Manufacturing method of self-leveling mortar terrace

A technology of self-leveling mortar and production method, which is applied in the direction of floors, coatings, polyurea/polyurethane coatings, etc., which can solve the problems of uneven surface covering and restricting large-scale use, so as to enhance fluidity and accelerate supersaturated crystallization speed , the effect of shortening the coagulation time

Active Publication Date: 2022-07-29
江苏砺彩砂品新材料有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, because its construction technology is mainly manual operation, its quality is greatly affected by human factors. The common quality problems that are difficult to overcome such as uneven surface, hollowing, cracks, and sanding cover up its own advantages and limit its large-scale use. Floor material is a new type of ground material, which is suitable for the maintenance and renovation of new ground engineering or ground engineering, and it requires mortar to have good fluidity, fast solidification speed, and high strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A method for making a self-leveling mortar floor, comprising the following steps:

[0038] Step 1: Prepare the following raw materials in parts by weight: 100 parts of epoxy resin, 10 parts of dibutyl phthalate, 60 parts of acetone, 8 parts of ethylenediamine and 60 parts of anionic water-based polyurethane. Dibutyl diformate, acetone, ethylenediamine and anionic water-based polyurethane were added to the reactor, the temperature in the reactor was controlled at 65-75°C, and the stirring speed was 300-500r / min for 30-60min to obtain coating A, the described The category of anionic waterborne polyurethane is sulfonic acid type;

[0039] Step 2: Lay emulsified asphalt on the ground to be constructed, then spread the fine river sand evenly on the emulsified asphalt, and then evenly apply the coating A to obtain an asphalt closed base. The thickness of the emulsified asphalt is 0.85mm, The particle size of the fine river sand is less than 0.125mm, and the uniform coating o...

Embodiment 2

[0058] A method for making a self-leveling mortar floor, comprising the following steps:

[0059] Step 1: Prepare the following raw materials by weight: 102 parts of epoxy resin, 12.5 parts of dibutyl phthalate, 62.5 parts of acetone, 9 parts of ethylene diamine and 62 parts of anionic water-based polyurethane. Dibutyl diformate, acetone, ethylenediamine and anionic water-based polyurethane were added to the reaction kettle, the temperature in the reaction kettle was controlled at 65-75 °C, and the stirring speed was 300-500 r / min for 45 minutes to obtain coating A, the anionic type The category of water-based polyurethane is sulfonic acid type;

[0060] Step 2: Lay emulsified asphalt on the ground to be constructed, then spread the fine river sand evenly on the emulsified asphalt, and then evenly apply the coating A to obtain an asphalt closed base. The thickness of the emulsified asphalt is 1.10mm, The particle size of the fine river sand is less than 0.125mm, and the unifo...

Embodiment 3

[0079] A method for making a self-leveling mortar floor, comprising the following steps:

[0080] Step 1: Prepare the following raw materials by weight: 105 parts of epoxy resin, 15 parts of dibutyl phthalate, 65 parts of acetone, 10 parts of ethylenediamine and 65 parts of anionic water-based polyurethane. Dibutyl diformate, acetone, ethylenediamine and anionic water-based polyurethane were added to the reaction kettle, the temperature in the reaction kettle was controlled at 65-75 °C, and the stirring speed was 300-500 r / min for 60 minutes to obtain coating A, the anionic type The category of water-based polyurethane is sulfonic acid type;

[0081] Step 2: Lay emulsified asphalt on the ground to be constructed, then spread the fine river sand evenly on the emulsified asphalt, and then evenly apply coating A to obtain an asphalt closed base. The thickness of the emulsified asphalt is 1.15mm, The particle size of the fine river sand is less than 0.125mm, and the uniform coati...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a manufacturing method of a self-leveling mortar terrace, which comprises the following steps: step 1, preparing the following raw materials in parts by weight: 100-105 parts of epoxy resin, 10-15 parts of dibutyl phthalate, 60-65 parts of acetone, 8-10 parts of ethylenediamine and 60-65 parts of anionic waterborne polyurethane; the preparation method comprises the following steps: adding epoxy resin, dibutyl phthalate, acetone, ethidene diamine and anionic waterborne polyurethane into a reaction kettle, and stirring for 30-60 minutes under the conditions that the temperature in the reaction kettle is controlled to be 65-75 DEG C and the rotating speed is controlled to be 300-500 r / min, so as to obtain a coating A; according to the invention, the pH value is adjusted, so that the raw material of the self-leveling mortar layer can obtain very high strength in the early stage, the raw material of the self-leveling mortar layer is constructed on the asphalt closed base layer, is coated with paint for three times, and is matched with fine river sand, so that capillary pores in the surface of emulsified asphalt can be filled, the closed base layer is formed, and the problem of moisture regain is avoided.

Description

technical field [0001] The invention belongs to the technical field of self-leveling mortar, and in particular relates to a manufacturing method of a self-leveling mortar floor. Background technique [0002] Cement floor and concrete floor are the most widely used traditional floors in my country's building floors. They are famous for their bright surfaces, durability and wear resistance. However, because its construction technology is mainly manual operation, its quality is greatly affected by human factors, and the insurmountable common quality problems such as uneven surface, hollowing, cracks, and sanding cover up its own advantages and limit its large-scale use. Floor material is a new type of ground material, which is suitable for the maintenance and renovation of new ground engineering or ground engineering, and it requires the mortar to have good fluidity, fast solidification speed, and high strength. SUMMARY OF THE INVENTION [0003] The purpose of the present in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/26C04B28/06E04F15/12C09D163/00C09D175/04C09D7/63C04B41/63C04B41/65
CPCC04B26/26C04B28/06E04F15/12C09D163/00C09D7/63C04B41/63C04B41/009C04B41/4884C04B41/65C04B41/5049C04B2201/50C08L75/04C08K5/17C04B14/068C04B18/08C04B18/141C04B18/146C04B7/12C04B2103/302C04B2103/465C04B24/2641C04B2103/24C04B40/0039C04B2103/0057C04B2103/50C04B22/064C04B41/4853C04B41/463C04B41/5041C04B41/5035C04B41/5031C04B41/4961C04B41/4892C04B41/4905
Inventor 张纯赵筛荣蔡晓娟
Owner 江苏砺彩砂品新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap