A kind of antibacterial medical glue material and preparation method thereof

A technology of matrix material and propolis, applied in application, medical science, surgery and other directions, can solve the problems of unsatisfactory strength performance and strength performance, and achieve the effect of improving long-term bonding strength and good antibacterial performance.

Active Publication Date: 2022-03-18
FUALIE SCI & TECH DEVING BEIJING
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, although the addition of polylactic acid materials improves the strength of medical adhesive materials to a certain extent, its strength properties, especially long-term strength properties, are not ideal.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of antibacterial medical glue material and preparation method thereof
  • A kind of antibacterial medical glue material and preparation method thereof
  • A kind of antibacterial medical glue material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example 1

[0022] The preparation of preparation example 1α-n-butyl cyanoacrylate

[0023] This preparation example is used for preparing required n-butyl cyanoacrylate, specifically comprises the following steps:

[0024] (1) Butyl ester transesterification reaction

[0025] CNCH 2 COOC 2 h 5 +C 4 h 9 OH—C 2 h 5 ONa→CNCH 2 COOC 4 h 9 +C 2 h 5 Oh

[0026] In a 5L three-necked beaker equipped with a stirrer and a thermometer, put 1400ml of ethyl cyanoacetate and 1200ml of n-butanol, turn on the stirring, condense water, add 25g of sodium ethoxide to 40°C and above; heat up to 100°C and the top temperature reaches 78 Start distilling ethanol at -82°C. When the internal temperature reaches 110°C and the top temperature reaches 98-100°C, stop heating and collect about 680ml of ethanol;

[0027] Cool down to an internal temperature of about 50°C, turn on the heating, change the bottle with the vacuum pump to receive n-butanol, the vacuum degree is -0.1MPa, and change the bottle ...

preparation example 2

[0037] Preparation Example 2 The preparation of n-octyl cyanoacrylate

[0038] This preparation example is used for preparing required n-octyl cyanoacrylate, specifically comprises the following steps:

[0039] (1) with step (1) in the preparation example 1;

[0040] (2) with step (2) in the preparation example 1;

[0041] (3) Synthesis of n-octyl α-cyanoacrylate

[0042]

[0043]Add 380ml of methanol-formaldehyde solution and 0.95ml of piperidine into a 5L three-neck flask equipped with a stirrer, dropping funnel, condenser, and water separator. When the temperature in the bottle reaches 40°C or above, start adding cyanoacetic acid After adding 750ml of octyl esters dropwise, collect methanol until the internal temperature reaches 120°C; then add 300ml of petroleum ether dropwise, start dehydration, and speed up stirring. After the water is finished, collect about 300ml of petroleum ether; when the internal temperature reaches 130°C, add 20g of phosphorus pentoxide and ...

Embodiment 1

[0048] The preparation method of antibacterial medical adhesive material described in the present embodiment, comprises the steps:

[0049] (1) According to the mass ratio of 55wt%: 45wt%, take the above-mentioned n-butyl cyanoacrylate and n-octyl α-cyanoacrylate and fully mix to obtain the alkyl α-cyanoacrylate compound; and according to α- Alkyl cyanoacrylate compound: polylactic acid = 70wt%: 30wt% The ratio is fully mixed to obtain a medical gel matrix, which is set aside;

[0050] (2) Add gum arabic airgel particles accounting for 20wt% of the quality of the medical glue matrix and propolis accounting for 25wt% of the quality of the medical glue matrix to the above-mentioned medical glue matrix, fully stir and mix until the gel state, and obtain the antibacterial matrix material, spare;

[0051] (3) above-mentioned base material is placed in the airtight container that choline chloride ionic liquid (accounting for 15wt% of described base material quality) is housed, gets...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
widthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of biomedical materials, in particular relates to an antibacterial medical adhesive material, and further discloses a preparation method thereof. The antibacterial medical glue material of the present invention uses α-cyanoacrylate alkyl compound and polylactic acid as a mixed medical glue matrix to obtain a better medical glue matrix material, and simultaneously adds propolis as an antibacterial agent to obtain a better Antibacterial performance, and adding airgel particles to improve the long-term bonding performance of the medical adhesive matrix material, and by using CO 2 The supercritical fluid carries the selected ionic liquid to swell and modify the medical adhesive base material, so that the bonding performance of the entire medical adhesive material, especially the long-term bonding strength, is greatly improved, which is more suitable for clinical application.

Description

technical field [0001] The invention belongs to the technical field of biomedical materials, in particular relates to an antibacterial medical adhesive material, and further discloses a preparation method thereof. Background technique [0002] Medical glue refers to the preparation, material or substance that can adhere to the surface or make the surface bond in the medical application. It belongs to the special functional adhesive of biomedicine. It is mainly used for local adhesion and repair of organs or tissues. Traditional suturing, or the combination and positioning of tissues and blood vessels for closure and other technical fields, in addition to the usual bonding and mechanical functions, also has biomedical functions. Compared with traditional methods such as suturing and stapling, the use of medical glue can effectively shorten the operation time and significantly reduce the pain of patients. It is the preferred material for medical operations at present. [0003...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): A61L24/04A61L24/00
CPCA61L24/0094A61L24/0015A61L24/0005A61L2300/30A61L2300/404C08L67/04
Inventor 王威田霞张俊杰张怡婷李俊超李晓芳王占光梁永菡
Owner FUALIE SCI & TECH DEVING BEIJING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap