Preparation method and application of mannitol-modified zero-valent iron nzvim

A mannitol, zero-valent iron technology, applied in chemical instruments and methods, special treatment targets, water/sludge/sewage treatment, etc., can solve the problems of inhibiting reactivity, particle agglomeration and clogging, easy passivation, agglomeration, etc.

Active Publication Date: 2022-04-08
CHINA THREE GORGES UNIV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, in the past, when zero-valent iron was used in underground environments, its mobility was low, and it was prone to particle agglomeration and blockage. In practical applications, it was easy to passivate, agglomerate, and inhibit reactivity.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method and application of mannitol-modified zero-valent iron nzvim
  • Preparation method and application of mannitol-modified zero-valent iron nzvim
  • Preparation method and application of mannitol-modified zero-valent iron nzvim

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Weigh 4.84g FeCl 3 ·6H 2 O powder (17.91 mmol Fe 3+ ) was dissolved in 50mL deionized water, and then the solution was transferred to a three-necked bottle, which was recorded as solution A. Weigh 6.118g of NaBH4 powder (161 mmol BH4-) and dissolve it in 100mL of water, and record it as liquid B. Take liquid B and add it dropwise to solution A at a rate of 15 drops / min, and continue to stir for 20 minutes after the addition is completed. 2 It was carried out under the atmosphere, then vacuum-filtered and washed several times with absolute ethanol to obtain a black solid which was vacuum-dried at 60° C. overnight, and then sealed and stored with nitrogen gas. You can get unmodified nano zero-valent iron NZVI 0 .

Embodiment 2

[0028] Weigh 4.84g FeCl 3 ·6H 2 O powder (17.91 mmol Fe 3+ ) was dissolved in 50 mL of 0.6 mol / L mannitol aqueous solution, which was designated as solution A. Weigh 6.118g NaBH 4 powder (161 mmol BH4 - ) was dissolved in 100mL of water and recorded as liquid B. in N 2Under the atmosphere, take liquid B and add it dropwise to solution A at a rate of 15 drops / min. After the dropwise addition, continue to stir and react for 30 minutes, then vacuum filter and wash several times with absolute ethanol to obtain a black solid and dry it in vacuum at 70°C. , overnight, and sealed after being filled with nitrogen. Mannitol-modified nano zero-valent iron NZVI can be obtained M0.6 .

Embodiment 3

[0030] Weigh 4.84g FeCl 3 ·6H 2 O powder (17.91 mmol Fe 3+ ) was dissolved in 50 mL of 1.0 mol / L mannitol aqueous solution, recorded as solution A. Weigh 6.118g NaBH 4 powder (161 mmol BH4 - ) was dissolved in 100mL of water and recorded as liquid B. in N 2 Under the atmosphere, take liquid B and add it dropwise to solution A at a rate of 15 drops / min. After the dropwise addition, continue to stir and react for 30 minutes, then vacuum filter and wash several times with absolute ethanol to obtain a black solid and dry it in vacuum at 70°C. , overnight, and sealed after being filled with nitrogen. Mannitol-modified nano zero-valent iron NZVI can be obtained M0.6 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a mannitol-modified zero-valent iron NZVI M The preparation method comprises the steps of: FeCl 3 ·6H 2 O powder is dissolved in mannitol aqueous solution, marked as solution A; weigh NaBH 4 Dissolve the powder in water and record it as solution B; under nitrogen, add solution B dropwise to solution A, continue to stir and react for 15-25min after the dropwise addition, then vacuum filter, wash with absolute ethanol, dry in vacuum, and fill with nitrogen Sealed and preserved to obtain mannitol-modified zero-valent iron NZVI Mx , wherein said M is mannitol, x is the molar concentration of mannitol 0.1<x<1.5. Mannitol modified zero-valent iron NZVI of the present invention M It can decompose sulfur-containing or nitrogen-containing azo dye pollutants, heavy metal solutions and natural toxins microcystins in the absence of light.

Description

technical field [0001] The technical field related to the present invention is the technical field of inorganic nanometer materials, in particular relates to zero-valent iron with reductive and highly active network chain structure and its preparation method. Background technique [0002] Nano zero valent iron (NZVI) has attracted widespread attention due to its good reducing properties and effective removal of some pollutants in groundwater or soil. However, due to the weak van der Waals force on the surface, high surface potential energy and magnetism of NZVI, the mobility of unmodified nZVI colloids is low when applied in underground environments, and the poor stability of the colloids makes the particles agglomerate and gels, which is prone to particle formation. Agglomeration and blockage, easy passivation and aggregation in practical applications, inhibit the reactivity of NZVI, thereby reducing its degradation efficiency for pollutants in water. In order to reduce th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22F9/24B82Y40/00C02F1/58C02F1/62C02F1/50C02F101/20C02F101/38C02F101/30
CPCB82Y40/00C02F1/50C02F1/58C02F1/62B22F9/24C02F2303/04C02F2101/38C02F2101/20C02F2101/308
Inventor 方艳芬黄应平付桂荣牛慧斌
Owner CHINA THREE GORGES UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com