomb Both the toughened sandwich beam and the non-toughened sandwich beam have 4 samples participating in the test. It can be seen from the figure that the load-displacement curve of the sample toughened with fiber tape is basically above the load-displacement curve of the untoug...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a sandwich structure of fiber tape toughened honeycomb core body, adding aramid short fiber film and fiber tape at the interface between the honeycomb core body and the skin, forming a transition zone in the structure, passing through the bridge of aramid short fiber The joint effect and the connection effect of the fiber tape can improve the surface-core interface contact area and the surface-core bonding strength, and avoid interface debonding and damage of the structure. The test results show that the fiber tape has a crack barrier effect, which can effectively avoid large-area debonding of the face-core interface and ensure the overall performance of the structure. At the same time, the toughened sandwich structure can also improve the local stiffness of the structure and avoid local buckling damage of the structure.

Description

technical field [0001] The invention relates to a sandwich structure of a fiber tape toughened aluminum honeycomb core. The structure can greatly improve the common surface of the sandwich structure on the premise of ensuring light weight and not damaging the mechanical properties of the skin and the core. The core interface is debonded, significantly improving the structural strength and stiffness. Background technique [0002] Carbon fiber sandwich structure is widely used in aerospace, shipbuilding, automobile manufacturing and other fields due to its light weight, high specific strength, high specific modulus, heat and sound insulation, and corrosion resistance. However, the carbon fiber sandwich structure has the problems of poor interface toughness and easy debonding of the face-core interface. At present, the commonly used methods to solve the poor toughness of the interface of the carbon fiber sandwich structure and the easy debonding of the surface-core interface a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B32B3/12B32B3/08B32B27/02B32B27/34B32B15/20B32B15/14B32B15/088B32B9/00B32B9/04B32B27/38B32B27/08B32B27/12B32B33/00
CPCB32B3/08B32B3/12B32B5/02B32B5/26B32B9/045B32B9/047B32B15/088B32B15/14B32B15/20B32B27/08B32B27/12B32B27/38B32B33/00B32B2262/0269B32B2262/106B32B2307/10B32B2307/558B32B2307/714
Inventor 孙直陈红杰石姗姗郭旭
Owner DALIAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap