A low yield ratio marine steel plate with good welding performance and its manufacturing method
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of welding performance and manufacturing method, which is applied to the low yield ratio marine steel plate and its manufacturing field, can solve the problem of difficult production and can not well guarantee the welding performance, yield ratio performance and oxide shape of the large thickness finished steel plate. , size, distribution and other issues have higher requirements to achieve the effect of high service safety
Active Publication Date: 2021-04-02
ANGANG STEEL CO LTD
View PDF4 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Publication No. CN106574316A discloses that the carbon equivalent of steel plates for large heat input welding is 0.38-0.43, and the rolling process only limits the cumulative reduction below 850°C. This composition process cannot well guarantee the welding performance and yield of large-thickness finished steel plates. Strong specific performance
Publication No. CN104603314A discloses steel plates with excellent toughness in welded heat-affected zones using oxide metallurgy theory to design components. Its disadvantages are that it is quite different from existing processes and has high requirements for the shape, size and distribution of oxides. Production more difficult
The publication number is CN106756543A. The TMCP low-cost high-energy-input welding steel plate disclosed by the patent uses oxide metallurgy to improve the welding performance of the steel plate. The steelmaking and continuous casting process is complicated and difficult to implement. The addition of Nb elements in the steel plate will affect thermomechanical rolling. The effect of grain refinement in the process
The steel for ocean engineering disclosed by the publication number CN106191659A does not fully combine N elements with Ti, V and other elements, and does not make full use of the low-temperature rolling stage to control the structure of the steel plate, and cannot achieve the effect of low yield ratio
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0035] The invention discloses a low yield ratio marine steel plate with good welding performance and a manufacturing method thereof. Those skilled in the art can refer to the content of this article to appropriately improve the process parameters to achieve. In particular, it should be pointed out that all similar replacements and modifications are obvious to those skilled in the art, and they are all considered to be included in the present invention. The method and application of the present invention have been described through preferred embodiments, and the relevant personnel can obviously make changes or appropriate changes and combinations to the method and application described herein without departing from the content, spirit and scope of the present invention to realize and Apply the technology of the present invention.
[0036] 【Example】
[0037] The chemical composition of the steel of the embodiments of the present invention (1~12) is shown in Table 1; the rolli...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
thickness
aaaaa
aaaaa
yield ratio
aaaaa
aaaaa
Login to view more
Abstract
The invention belongs to the field of steel material preparation, and particularly relates to a low-yield-ratio marine steel plate with good welding performance and a manufacturing method thereof. Thelow-yield-ratio marine steel plate comprises the following components of, by weight, 0.05%-0.09% of C, 0.1%-0.4% of Si, 1.0%-1.5% of Mn, less than or equal to 0.02% of P, less than or equal to 0.02%of S, 0.005%-0.03% of Als, 0%-0.6% of Ni, 0%-0.3% of Cu, 0.008%-0.05% of Nb, 0.005%-0.03% of Ti, 0.002%-0.01% of N, 0.02%-0.08% of V, 0%-0.3% of Mo, and the balance Fe and inevitable impurities, wherein the yield ratio of the steel plate is less than or equal to 0.80, the carbon equivalent Ceq is less than or equal to 0.41, and Pcm is less than or equal to 0.21. According to the low-yield-ratio marine steel plate with the good welding performance and the manufacturing method thereof, a certain content of N element is added, and second phase dispersion precipitation of V, Ti element is matched,so that the high-heat input welding performance and the low-temperature impact toughness of the steel plate are improved; and chemical components and the processes of high finish rolling temperature,low water inlet high red returning temperature and low cooling speed are combined, so that the high service safety with the yield ratio being less than or equal to 0.8 can be obtained, and a corresponding production process is formed while the high-service safety steel plate which is easy to weld with high heat input is obtained.
Description
technical field [0001] The invention belongs to the field of iron and steel material preparation, and in particular relates to a low-yield ratio marine steel plate with good welding performance and a manufacturing method thereof. Background technique [0002] With the rapid development of ocean engineering, steel is the main structure of ocean engineering, and its research and development level and production capacity are also constantly improving. The operating environment of marine engineering equipment is generally relatively harsh, so steel for marine engineering should have high comprehensive properties, such as excellent plasticity, low temperature impact toughness and high heat input weldability. At present, steel for marine engineering can meet most of the needs of the marine engineering market, but some high-grade special steels are still unable to be produced stably. Ultra-high-strength steel plates that are resistant to low-temperature impact, high-efficiency, eas...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.