Complexed shavings and complexed shaving board and manufacture methods thereof

A technology of particleboard and shavings, applied in the field of complexed particleboard and its manufacture, and complexed shavings, can solve the problems of being difficult to superimpose at the same time, difficult to realize the unity of functionalization and individualization, etc. Increase anti-corruption effect

Active Publication Date: 2019-12-20
INST OF WOOD INDUDTRY CHINESE ACAD OF FORESTRY
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In decoration, the pursuit of wood products has undergone a huge change from practicality to individualization and functionality. The existing particleboard processing technology is difficult to achieve the unity of functionality and individualization. For example, increasing the color of parti

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Complexed shavings and complexed shaving board and manufacture methods thereof
  • Complexed shavings and complexed shaving board and manufacture methods thereof
  • Complexed shavings and complexed shaving board and manufacture methods thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] A preparation method of complexed radiata pine shavings, comprising

[0052] Step 1: Prepare an appropriate amount of radiata pine shavings;

[0053] Saw radiata pine into 1000-2000mm wood sections, after peeling, use a planer to plan and form flat shavings; after drying, use airflow sorting to obtain flat shavings, such as figure 1 Shown in (a), belongs to prior art.

[0054] Step 2: introduce plant polyphenols into shavings to obtain polyphenol shavings;

[0055] 21) Dissolving tannin with an average molecular weight of 170 and a polymer of 1 in water, and stirring uniformly to form an aqueous tannin solution with a concentration of 1.0 g / L;

[0056] 22) Immerse the above-mentioned shavings in an aqueous tannin solution under normal pressure, the immersion time is 48 hours, and the immersion temperature is 25°C;

[0057] 23) Dry the shavings impregnated with the aqueous tannin solution.

[0058] Step 3: introducing metal salt into polyphenol shavings to obtain pol...

Embodiment 2

[0066] A preparation method of complexed eucalyptus shavings, comprising

[0067] Step 1: Prepare an appropriate amount of shavings;

[0068] Saw the eucalyptus into 1300mm wood sections, use a rotary cutter to cut into veneers of 1.0mm, form large regular shavings after cutting, and make eucalyptus shavings after drying, such as image 3 (a) shown.

[0069] Step 2: Introduce black wattle bark extract (polyflavanoid plant polyphenols) into shavings to obtain polyphenol shavings;

[0070] 21) Dissolving black wattle bark extract in water and stirring evenly to form an aqueous solution of black wattle bark extract with a concentration of 1 g / L;

[0071] 22) Immerse the above shavings in the black wattle bark extract solution, the immersion pressure is 0.4MPa, the immersion time is 10min, and the immersion temperature is 20°C;

[0072] 23) Dry the shavings impregnated with the aqueous solution of black wattle bark extract.

[0073] Step 3: introducing metal salt into polyphen...

Embodiment 3

[0081] A preparation method for complex poplar wood shavings, comprising

[0082] Step 1: Prepare appropriate amount of poplar wood shavings;

[0083] Poplar or poplar branches are cut into wood chips with a chipper, and then planed into rod-shaped shavings with a double-drum planer, which belongs to the prior art;

[0084] Step 2: import bayberry extract (polygallate plant polyphenol) into shavings to obtain polyphenol shavings;

[0085] 21) Dissolving red bayberry extract in water and stirring evenly to form an aqueous solution of red bayberry extract with a concentration of 3.0 g / L;

[0086] 22) Immerse the above-mentioned shavings in the plant polyphenol aqueous solution under normal pressure, the immersion time is 8 hours, and the immersion temperature is 25°C;

[0087] 23) Drying the shavings impregnated with the aqueous solution of bayberry extract.

[0088] Step 3: introducing metal salt into the shavings of bayberry extract to obtain metal salt shavings of bayberry...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Concentrationaaaaaaaaaa
Densityaaaaaaaaaa
Densityaaaaaaaaaa
Login to view more

Abstract

The invention relates to complexed shavings and a complexed shaving board and manufacture methods thereof, and belongs to the technical field of processing of artificial boards. The complexed shavingboard is composed of the complexed shavings and an adhesive, a plant polyphenol metal salt complex is introduced into the complexed shavings, and metal ions are fixed on the surface of the shavings and in cell walls, cell cavities and/or cell gaps, so that not only can the color of the shaving board be changed effectively, but also the waterproof performance, corrosion resistance, mildew resistance and other properties of the shaving board can be increased.

Description

technical field [0001] The invention relates to the technical field of wood-based board processing, in particular to a complexed particle board, a complexed particle board and a manufacturing method thereof. Background technique [0002] Particleboard, also known as particle board, is made of wood or other wooden materials after shavings are applied, and then glued together under heat and pressure to form a wood composite material. Due to its good physical and mechanical properties and easy processing, it has been widely used in the fields of panel furniture, building structural materials, and decorative materials. With the continuous development of particleboard in the field of home decoration, and people's continuous pursuit of a better life. In decoration, the pursuit of wood products has undergone a huge change from practicality to individualization and functionality. The existing particleboard processing technology is difficult to achieve the unity of functionality and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B27K3/02B27K3/08B27K3/16B27K3/38B27K5/04B27N1/00B27N1/02B27N3/08B27N3/10
CPCB27K3/025B27K3/08B27K3/16B27K3/38B27K5/04B27K2200/15B27N1/00B27N1/0263B27N3/08B27N3/10
Inventor 余养伦于文吉吕斌张耀明
Owner INST OF WOOD INDUDTRY CHINESE ACAD OF FORESTRY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap