Preparation method of novel particle-reinforced 7XXX aluminum alloy thin strip

A particle-enhanced, aluminum alloy technology, applied in the field of particle-enhanced new 7XXX aluminum alloy thin strip preparation, can solve problems such as hindering wide application, and achieve the effects of increasing nucleation, low energy consumption, and hindering the recrystallization process

Active Publication Date: 2022-03-01
BAOSHAN IRON & STEEL CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, there are still many problems in the microstructure of the 7XXX aluminum alloy produced at present, which hinder its wide application, such as grain and precipitation coarsening, thermal cracking, and intermetallic compounds and eutectic phases are usually distributed along grain boundaries, etc., while the microstructure of aluminum alloy largely determines its mechanical properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of novel particle-reinforced 7XXX aluminum alloy thin strip
  • Preparation method of novel particle-reinforced 7XXX aluminum alloy thin strip
  • Preparation method of novel particle-reinforced 7XXX aluminum alloy thin strip

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0078] The present invention will be further described below by embodiment and accompanying drawing, but this is not limitation of the present invention, those skilled in the art can make modification or improvement according to the basic idea of ​​the invention, but as long as not departing from the basic idea of ​​the present invention, all in within the scope of the present invention.

[0079] see figure 1 , Embodiment 1 of the present invention, using a vertical casting machine to prepare particle-reinforced new 7XXX aluminum alloy strips.

[0080]The smelted aluminum alloy liquid conforming to the design of the chemical composition of the present invention is introduced from the smelting furnace 1 through the launder 2 into the resting furnace 3 for standing. The aluminum alloy liquid is transported from the static furnace 3 to the front box 4 through the launder 2, and flows into the tundish 7 after degassing 5 and filtering 6 processes, and the aluminum alloy liquid in...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
widthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of a particle-reinforced novel 7XXX aluminum alloy thin strip, which comprises the following steps of: 1) smelting according to the following chemical components in percentage by weight: 4.8 to 6.3 percent of Zn, 1.6 to 2.5 percent of Mg, 1.6 to 2.5 percent of Cu, 0.1 to 0.15 percent of Zr and the balance of Al and other inevitable impurities; the single impurity content is less than or equal to 0.1%, and the total impurity content is less than or equal to 0.2 (2) nano-particle enhancement; 3) continuous casting; 4) cooling; 5) primary hot rolling; (6) cooling and secondary hot rolling; (7) coiling; and 8) post-processing. According to the preparation method, the 7XXX aluminum alloy thin strip is prepared by combining nanoparticle reinforcement with a double-roller thin strip continuous casting process, and compared with an existing 7XXX aluminum alloy, the strength of the obtained aluminum alloy thin strip is higher than 20%, and the ductility is higher than 30%; and compared with a steel plate, the weight can be easily reduced by more than 40%.

Description

technical field [0001] The invention relates to the field of aluminum alloy preparation, in particular to a method for preparing a particle-reinforced novel 7XXX aluminum alloy strip. Background technique [0002] The thin strip continuous casting technology is a cutting-edge technology in the field of metallurgy today. The twin-roll thin strip continuous casting technology was first proposed by Henry Bessemer in 1865 (US Patent: 49053). Thin strip continuous casting integrates continuous casting, rolling, and even heat treatment into one, so that the produced thin strip can be rolled into an industrial product at one time, which greatly simplifies the production process of aluminum alloy thin strip and shortens the production time. The production cycle makes the aluminum alloy thin strip production process more compact, more continuous, more efficient, and more environmentally friendly; at the same time, the production cost is significantly reduced, and the quality and perf...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/10C22C32/00C22F1/053B22D11/108B22D11/11B22D11/06
CPCC22C21/10C22C32/0047C22C32/0052C22C32/0057C22C32/0063C22C32/0068C22F1/053C22F1/002B22D11/108B22D11/11B22D11/0622B22D11/0651B22D11/0668B22D11/003
Inventor 吴建春支卫军吴军蒋浩民方园
Owner BAOSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products