Artificial stone and preparation method thereof

A technology of artificial stone and pyroxene, applied in the field of artificial stone, can solve problems such as uneconomical, unenvironmental protection, and affecting the production and sales requirements of artificial stone, and achieve the effects of cheap price, multiple acquisition channels, and reduced production costs

Pending Publication Date: 2020-06-30
山东天马泰山机械集团有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Aiming at the deficiencies of the prior art, the present invention provides an artificial stone and its preparation method, which has the advantages of economy and environmental protection, and solves the problem that non-renewable resources are directly produced, which is not economical or environmentally friendly, and will seriously affect the production of artificial stone. production and sales requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Artificial stone and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A kind of artificial stone, including potassium feldspar, pyroxene, quartz, synthetic agent, its weight ratio is:

[0030] 40 parts of potassium feldspar, 15 parts of pyroxene, 15 parts of quartz, 2.5 parts of synthetic agent, and the main component of potassium feldspar is SiO 2 、Al 2 o 3 , CaO, Fe 2 o 3 , the main component of pyroxene is Al 2 o 3 , the main component of quartz is SiO 2 .

[0031] Sio 2 The composition is 70%, Al 2 o 3 The composition is 10%, Fe 2 o 3 The composition of the grass is 3%, and the composition of Cao is 1%.

[0032] The synthetic agent is unsaturated resin and acrylic resin, and there are 2 parts of unsaturated resin and 0.5 part of acrylic resin.

[0033] A preparation method of artificial stone, comprising the following steps:

[0034] 1) Potassium feldspar, pyroxene, and quartz are loaded into the silo to achieve the homogenization effect;

[0035] 2) Pour the homogenized filler into a vacuum mixer for vacuum stirring, a...

Embodiment 2

[0043] A kind of artificial stone, including potassium feldspar, pyroxene, quartz, synthetic agent, its weight ratio is:

[0044] 80 parts of potassium feldspar, 25 parts of pyroxene, 25 parts of quartz, 2.5 parts of synthetic agent, and the main component of potassium feldspar is SiO 2 、Al 2 o 3 , CaO, Fe 2 o 3 , the main component of pyroxene is Al 2 o 3 , the main component of quartz is SiO 2 .

[0045] Sio 2 The composition is 74%, Al 2 o 3 The composition is 14%, Fe 2 o 3 The composition of the grass is 4%, and the composition of Cao is 1.5%.

[0046] The synthetic agent is unsaturated resin and acrylic resin, and the unsaturated resin is 2 parts, and the acrylic resin is 0.5 part.

[0047] A preparation method of artificial stone, comprising the following steps:

[0048] 1) Potassium feldspar, pyroxene, and quartz are loaded into the silo to achieve the homogenization effect;

[0049] 2) Pour the homogenized filler into a vacuum mixer for vacuum stirring, ...

Embodiment 3

[0057] A kind of artificial stone, including potassium feldspar, pyroxene, quartz, synthetic agent, its weight ratio is:

[0058] 60 parts of potassium feldspar, 20 parts of pyroxene, 20 parts of quartz, 2.5 parts of synthetic agent, and the main component of potassium feldspar is SiO 2 、Al 2 o 3 , CaO, Fe 2 o 3 , the main component of pyroxene is Al 2 o 3 , the main component of quartz is SiO 2 .

[0059] Sio 2 The composition is 72.68%, Al 2 o 3 The composition is 12.4%, Fe 2 o 3 The composition of Cao is 3.84%, and the composition of Cao is 1.24%.

[0060] The synthetic agent is unsaturated resin and acrylic resin, and there are 2 parts of unsaturated resin and 0.5 part of acrylic resin.

[0061] A preparation method of artificial stone, comprising the following steps:

[0062] 1) Potassium feldspar, pyroxene, and quartz are loaded into the silo to achieve the homogenization effect;

[0063] 2) Pour the homogenized filler into a vacuum mixer for vacuum stirri...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Densityaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of artificial stones, in particular to an artificial stone and a preparation method thereof. The artificial stone comprises, by weight, 40-80 parts of potassium feldspar, 15-25 parts of pyroxene, 15-25 parts of quartz, 2.5 parts of a synthesis agent, wherein the main component of the potassium feldspar is SiO2, Al2O3, CaO and Fe2O3, the main component of the pyroxene is Al2O3, the main component of the quartz is SiO2, and the optimal weight ratio is as follows: 60 parts of the potassium feldspar, 20 parts of the pyroxene, 20 parts of the quartz and2.5 parts of the synthetic agent. According to the artificial stone and the preparation method thereof, the potassium feldspar, the pyroxene and the quartz are used for replacing a quartz stone or glass stone material, the optimal loose specific gravity is tested through multiple times of grain composition, and the specific gravity of the molded artificial stone is infinitely close to the specificgravity of natural granite. Moreover, the raw materials are available in many ways and are convenient and environment-friendly, so that the price of the main filler is lower, the production cost of the artificial granite can be greatly reduced, and environmental protection is facilitated.

Description

technical field [0001] The invention relates to the technical field of artificial stone, in particular to an artificial stone and a preparation method thereof. Background technique [0002] Artificial stone usually refers to artificial stone solid surface material, artificial quartz stone, artificial granite and artificial glass stone, etc. There are many types of artificial stone, and different types of artificial stone have different compositions. [0003] Granite is a kind of structural rock formed by lava from volcanic eruption in a molten state under considerable pressure to the surface of the earth's crust. The magma does not eject out of the ground, but slowly cools and solidifies underground. Acidic igneous rocks belong to igneous rocks (igneous rocks). Granite is mainly composed of quartz, feldspar and mica. [0004] Quartz sand and quartz powder in artificial quartz stone are obtained by crushing minerals through mining, which are non-renewable resources. If they...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B26/06C04B111/54
CPCC04B26/06C04B2111/542C04B24/24C04B14/045C04B14/06C04B14/041
Inventor 袭祥栋
Owner 山东天马泰山机械集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com