Illite mineral compounded quick-heating warm-feeling textile and preparation method thereof

A technology of illite and textiles, which is applied in the field of fast-heating and warming textiles and the preparation of industrialized production of fast-heating and warming textiles. It can solve the problems of excessive emission of greenhouse gases, increase high energy consumption, increase the weight of textiles, etc., and achieve processing capacity. Low energy consumption, reduced energy consumption, and good washing resistance

Active Publication Date: 2022-01-07
CHINA UNIV OF GEOSCIENCES (BEIJING)
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, far-infrared textiles currently on the market generally require external power supply heating, which not only increases the cost, but also takes a short heating time, increases the weight of the textile, and requires frequent charging.
This type of product is derived from active heating products, and the portability is insufficient
Moreover, external power supply heating will also increase the high energy consumption, which will directly lead to excessive emission of greenhouse gases, which is not conducive to the pursuit of reducing carbon emissions.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Illite mineral compounded quick-heating warm-feeling textile and preparation method thereof
  • Illite mineral compounded quick-heating warm-feeling textile and preparation method thereof
  • Illite mineral compounded quick-heating warm-feeling textile and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] An illite mineral-composite fast-heating warm-sensing textile, comprising the following steps:

[0044] (1) Water-based slurry preparation: 20ml of deionized water was used to dissolve the auxiliary agent, including 0.4g of water-resistant dispersant CX003 dispersant and 0.03g of AMP-95 regulator. Then put 20g of illite powder with a particle size of 10 μm and 10g of black tourmaline powder with a particle size of 10 μm, 5g of SiO 2 , 5g ZrO 2 Powder with a particle size of 30nm, then stir evenly;

[0045] (2) Printing slurry preparation: add SHW binder accounting for 60g of printing slurry and 100g thickener accounting for printing slurry in turn, stir evenly;

[0046] (3) Printing and dyeing: the post-processing parameters of the pure fiber cloth are set as follows: the magnetic force is 5V, and the speed is 22m / min. Dry in an oven at 80°C after printing and dyeing. After drying, carry out secondary printing and dyeing and then dry, and finally obtain illite compo...

Embodiment 2

[0048] An illite mineral-composite fast-heating warm-sensing textile, comprising the following steps:

[0049] (1) Water-based slurry preparation: 30ml of deionized water was used to dissolve the aid, including 0.4g of water-resistant dispersant CX003 dispersant and 0.03g of AMP-95 regulator. Then put 20g of illite powder with a particle size of 10 μm and 10g of black tourmaline powder with a particle size of 10 μm, 5g of SiO 2 , 5g ZrO 2 Powder with a particle size of 30nm, then stir evenly;

[0050] (2) Preparation of printing paste: add 50g of SHW binder and 100g of thickener in printing paste in sequence, and stir evenly;

[0051] (3) Printing and dyeing: the post-processing parameters of the pure fiber cloth are set as follows: the magnetic force is 5V, and the speed is 22m / min. Dry in an oven at 80°C after printing and dyeing. After drying, carry out secondary printing and dyeing and then dry, and finally obtain illite compound warm feeling health care printed textil...

Embodiment 3

[0053] An illite mineral-composite fast-heating warm-sensing textile, comprising the following steps:

[0054] (1) Water-based slurry preparation: 30ml of deionized water was used to dissolve the aid, including 0.4g of water-resistant dispersant CX003 dispersant and 0.03g of AMP-95 regulator. Then put 20g of illite powder with a particle size of 10 μm and 5g of black tourmaline powder with a particle size of 10 μm, 5g of SiO 2 , 5g ZrO 2 Powder with a particle size of 30nm, then stir evenly;

[0055] (2) Preparation of printing paste: add SHW binder accounting for 50g of printing paste and 100g thickener accounting for printing paste in turn, stir evenly;

[0056] (3) Printing and dyeing: the post-processing parameters of the pure fiber cloth are set as follows: the magnetic force is 5V, and the speed is 22m / min. Dry in an oven at 80°C after printing and dyeing. After drying, carry out secondary printing and dyeing and then dry, and finally obtain illite compound warm feel...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thermal resistanceaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention generally relates to the technical field of functional textiles, in particular to an illite mineral compounded quick-heating warm-feeling textile and a preparation method for industrially producing the quick-heating warm-feeling textile. The invention provides the illite mineral compounded quick-heating warm-feeling textile, which is prepared by taking illite as a main component and taking metal oxide and schorlite as auxiliary components, adding a dispersing agent and a conditioning agent to prepare aqueous slurry, then adding an adhesive and a printing thickening agent to prepare printing slurry, and finally printing and dyeing to obtain the illite mineral compounded quick-heating warm-feeling textile. The whole preparation method is simple and suitable for large-scale industrial production and preparation, large-scale continuous production can be achieved, and the prepared illite mineral compounded quick-heating warm-feeling textile can be directly converted into an actual commercial product by simply spraying patterns in the later period.

Description

technical field [0001] The present invention generally relates to the technical field of functional textiles, in particular to an illite mineral-composited fast-heating and warming textile, and a preparation method for industrially producing the fast-heating and warming textile. Background technique [0002] With the development of society and the continuous improvement of people's quality of life, people's requirements for clothing are no longer shelter from the cold, nor is it just fashionable and beautiful. In addition to basic convenience (easy to wash, quick-drying, no fading, non-ironing, shrink-proof, etc.), comfort (soft fit, moisture absorption, skin-friendly and breathable), people's clothing health care (anti-ultraviolet, antibacterial, etc.) , antistatic, deodorant, insect-proof) also have requirements. [0003] Functional textiles refer to textiles that, in addition to their own basic use value, also have other additional special functions, such as healthy func...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06P1/673D06P1/52D06P1/645
CPCD06P1/67383D06P1/673D06P1/5257D06P1/525D06P1/645
Inventor 张以河高路张国清田娜张磊周博文高彩霞陈宇王兰心李兴娜文洪杰路明磊
Owner CHINA UNIV OF GEOSCIENCES (BEIJING)