Hydrogen-aluminum metal compound and preparation method thereof

A technology of metal composites and aluminum hydrogen, applied in the production of hydrogen, etc., can solve the problems of complex design of hydrogen preparation methods, and achieve the effect of efficient and safe preparation methods

Inactive Publication Date: 2021-12-07
江苏中靖氢能源科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Hydrogen molecules can enter the crystal lattice of many metals, causing "hydrogen embrittlement", which makes the design of hydrogen production methods more complicated
In the traditional method of producing hydrogen, there are problems such as production efficiency and temperature control

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hydrogen-aluminum metal compound and preparation method thereof
  • Hydrogen-aluminum metal compound and preparation method thereof
  • Hydrogen-aluminum metal compound and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The invention provides a hydrogen-aluminum metal composite, select two groups of 20 parts by weight of aluminum powder, two groups of 2 parts of hydrochloric acid as a trigger, 5 parts by weight of pure water, and the composite also includes 10 parts by weight of carbon powder, 12 parts of organic solvent, 4 parts of solid sodium hydroxide, the concentration of the hydrochloric acid is set to 12mol / L-20mol / L, and the organic solvent can be ethanol.

[0033] Further, in the above technical solution, in the preparation method of the hydrogen-aluminum metal complex, the reactor is first divided into a first reaction zone and a second reaction zone;

[0034] Further, in the above technical scheme, 20 parts by weight of aluminum powder, 10 parts by weight of carbon powder, 12 parts of ethanol and 2 parts of hydrochloric acid with a concentration of 15mol / L are put into the first reaction zone; 20 parts by weight of aluminum Powder, 5 parts by weight of pure water, 4 parts of...

Embodiment 2

[0049] The invention provides a hydrogen-aluminum metal composite. Two groups of 20 parts by weight of aluminum powder, two groups of 1 part of hydrochloric acid are used as a trigger, 3 parts by weight of pure water, and the composite also includes 6 parts by weight of carbon powder. 10 parts of organic solvent, 3 parts of solid sodium hydroxide, the concentration of the hydrochloric acid is set to 12mol / L-20mol / L, and the organic solvent is ethanol.

[0050] Further, in the above technical solution, in the preparation method of the hydrogen-aluminum metal complex, the reactor is first divided into a first reaction zone and a second reaction zone;

[0051] Further, in the above technical scheme, 20 parts by weight of aluminum powder, 6 parts by weight of carbon powder, 10 parts of ethanol and 1 part of hydrochloric acid with a concentration of 12mol / L are put into the first reaction zone; 20 parts by weight of aluminum Powder, 3 parts by weight of pure water, 3 parts of solid...

Embodiment 3

[0066] The invention provides a hydrogen-aluminum metal composite. Two groups of 20 parts by weight of aluminum powder, two groups of 3 parts of hydrochloric acid are used as triggers, 6 parts of pure water by weight, and the composite also includes 12 parts by weight of carbon powder. 15 parts of organic solvent, 5 parts of solid sodium hydroxide, the concentration of the hydrochloric acid is set to 12mol / L-20mol / L, and the organic solvent is ethanol.

[0067] Further, in the above technical solution, in the preparation method of the hydrogen-aluminum metal complex, the reactor is first divided into a first reaction zone and a second reaction zone;

[0068] Further, in the above technical scheme, 20 parts by weight of aluminum powder, 12 parts by weight of carbon powder, 15 parts of ethanol and 1 part of hydrochloric acid with a concentration of 20mol / L are put into the first reaction zone; 20 parts by weight of aluminum powder, 6 parts by weight of pure water, 5 parts of sol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a hydrogen-aluminum metal compound which comprises 20 parts by weight of two groups of aluminum powder, 1-3 parts by weight of hydrochloric acid serving as a triggering agent, 3-6 parts by weight of pure water, 6-12 parts by weight of carbon powder, 10-15 parts by weight of an organic solvent and 3-5 parts by weight of solid sodium hydroxide. The preparation method comprises the following steps: generating aluminum chloride and hydrogen in a first reaction zone, generating sodium metaaluminate in a second reaction zone, and generating aluminum chloride and hydrogen under the action of sodium metaaluminate and hydrochloric acid, and allowing the aluminum chloride in the second reaction zone to enter the first reaction zone, the aluminum chloride in the first reaction zone to be simultaneously dissolved in ethanol to generate a hydrogen-aluminum compound with high stability and to generate a large amount of heat, and releasing a large amount of hydrogen while the heat is absorbed by utilizing a water gas principle of carbon powder in the first reaction zone; and the preparation method is efficient and safe.

Description

technical field [0001] The invention relates to the field of composites for hydrogen. A large amount of hydrogen can be produced simultaneously by preparing a hydrogen-aluminum metal composite, and the invention belongs to the application field of real-time hydrogen production. Background technique [0002] Hydrogen, the chemical formula is H 2 , under normal temperature and pressure, is a highly flammable gas. Colorless, transparent, odorless, tasteless and insoluble gas. Hydrogen is the least dense gas known in the world. The density of hydrogen is only 1 / 14 of that of air, that is, at 1 standard atmospheric pressure and 0°C, the density of hydrogen is 0.089g / L. Therefore, hydrogen can be used as filling gas for airships and hydrogen balloons. Hydrogen is the substance with the smallest relative molecular mass and has strong reducibility. It is often used as a reducing agent to participate in chemical reactions. [0003] In industry, hydrogen is generally produced from...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01B3/08C01B3/06
CPCC01B3/08C01B3/06Y02E60/36
Inventor 王纪忠王靖
Owner 江苏中靖氢能源科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com