A technology of supercapacitors and modification methods, applied in capacitors, capacitor manufacturing, circuits, etc., can solve the problems of narrow electrochemical window, affecting the weight specific energy characteristics of carbon-based supercapacitors, and low capacitance

Inactive Publication Date: 2004-03-17
江苏隆源双登电源有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

All kinds of activated carbon produced in China are usually obtained by thermal decomposition of coconut shell, coal, wood and some organic polymers in a non-oxidative atmosphere, and are mainl

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modification method for anode activated charcoal of ultracapacitor
  • Modification method for anode activated charcoal of ultracapacitor
  • Modification method for anode activated charcoal of ultracapacitor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0008] Use one of the above schemes to modify the activated carbon material for the positive electrode of the supercapacitor. The specific surface area of ​​the activated carbon used in the experiment is 1000-1500m 2 / g, the particle size is 200-300 mesh, and it has been pre-treated with sulfuric acid and nitric acid before mixing the paste.

[0009] At room temperature, pretreated activated carbon was mixed with 0.05 mol / l Co(NO 3 ) 2 Vacuum impregnation in the solution at 40°C for 3 hours, suction filtration, and then adding an excess of 9mol / l KOH solution for immersion and alkalization for 1 hour, at this time a layer of nano-scale Co(OH) was deposited in the micropores of the activated carbon. 2 The modified layer was suction-filtered until the pH was less than 7.5, and dried at 100° C. for 6 hours to complete the cobalt modification.

[0010] The activated carbon modified by impregnating cobalt was mixed with 3mol / l Ni(NO 3 ) 2 and 0.09mol / l Co(NO 3 ) 2 Vacuum impr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A process for the modification of activated charcoal material for the use of super capacitor negative electrode, wherein a nanometer level lead phosphate or lead cobalt modification layer is first formed in the activated charcoal micropore, After modification, the capacity of the active compound is increased, the electrochemical window is expanded by about 200 mV, thus improving the weight ratio energy capacity of the charcoal group super capacitor. íí

Description

technical field [0001] The invention relates to a method for modifying an activated carbon material for a positive electrode of a supercapacitor, in particular to a method for modifying an activated carbon material to deposit a cobalt modification layer and a cobalt-nickel composite modification layer, and belongs to the technical field of supercapacitors. Background technique [0002] A supercapacitor is an excellent compact energy source located between batteries and traditional capacitors. It has large energy storage, light weight, large specific capacity, large specific power (1500W / kg), good high-current discharge performance, and fast charging ( It can be several seconds), and the number of cycles is large (in the order of 10 5 Meter), low temperature resistance (-50 ℃), maintenance-free, low pollution and other outstanding advantages, it can be used as an independent power supply or a compound power supply, and is widely used in the fields of starting, traction power,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01G9/042H01G13/00
CPCY02E60/13
Inventor 阎智刚褚德威唐民洪衡建坡管雄俊陈怀林
Owner 江苏隆源双登电源有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap