Preparation method of antistatic and antibacterial decorative paper
A decorative paper, anti-static technology, applied in the direction of paper, papermaking, paper coating, etc., can solve the problems of poor anti-static performance, poor wear resistance, etc., to improve the degree of bonding, enhance wear resistance, and broad application prospects Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0032] Preparation of homemade nanopowder:
[0033] Put sodium sulfide and zinc acetate into a stirrer with a mass ratio of 1:3 and mix them evenly to prepare a mixed material. Put the mixed material and deionized water into a beaker with a mass ratio of 1:20, and use a stirrer at a speed of 300r / min. Stir at a rotating speed for 30 minutes. After stirring, place the beaker in the liner of the hydrothermal kettle, raise the temperature in the liner to 70°C, oscillate at a constant temperature for 10 hours, and then filter with suction to obtain the reaction solid product;
[0034] Put titanium sulfate and deionized water into a beaker at a mass ratio of 1:10, stir with a stirring device at a speed of 500r / min for 30 minutes to prepare a mixed solution, and add 12% of the mass of the mixed solution to the beaker with a mass fraction of 6% ammoniacal liquor, continue to stir 40min and make mixed slurry, add the reaction solid product of mixed slurry quality 8% in the beaker, mix...
Embodiment 2
[0042] Preparation of homemade nanopowder:
[0043] Put sodium sulfide and zinc acetate into a stirrer with a mass ratio of 1:3 and mix them evenly to prepare a mixed material. Put the mixed material and deionized water into a beaker with a mass ratio of 1:20, and use the stirrer at a speed of 350r / min. Stir at a rotating speed for 35 minutes. After stirring, place the beaker in the liner of the hydrothermal kettle, raise the temperature in the liner to 75°C, oscillate at a constant temperature for 11 hours, and obtain the reaction solid product by suction filtration after oscillation;
[0044] Put titanium sulfate and deionized water into a beaker at a mass ratio of 1:10, stir with a stirring device at a speed of 550r / min for 35 minutes to prepare a mixed solution, and add dropwise to the beaker a mass fraction of 14% of the mixed solution with a mass fraction of 8% ammoniacal liquor, continue to stir for 45min to make mixed slurry, add the reaction solid product of mixed slu...
Embodiment 3
[0052] Preparation of homemade nanopowder:
[0053] Put sodium sulfide and zinc acetate into a stirrer with a mass ratio of 1:3 and mix them evenly to prepare a mixed material. Put the mixed material and deionized water into a beaker with a mass ratio of 1:20, and use a stirrer at a speed of 400r / min. Stir at a rotating speed for 40 minutes. After stirring, place the beaker in the liner of the hydrothermal kettle, raise the temperature in the liner to 80°C, and shake at a constant temperature for 12 hours. After shaking, suction filter to obtain the reaction solid product;
[0054] Put titanium sulfate and deionized water into a beaker at a mass ratio of 1:10, stir with a stirring device at a speed of 600r / min for 40min to obtain a mixed solution, and add dropwise to the beaker a mass fraction of 16% of the mass of the mixed solution to be 10% ammoniacal liquor, continue to stir for 50min to make mixed slurry, add the reaction solid product of mixed slurry quality 12% in the b...
PUM
| Property | Measurement | Unit |
|---|---|---|
| quality score | aaaaa | aaaaa |
| quality score | aaaaa | aaaaa |
| quality score | aaaaa | aaaaa |