High-temperature-resistant Nixing pottery teapot and manufacturing method thereof

A technology of Nixing pottery and high temperature resistance, applied in the field of Nixing pottery teapot and its production, can solve the problems of high cost, poor ash falling effect, increased fuelwood consumption, etc., and achieves good plasticity, energy saving, soil quality and so on. Smooth and smooth effect

Pending Publication Date: 2021-09-03
广西道地药食同源文化科技有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, it takes more than two days to burn Nixing pottery with firewood, and the firing temperature must be above 1260°C. Otherwise, the effect of falling ash will be poor, which will greatly increase the consumption of firewood and cause the cost of burning Nixing pottery with firewood. Higher; while the heating rate of electric kiln is easy to control, the highest temperature can be easily reached, and the energy consumption is relatively small
Both firewood kiln and electric kiln have their own advantages and disadvantages, but so far there is no report on the combination of the two to make Nixing pottery.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-temperature-resistant Nixing pottery teapot and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A high-temperature-resistant Nixing pottery teapot is made from natural raw ore mud through the following steps:

[0032] (1) Mechanically activate the natural ore mud with a ball mill, pass through a 500-mesh sieve, and put the mud with a size of less than or equal to 500 mesh in the pond to keep moisture and stale for more than 6 months.

[0033] (2) Awaken and smelt the stale mud for more than 3 days, and use a plastic film to isolate the air and keep water and store the smelted mud for later use.

[0034] (3) Make the blank into the pot body, pot lid and other accessories according to the conventional method, then place the finished blank in a cool place to dry until the water content is 22%, trim the pot body and pot lid, and then use a knife Engraving and depicting patterns or writing characters on the pot.

[0035] (4) Put the obtained pot billet into the kiln, first heat up to 300°C at a heating rate of 19°C per hour to make it lose internal and external moistu...

Embodiment 2

[0044] A high-temperature-resistant Nixing pottery teapot is made by mixing eastern clay and western clay at a weight ratio of 5:5, and is made through the following steps:

[0045] (1) Mix the east mud and west mud in proportion, then mechanically activate them with a ball mill, pass through a 500-mesh sieve, and put the mud with a mesh size less than or equal to 500 mesh in the pond to keep it moist and stale for more than 6 months.

[0046] (2) Awaken and smelt the stale mud for more than 3 days, and use a plastic film to isolate the air and keep water and store the smelted mud for later use.

[0047] (3) Make the blank into the pot body, pot lid and other accessories according to the conventional method, then put the finished blank in a cool place to dry until the water content is 25%, trim the pot body and pot lid, and then use a knife Engraving and depicting patterns or writing characters on the pot.

[0048] (4) Put the obtained pot billet into the kiln, first heat up ...

Embodiment 3

[0057] A high-temperature-resistant Nixing pottery teapot is made by mixing eastern clay and western clay at a weight ratio of 4:6, and is made through the following steps:

[0058] (1) Mix the east mud and west mud in proportion, then mechanically activate them with a ball mill, pass through a 500-mesh sieve, and put the mud with a mesh size less than or equal to 500 mesh in the pond to keep it moist and stale for more than 6 months.

[0059] (2) Awaken and smelt the stale mud for more than 3 days, and use a plastic film to isolate the air and keep water and store the smelted mud for later use.

[0060] (3) Make the blank into a pot body, pot lid and other accessories according to the conventional method, then place the finished blank in a cool place to dry until the water content is 30%, trim the pot body and pot lid, and then use a knife Engraving and depicting patterns or writing characters on the pot.

[0061](4) Put the obtained pot billet into the kiln, first heat up t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
water absorptionaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-temperature-resistant Nixing pottery teapot and a manufacturing method thereof. The teapot is prepared from natural raw ore pug through the steps of grinding and mechanical activation, pug aging, blank preparation, blank forming, blank finishing, blank drying, blank firing, blank polishing and the like, and the obtained Nixing pottery teapot can be heated with open fire; the teapot has good high-temperature-resistant performance and can withstand huge temperature changes, and after being heated to 90 DEG C to 150 DEG C, the teapot can be intact even if the high-temperature-resistant performance is immediately when used for boiling tea, the teapot has the functions of air permeability, no water leakage, water quality activation and the like, and beneficial elements in the Nixing pottery clay can be dissolved in tea soup, so that the beneficial elements can be easily absorbed by a human body; and the effect of melting the tea can be achieved, so that the tea water is better in mouth feel and is more beneficial to body health.

Description

technical field [0001] The invention relates to the technical field of Nixing pottery containers, in particular to a high-temperature-resistant Nixing pottery teapot and a manufacturing method thereof. Background technique [0002] Qinzhou Nixing pottery is a kind of pottery obtained by processing and firing the unique purple red pottery clay on the east and west banks of Qinzhou City, Qinzhou City, Guangxi Zhuang Autonomous Region. Chinese and foreign. According to the history of Nixing pottery, there was no exact name in the middle of the Qing Dynasty. During the Xianfeng period of the Qing Dynasty, Qinzhou pottery developed at its peak, and Nixing pottery was widely used, so it was named "Nixing". Nixing pottery has a wide variety of products, is well-made and has a long history. It is not only an elegant handicraft but also has high practical value, and is deeply loved by collectors at home and abroad. Pure Nixing clay gives people sensory enjoyment because of its "sof...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/04C04B33/13C04B33/32
CPCC04B33/04C04B33/13C04B33/32C04B2235/5436C04B2235/606C04B2235/656C04B2235/6562C04B2235/6567C04B2235/963C04B2235/9607C04B2235/612
Inventor 兰坚毅李覃美
Owner 广西道地药食同源文化科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap