Antistatic high-cleanliness latex gloves and preparation method thereof

A latex glove and antistatic technology, which is applied in the field of latex gloves, can solve the problems of latex gloves such as easy damage, unfavorable use, and poor antistatic performance, and achieve the effects of good antistatic ability, long service life, and increased viscosity

Pending Publication Date: 2022-03-04
南京瑞润新材料科技有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The latex gloves in the prior art have poor antistatic properties, and at the same time, after a long period of use, the latex gloves are easily damaged and are not conducive to use, so we propose an antistatic high-clean latex glove and its preparation method for solving the questions raised above

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antistatic high-cleanliness latex gloves and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A kind of antistatic high-clean latex gloves and preparation method thereof are proposed in this embodiment, comprising the following raw materials in parts by weight: 70 parts of latex, 22 parts of nitrile, 2 parts of polyvinyl chloride, 20 parts of sulfur, and 15 parts of conductive outer layer , 36 parts of leather material, 12 parts of anti-static PC board, 24 parts of carbon black, 25 parts of mica powder, 8 parts of defoamer, 10 parts of lanolin, 10 parts of accelerator, 10 parts of anti-aging agent, and 6 parts of thickener.

[0028] Its preparation method includes the following steps: firstly, latex, nitrile, polyvinyl chloride, sulfur and leather materials are added into the mixer, stirred at a speed of 20 revolutions per minute for 22 minutes, and the No. 1 mixture is obtained after stirring, and the No. 1 mixture is mixed Put it in the static box and let it stand still, let the No. 1 mixture be placed and mixed, then add the conductive outer layer, anti-static...

Embodiment 2

[0030] A kind of antistatic high-clean latex gloves and preparation method thereof are proposed in this embodiment, comprising the following raw materials in parts by weight: 60 parts of latex, 30 parts of nitrile, 28 parts of polyvinyl chloride, 15 parts of sulfur, and 15 parts of conductive outer layer , 30 parts of leather material, 10 parts of anti-static PC board, 20 parts of carbon black, 20 parts of mica powder, 8 parts of defoamer, 19 parts of lanolin, 17 parts of accelerator, 14 parts of anti-aging agent, and 9 parts of thickener.

[0031]Its preparation method includes the following steps: firstly, latex, nitrile, polyvinyl chloride, sulfur and leather materials are added into the mixer, stirred at a speed of 30 revolutions per minute for 25 minutes, and the No. 1 mixture is obtained after stirring, and the No. 1 mixture is mixed Put it in the static box and let it stand still, let the No. 1 mixture be placed and mixed, then add the conductive outer layer, anti-static...

Embodiment 3

[0033] A kind of antistatic high-clean latex gloves and preparation method thereof are proposed in this example, comprising the following raw materials in parts by weight: 55 parts of latex, 33 parts of nitrile, 21 parts of polyvinyl chloride, 16 parts of sulfur, and 17 parts of conductive outer layer , 31 parts of leather material, 11 parts of anti-static PC board, 36 parts of carbon black, 31 parts of mica powder, 7 parts of defoamer, 12 parts of lanolin, 17 parts of accelerator, 17 parts of anti-aging agent, and 6 parts of thickener.

[0034] Its preparation method includes the following steps: firstly, latex, nitrile, polyvinyl chloride, sulfur and cortical materials are added into the mixer, stirred at a speed of 15 revolutions per minute for 22 minutes, and the No. 1 mixture is obtained after stirring, at this time, the No. 1 mixture Put it in the static box and let it stand still, let the No. 1 mixture be placed and mixed, then add the conductive outer layer, anti-static...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an antistatic high-cleanliness latex glove and a preparation method thereof. The anti-static waterproof coating is prepared from the following raw materials in parts by weight: 50 to 100 parts of latex, 20 to 40 parts of butyronitrile, 20 to 40 parts of polyvinyl chloride, 10 to 20 parts of sulfur, 10 to 20 parts of a conductive outer layer, 30 to 60 parts of a leather material, 10 to 20 parts of an anti-static PC (Polycarbonate) board, 20 to 40 parts of carbon black, 20 to 40 parts of mica powder, 5 to 10 parts of a de-foaming agent, 10 to 20 parts of wool fat, 10 to 20 parts of an accelerant, 10 to 20 parts of an anti-aging agent and 5 to 10 parts of a thickening agent. The preparation method comprises the following steps: S1, firstly, adding latex, butyronitrile, polyvinyl chloride, sulfur and a leather material into a stirrer, stirring and mixing according to fixed time, obtaining a first mixture after mixing is finished, meanwhile, putting the first mixture into a standing box, standing, and mixing, so as to obtain a second mixture; the antistatic high-cleanliness latex glove is good in antistatic capacity, long in service life, convenient to produce and convenient to popularize and use.

Description

technical field [0001] The invention relates to the technical field of latex gloves, in particular to an antistatic high-clean latex glove and a preparation method thereof. Background technique [0002] Latex gloves are a kind of gloves. They are different from ordinary gloves and are made of latex. It can be used in household, industrial, medical, beauty and other industries. It is an essential hand protection product. It is made of natural latex and other fine additives. The product is specially treated and comfortable to wear. It is widely used in industrial and agricultural production, medical treatment and daily life. [0003] The latex gloves in the prior art have poor antistatic properties, and at the same time, after a long period of use, the latex gloves are easily damaged and are not conducive to use, so we propose an antistatic high-clean latex glove and its preparation method for solving the questions raised above Contents of the invention [0004] Based on ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L21/02C08L9/02C08L27/06C08L69/00C08L91/00C08K3/06C08K3/04C08K3/34C08K5/39C08K5/09C08K5/101C08K5/521C08K5/05A41D19/015
CPCC08L21/02A41D19/0062A41D2500/52C08L2201/04C08K2201/017C08L9/02C08L27/06C08L69/00C08L91/00C08K3/06C08K3/04C08K3/34C08K5/39C08K5/09C08K5/101C08K5/521C08K5/05
Inventor 江文养
Owner 南京瑞润新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com