Low-earing and low-hardness capacitor shell and preparation method thereof

A technology of shell preparation and low hardness, which is applied in metal rolling and other directions, can solve the problem of high earing rate, achieve low earing rate, improve processing efficiency, and have good plasticity

Inactive Publication Date: 2020-12-25
JIANGSU DINGSHENG NEW MATERIAL JOINT STOCK CO LTD
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, high lug rate has always been a major problem for capacitor shells.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The present invention relates to a high-stretch cable foil and its manufacturing method. Firstly, its composition and mass percentage are controlled as follows: Si≤0.1%, Fe 0.18-0.28%, Cu≤0.03%, Mn≤0.01%, Zn≤0.03% , Ti≤0.03%, the balance is Al.

[0026] According to the above composition control, further obtain the base material of the cable foil finished product, and the specific preparation steps are as follows:

[0027] (1) Smelting: The raw materials are fully stirred evenly during smelting, the smelting temperature is 745°C, the special refining agent is refined at 730°C for 20 minutes, and at 740°C for 20 minutes, and the composition is adjusted to meet the control requirements of the present invention. ℃;

[0028] (2) Casting and rolling: during casting and rolling production, the temperature of the degassing box is controlled at 725°C, the pressure of argon gas is controlled at 0.2Mpa, and the gas flow rate is controlled at 2.0m 3 / h, the rotor speed is contro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of aluminum strip calendering manufacturing, and discloses a low-earing and low-hardness capacitor shell and a preparation method thereof. The low-earing and low-hardness capacitor shell comprises the following components in percentage by mass: 0.1% of Si, 0.18-0.28% of Fe, not greater than 0.03% of Cu, not greater than 0.01% of Mn, not greater than 0.03% of Zn, not greater than 0.03% of Ti, and the balance Al. The process flow comprises such steps as smelting, cast rolling, rough rolling, edge cutting, finish rolling and finished product annealing;and the prepared capacitor shell is 75-85Mpa in tensile strength, can reach the elongation above 30%, is excellent in machining performance, low in strength, excellent in plasticity, high in elongation and low in earing rate, and greatly improves the machining efficiency.

Description

technical field [0001] The invention relates to a capacitor shell with low lug and low hardness and a preparation method thereof, belonging to the technical field of aluminum strip rolling manufacturing. Background technique [0002] Capacitor is a device that holds charge and is an indispensable key component of electronic products. It is widely used in electronic products, computer products, communication products, instrumentation, automation control, optoelectronics and military fields, and its development prospects are very promising. The high ear rate has always been a major problem for capacitor shells. Contents of the invention [0003] The present invention aims to develop a capacitor casing with low lug, low hardness and stable processability. Based on the purpose of the present invention's research on low-ear capacitor housings, the technical solutions provided by the present invention are as follows: [0004] A low-quality low-hardness capacitor shell. The inv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/00C22F1/04C22C1/02C22C1/06B22D11/119B22D11/06B21B1/46B21B3/00
CPCB21B1/463B21B3/00B21B2003/001B22D11/06B22D11/119C22C1/026C22C1/06C22C21/00C22F1/04
Inventor 曾元宦文辉张明成朱江文
Owner JIANGSU DINGSHENG NEW MATERIAL JOINT STOCK CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com