Recipe of high temperature hard glaze for bone china and bone china producing process

A production process and bone china technology, applied in the field of bone china production technology and high-temperature hard glaze formulation for bone china, can solve the problems of excessive lead in glaze and easy deformation of bone china, and achieve advanced production technology, high resistance to high grinding effect

Inactive Publication Date: 2006-10-18
赵孟冬
View PDF0 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to address the shortcomings of the above-mentioned existing bone china products, to provide a method to solve the problem of excessive lead in bone china glaze, improve the hardness of bone china g

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0006] Implementation mode:

[0007] The following examples further illustrate the present invention:

[0008] A high-temperature hard glaze formula for bone china and a bone china production process. The maximum weight percentage of the material components of the high-temperature hard glaze formulation for bone china is: 15-30% of quartz, 30-50% of feldspar, 3-10% of talc, and 5--- of porcelain powder. 25%, calcium carbonate 5-15%, dolomite 3-10%, kaolin 3-10%, frit 3-8%; the preferred range is 15-25% quartz , Feldspar 35---45%, talc 3---8%, porcelain powder 5--10%, calcium carbonate 10---15%, dolomite 4--9%, kaolin 3--- 8%, frit 3--6%; the best range is: quartz 15%, feldspar 42%, talc 4%, porcelain powder 8%, calcium carbonate 15%, dolomite 5%, kaolin 8%, melting Block 3%. The production process of bone china is as follows: the first step is to prepare a glaze slurry according to the above-mentioned high-temperature hard glaze material components for later use, mix and mix accor...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention is recipe of high temperature hard glaze for bone china and bone china producing process. The recipe of high temperature hard glaze for bone china consists of quartz, feldspar, talc, ceramic powder, calcium carbonate, dolomite, kaolin and clinker. The bone china producing process includes the first step of spraying high temperature hard glaze for bone china in the front face of dried biscuit, supporting the back of the biscuit with sagger to avoid deformation and sintering in kiln at 1270-1280 deg.c; and the second step of spraying low temperature glaze to the back of first sintered piece and sintering for the second time in the glaze kiln at 1050-1160 deg.c. The bone china product of the present invention has high glaze surface hardness, high strength, high heat stability and no lead contained. The present invention is suitable for produce various kinds of household china products.

Description

Technical field: [0001] The invention belongs to the technical field of chemical ceramic materials, in particular to the formula of high-temperature hard glaze for bone china and the production process of bone china. Background technique: [0002] Existing bone china generally adopts high-lead glaze, one-time glazing, one-time glaze firing process, and the produced products contain high lead content, which is harmful to human body, and the glaze surface hardness of ceramic products is poor. The strength of the parts is low, the thermal stability is poor, and the product is easily deformed. Because the amount of lead dissolved in the product exceeds the standard, the export of daily-use ceramic products is greatly restricted. Invention content: [0003] The purpose of the present invention is to address the shortcomings of the above-mentioned existing bone china products, to provide a method to solve the problem of excessive lead in bone china glaze, improve the hardness o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B41/86C03C8/22C04B33/34
Inventor 赵孟冬李素芬李连明赵学仁赵楠李尹
Owner 赵孟冬
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap