Magnesia refractory materials property promotion method and the product produced thereby

A refractory material and magnesia technology, which is applied in the field of improving and improving the technical performance of magnesia refractory materials, and can solve the problems of increasing chromium oxide content, pore diameter, etc.

Inactive Publication Date: 2006-02-08
WUHAN UNIV OF SCI & TECH
View PDF1 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although a solution is proposed, there is no report on how to increase the c

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] Embodiment 1 A method for improving the performance of magnesia-chrome bricks

[0014] A method for improving the performance of magnesia-chrome bricks, the specific steps are as follows:

[0015] 1. Preparation of chromium oxide precursor sol: mix chromium chloride / urea at a molar ratio of 2 to 5 / 5 to 10, prepare a solution with a concentration of 1.0 to 5.0 mol / L with water, and add 0.05 to 0.2 mol / L per liter of solution mol of ethyl acetate, then reacted at 80-95°C for 10-20 hours, and cooled naturally.

[0016] 2. Preparation of magnesia-chromium spinel precursor sol: mix chromium sulfate / magnesium sulfate / urea according to the molar ratio of 2~5 / 2~5 / 5~10, and prepare it with ethanol to a concentration of 1.0~5.0mol / L Add 0.05 to 0.5 mol of polyethylene glycol per liter of the solution, react the solution at 80 to 90°C for 12 to 24 hours, and cool naturally.

[0017] 3. The method to improve the performance of magnesia-chrome bricks: place the magnesia-chrome bri...

Embodiment 2

[0020] Embodiment 2 A method for improving the performance of magnesium-chromium castables

[0021] A method for improving the performance of magnesium-chromium castables, the specific steps are as follows:

[0022] 1. Chromium oxide precursor sol: mix chromium chloride / urea according to the molar ratio of 3~6 / 5~10, and prepare a solution with a concentration of 1.0~5.0mol / L with ethyl acetate, and add 0.02~ 0.1 mol of polyacrylamide, then react at 80-95°C for 10-20 hours, and cool naturally.

[0023] 2. Magnesium chromium spinel precursor sol: mix chromium sulfate / magnesium sulfate / urea according to the molar ratio of 3~6 / 3~6 / 5~10, and prepare the concentration of 1.0~5.0mol with ethanol and water mixed solvent / L of solution, add 0.10-0.8mol of polyglycol per liter of solution, react the solution at 80-90°C for 12-24 hours, and cool naturally.

[0024] 3. The method to improve the performance of magnesia-chrome castables: place the prefabricated parts of magnesia-chrome ca...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for improving technical characteristics of magnesia refractory materials which comprises, placing the magnesia refractory materials into a vacuum plant, vacuum-pumping to -0.05~-0.1MPa, pressure maintaining 1-15 minutes, pumping in chromium-containing precursor nano collosol under vacuum state, pressurizing to 0.1-0.5 MPa, pressure maintaining 1-15 minutes, releasing pressure, taking out magnesia refractory materials, baking and drying 10-72 hours at 100-200 deg. C.

Description

1. Technical field [0001] The invention belongs to the technical field of magnesia refractories. In particular, it relates to a method for improving and enhancing the technical performance of magnesia refractories. 2. Background technology [0002] Magnesia refractories, such as magnesia-chrome refractories, are mainly used in copper smelting furnaces, VOD / AOD furnaces, EAF furnaces, RH dip tubes and rotary kilns (M.K.Haldar, H.S.Tripathi, S.K.Das, A.Ghosh.Effect of compositional variation on the synthesis of magnesite-chrome composite refractory. Ceramics International, 2004, 30: 911-915.), in order to improve the performance of magnesite-chrome refractories, a method of impregnation is proposed. In the selection of impregnation solution materials, magnesium sulfate and magnesium chloride are generally popular at home and abroad. At present, only magnesia-chrome refractory materials for RH dipped pipe lining are impregnated with high-concentration magnesium salt solution ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/66C04B41/60C04B41/65
Inventor 汪厚植邓勇跃赵惠忠顾华志
Owner WUHAN UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap