Low-temperature welding material

A low-temperature solder, weight percentage technology, applied in the direction of welding/cutting media/materials, welding media, welding equipment, etc., can solve the problems of capacitors' poor ability to withstand inrush current and harmonic current, and affect the quality of capacitors

Inactive Publication Date: 2005-12-28
上海上电电容器有限公司
View PDF0 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The ordinary zinc-tin alloy is used, its melting temperature is between 280 and 330°C, and the polypropylene film will be melted during welding, and the combination rate with the aluminum foil is only 70%, which affects the quality of the capacitor, and the loss tangent of the capacitor is 0.04%.
Capacitors have poor ability to withstand inrush and harmonic currents

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Weigh 60 parts of tin, 0.015 part of copper, 0.03 part of lead, 0.03 part of iron, 0.01 part of antimony, 0.01 part of arsenic, 0.005 part of aluminum, 0.005 part of bismuth, 0.003 part of nickel, 0.001 part of cadmium, and 39.891 parts of zinc.

[0022] Put zinc in the heating furnace first, control the temperature at about 400°C, add tin after melting, keep the temperature at 200°C, stir after the tin is melted, and add other metals to obtain the low-temperature solder of the present invention .

Embodiment 2

[0024] Weigh 61.991 parts of tin, 0.015 parts of copper, 0.03 parts of lead, 0.03 parts of iron, 0.01 parts of antimony, 0.01 parts of arsenic, 0.005 parts of aluminum, 0.005 parts of bismuth, 0.003 parts of nickel, 0.001 parts of cadmium, and 37.9 parts of zinc.

[0025] Put zinc in the heating furnace first, control the temperature at about 400°C, add tin after melting, keep the temperature at 200°C, stir after the tin is melted, and add other metals to obtain the low-temperature solder of the present invention .

Embodiment 3

[0027] Weigh 63 parts of tin, 0.015 part of copper, 0.03 part of lead, 0.03 part of iron, 0.01 part of antimony, 0.01 part of arsenic, 0.005 part of aluminum, 0.005 part of bismuth, 0.003 part of nickel, 0.001 part of cadmium, and 36.891 parts of zinc.

[0028] Put zinc in the heating furnace first, control the temperature at about 400°C, add tin after melting, keep the temperature at 200°C, stir after the tin is melted, and add other metals to obtain the low-temperature solder of the present invention .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
Login to View More

Abstract

A low-temp solder for soldering electric capacitors contains Sn (60-64 wt.%), Zn (35.891-39.891 wt.%) and the Cu, Pb, Fe, Sb, As, Al, Bi, Ni and Cd (rest). Its advantages are low smelting temp, no damage to polypropene film, and high adhesion to Al foil.

Description

technical field [0001] The invention relates to a solder, in particular to a low-temperature solder. Background technique [0002] At present, the components of the capacitor are in the form of protruding pole plates, using aluminum foil as the pole plate and polypropylene film as the medium. The lead-out of the pole plate is welded by a rotary soldering iron welding process. The ordinary zinc-tin alloy is used, its melting temperature is between 280 and 330°C, and the polypropylene film will be melted during welding, and the combination rate with the aluminum foil is only 70%, which affects the quality of the capacitor, and the loss tangent of the capacitor is 0.04%. . Capacitors have poor tolerance to inrush and harmonic currents. Contents of the invention [0003] In view of the deficiencies in the prior art, the object of the present invention is to provide a low-temperature solder that does not damage the polypropylene film during welding, has a high bonding rate w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B23K35/26
Inventor 傅胜春
Owner 上海上电电容器有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com