Technological process of forming composite silicon carbide ceramic material based on pyrolysis of photocured prototype

A technology of silicon carbide ceramics and composite materials, which is applied in the field of silicon carbide ceramic composite material forming technology based on photocuring prototype pyrolysis, can solve problems such as difficulty in meeting requirements, poor plasticity of silicon carbide materials, plastic forming parts, etc. The effect of high development speed and dimensional accuracy

Inactive Publication Date: 2006-04-26
XI AN JIAOTONG UNIV
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The traditional preparation process is to make green bodies from powder raw materials, and then sinter them at high temperature to manufacture components. The green bodies made by this method cannot meet the requirements in terms of dimensional accuracy and shape complexity.
At present, the most commonly used method is plastic molding of powder, but it has high requirements on the rheological properties of raw materials, and silicon carbide materials have poor plasticity, and it is difficult to plastically form complex and precise parts.
The recent method of using wood, natural fibers, etc. as organic templates for in-situ conversion to prepare silicon carbide ceramic parts is difficult to meet the requirements due to the uneven structure of natural wood or fibers and large individual differences.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Technological process of forming composite silicon carbide ceramic material based on pyrolysis of photocured prototype
  • Technological process of forming composite silicon carbide ceramic material based on pyrolysis of photocured prototype
  • Technological process of forming composite silicon carbide ceramic material based on pyrolysis of photocured prototype

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] see figure 1 , process step of the present invention comprises:

[0020] 1. 3D model design step, according to actual requirements, use Pro / E software to construct the 3D data model of the workpiece, such as figure 2 shown; and figure 2 The model shown is stored as an STL format file;

[0021] 2. Use the layering software that comes with the light-curing rapid prototyping machine to do layering processing, and import the processing data into the manufacturing program;

[0022] 3. Manufacture the resin prototype on the photocuring rapid prototyping machine; the above steps are mature technologies in this field.

[0023] 4. Put the resin prototype obtained by photocuring into a crucible, put it into a vacuum high-temperature furnace for carbonization, heating rate: 100°C / h, carbonization temperature: 600°C, holding time: 4h, then cool to room temperature with the furnace and take it out. Get the three-dimensional carbon support of the workpiece, such as image 3 sh...

Embodiment 2

[0027] The difference between this example and Example 1 is that in step 4, the carbonization temperature is 500°C, and the holding time is 5h; in step 5, the Si powder particle size is 50 μm, the reaction temperature is 1500°C, and the holding time is: 1h, all the other are the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention proposes a silicon carbide ceramic composite molding process based on light-curing prototype pyrolysis, and its basic principle is the combination of light-curing rapid prototyping technology and reaction sintering silicon carbide technology. The main process method is to use liquid photosensitive resin as the raw material for the molding of the part, and make a prototype through the photocuring rapid prototyping process to provide an organic template for the shape and internal structure of silicon carbide ceramics, and convert it into an inorganic template through a pyrolysis process—three-dimensional carbon stand. Then carry out high-temperature siliconizing, and silicon reacts in situ on the carbon support to form silicon carbide ceramics and its composite material components. The method changes the traditional ceramic component preparation process, overcomes the shortcomings of the traditional process that it is difficult to manufacture ceramic parts with complex shapes and precise dimensions, and realizes the moldless precision manufacturing of silicon carbide ceramics.

Description

technical field [0001] The invention relates to a new technology for ceramic parts, in particular to a silicon carbide ceramic composite material molding method based on light-cured prototype pyrolysis with complex shape and high dimensional accuracy. Background technique [0002] Silicon carbide ceramic material is one of the most important high-performance engineering ceramic materials, and its parts are widely used and urgently needed in petrochemical, aerospace, national defense and military industries. The traditional preparation process is to make green bodies from powder raw materials, and then sinter them at high temperature to manufacture components. The green bodies made by this method cannot meet the requirements in terms of dimensional accuracy and shape complexity. At present, the most commonly used method is plastic molding of powder, but it has high requirements on the rheological properties of raw materials, and silicon carbide materi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/565C04B35/634C04B35/622
Inventor 李涤尘乔冠军崔志中
Owner XI AN JIAOTONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap