Preparation process for polyvinyl alcohol film

A polyvinyl alcohol film and preparation technology, which is applied in the field of composite materials, can solve the problems of limitations in the field of life technology, plastics do not have antibacterial and anti-oxidation, etc., and achieve the improvement of mechanical properties and moisturizing properties, great application value, and wide application prospects Effect

Inactive Publication Date: 2019-06-18
江苏佳凯塑胶制品有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Plastics are widely used in many fields due to their advantages of low price, easy molding, chemical corrosion resistance and easy coloring; but at the same time, plastics themselves do not have antibacterial and anti-oxidation properties, so they are greatly restricted in the field of life technology. therefore needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] The present invention includes polyvinyl alcohol, nanoscale rare earth, ethyl vanillin, Tween 80 and castor oil;

[0018] Follow the steps below:

[0019] 2) Put the polyvinyl alcohol in a water bath at a temperature of 90 to prepare a polyethylene film liquid;

[0020] 2) Mix ethyl vanillin and castor oil evenly for use, and record it as substance A;

[0021] 3) Mix the nanoscale rare earth and Tween 80 evenly for use, and record it as substance B;

[0022] 4) Add substance A to the polyethylene film liquid, mix well and set aside, record as substance C;

[0023] 5) Add substance B to substance C, mix well, and then spread it on a glass plate to prepare a polyvinyl alcohol film.

[0024] In the step 1), the water bath time is 2.2h.

[0025] In the step 2), the mass ratio of ethyl vanillin and castor oil is 1:0.5.

[0026] In the step 3), the mass ratio of nanoscale rare earth to Tween 80 is 1:0.5.

Embodiment 2

[0028] The present invention includes polyvinyl alcohol, nanoscale rare earth, ethyl vanillin, Tween 80 and castor oil;

[0029] Follow the steps below:

[0030] 3) The polyvinyl alcohol is placed in a water bath at a temperature of 92 to prepare a polyethylene film liquid;

[0031] 2) Mix ethyl vanillin and castor oil evenly for use, and record it as substance A;

[0032] 3) Mix the nanoscale rare earth and Tween 80 evenly for use, and record it as substance B;

[0033] 4) Add substance A to the polyethylene film liquid, mix well and set aside, record as substance C;

[0034] 5) Add substance B to substance C, mix well, and then spread it on a glass plate to prepare a polyvinyl alcohol film.

[0035] In the step 1), the water bath time is 2 hours.

[0036] In the step 2), the mass ratio of ethyl vanillin and castor oil is 1:0.4.

[0037] In the step 3), the mass ratio of nanoscale rare earth to Tween 80 is 1:0.6.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation process for a polyvinyl alcohol film. The polyvinyl alcohol film is prepared from polyvinyl alcohol, nano-scale rare earth, ethyl vanillin, Tween 80 and castor oil. The preparation process is carried out according to the following process steps: polyvinyl alcohol is put in a water bath with the temperature of 85-95 to prepare a polyethylene film solution; ethyl vanillin and the castor oil are mixed uniformly to obtain a substance A for standby use; the nano-scale rare earth and Tween 80 are mixed uniformly to obtain a substance B for standby use; the substance A is added to the polyethylene film solution, and the mixture of the substance A and the polyethylene film solution is uniformly mixed to obtain a substance C for standby use; the substance B isadded to the substance C, uniform mixing is performed, and then the mixture of the substance B and the substance C is applied to a glass plate to prepare the polyvinyl alcohol film. The invention provides the polyvinyl alcohol film preparation process which is reasonable in process and provided with suitable aids to improve the antibacterial properties of plastics.

Description

technical field [0001] The invention relates to a preparation process of a polyvinyl alcohol film, which belongs to the technical field of composite materials. Background technique [0002] Plastic is a polymer compound (macromolecules) that is polymerized by addition or polycondensation of monomers, commonly known as plastics or resins. It can freely change its composition and shape. It is composed of synthetic resins and fillers, Plasticizer, stabilizer, lubricant, colorant and other additives. [0003] Plastics are widely used in many fields due to their advantages of low price, easy molding, chemical corrosion resistance and easy coloring; but at the same time, plastics themselves do not have antibacterial and anti-oxidation properties, so they are greatly restricted in the field of life technology. Therefore need to improve. Contents of the invention [0004] The purpose of the present invention is to provide a preparation process of a polyvinyl alcohol film with a ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L29/04C08L91/00C08K3/08C08K5/13C08J5/18
Inventor 张家海
Owner 江苏佳凯塑胶制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com