High temperature luminous glazing and its production process and application in luminous glazed tile

A processing technology, luminous glaze technology, applied in the production of luminous glaze, the application field of production of luminous tiles, can solve the problems of human body and environmental damage, poor stability, luminous pigment easy to lose light, etc., achieve short light absorption time, strong active effect

Inactive Publication Date: 2007-04-04
梁锋
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Although there are many kinds of luminescent products for warning or prompting at night, they are all inseparable from the most basic luminescent materials, which are mostly sulfide luminescent materials with a small amount of radiation added, so It is easy to produce radioactive pollution; at the same time, due to the existence of sulfur, harmful gases such as sulfur dioxide and other sulfides are often produced during production and use, which will cause damage to the human body and the environment; in addition, sulfide luminescent materials are exposed to light for a long time Easy to decompose, its stability is poor, after long-term use, it cannot maintain a stable illumin

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0024] Example 1 Luminous parameters are measured according to DIN67510, and the brightness at the 10th minute is 202.9mcd / m 2

[0025] 1. The high-temperature luminous glaze is composed of the following components according to weight percentage:

[0026] SrAl 2 O 4 EuDy (alkaline earth aluminate) 50%, SiO 2 40%, Al 2 O 3 6%, CaO2.5%, MgO 1.0%, Fe2O3 0.5%;

[0027] 2. The processing technology of the above-mentioned high temperature luminous glaze includes the following contents:

[0028] A. Mixed grinding

[0029] After mixing the components described in 1 above, place them in a ball mill and grind for 6 hours; and sieve 325 mesh;

[0030] B. High temperature melting

[0031] Place the above mixed and ground luminous glaze on the shuttle furnace of the oxidation isolation device to form a frit. The firing temperature is 800-1000°C and the firing time is 3-6 hours;

[0032] C. Crush for use

[0033] The above luminous glaze frit is crushed into 325 mesh to make powder:

[0034] 3...

Example Embodiment

[0042] Example 2 Luminous parameters are measured according to DIN67510, and the brightness at the 10th minute is 450.2mcd / m 2

[0043] 1. The high-temperature luminous glaze is composed of the following components according to weight percentage:

[0044] SrAl 2 O 4 EuDy (alkaline earth aluminate) 65%, SiO 2 25%, Al 2 O 3 5%, CaO2.5%, MgO 1.0%, Fe 2 O 3 0.5%;

[0045] 2. The processing technology of the above-mentioned high temperature luminous glaze includes the following contents:

[0046] A. Mixed grinding

[0047] After mixing the components described in 1 above, place them in a ball mill for 6 hours and sieved through 325 mesh;

[0048] B. High temperature melting

[0049] Place the above mixed and ground luminous glaze on the shuttle furnace of the oxidation isolation device to form a frit. The firing temperature is 800-1000°C and the firing time is 3-6 hours;

[0050] C. Crush for use

[0051] Crush the above luminous glaze frit into 325 mesh to make powder;

[0052] 3. Ap...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The high temperature luminous glazing consists of SrAl2O4EuDy 50-68 wt%, SiO2 25-40 wt%, Al2O3 4-6 wt%, CaO 1.5-3.0 wt%, MgO 0.5-1.0 wt% and Fe2O3 0.1-0.8 wt%, and is prepared through mixing, grinding, high temperature baking, crushing and other steps. It may be used in producing luminous glazed tile. It contains no any matter harmful to human body, produces no any harmful matter during use and has no harm to human body and environment. The luminous glazed tile has short light absorbing time, long afterglow time and high adaptability to weather and environment.

Description

technical field [0001] The invention relates to a luminous material technology, in particular to a luminous glaze production technology and its application in the production of luminous ceramic tiles. Background technique [0002] Although there are many kinds of luminescent products for warning or prompting at night, they are all inseparable from the most basic luminescent materials, which are mostly sulfide luminescent materials with a small amount of radiation added, so It is easy to produce radioactive pollution; at the same time, due to the existence of sulfur, harmful gases such as sulfur dioxide and other sulfides are often produced during production and use, which will cause damage to the human body and the environment; in addition, sulfide luminescent materials are exposed to light for a long time It is easy to decompose, and its stability is poor. After long-term use, it cannot maintain a stable illuminance. [0003] In addition, most of the above-mentioned existi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C8/02C04B33/34C09K11/64B44C1/16
Inventor 梁锋林同润
Owner 梁锋
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap