Oxygen-scavenging containers having low haze

Inactive Publication Date: 2007-05-03
M&G USA
View PDF7 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

[0013] The iron or other oxygen scavenger is present in an amount sufficient to effectively scavenge oxygen and provide longer shelf life for oxygen-sensitive materials. The particle size of the particle population is optimized to provide effective scavenging activity, while reducing haze.

Problems solved by technology

Foods, beverages, and medicines can deteriorate or spoil if exposed to oxygen.
Using distinct layers of differing materials is not preferred, however, because it adds cost to packaging construction and does not reduce the levels of oxygen already present in the package.
Sachets are generally limited to solid foods, where the sachet can be readily removed from the foodstuff and not accidentally ingested.
Construction of the sachets and the cumbersome nature of their introduction into the package result in increased costs.
However, containers requiring clarity have heretofore been limited to organic type scavengers that maintain their clarity when placed in a separate layer in the wall of the container.
The use of the organic scavenger in a mono-layer or single-layer construction is limited by cost and regulatory constraints due to the nature of the organic scavenger or the by-products of the scavenging reaction.
Contributing to the cost is the logistical problems encountered with the use of organic type scavengers.
A disadvantage of this technique is that the polymer begins reacting with oxygen as soon as the package is made.
However, UV activation techniques are relatively expensive, and the initiators are often not regulated for use in food packaging.
Packages designed for beers and juices are specifically designed to prevent UV penetration, hence UV activation would not be practical for these containers which block UV.
The use of scavenging powders in clear packages has previously been limited by aesthetics, particularly haze and color.
In practice, this means a large number of small particles.
Unfortunately, previous attempts at preparing resin compositions comprising high levels of small particles of iron for use in clear packages have resulted in packages with poor optical properties.
Haze values for these bottles are generally high, and clarity is lacking.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] The present invention is directed to a container and a container wall. The wall includes a populated area comprising a film-forming polymer. Suitable thermoplastic polymers for use in the present invention include any thermoplastic homopolymer or copolymer. Examples of thermoplastic polymers include polyamides, such as nylon 6, nylon 66 and nylon 612, linear polyesters, such as polyethylene terephthalate, polybutylene terephthalate, polytrimethylene terephthalate, and polyethylene naphthalate, branched polyesters, polystyrenes, polycarbonate, polyvinyl chloride, polyvinylidene dichloride, polyacrylamide, polyacrylonitrile, polyvinyl acetate, polyacrylic acid, polyvinyl methyl ether, ethylene vinyl acetate copolymer, ethylene methyl acrylate copolymer, polyethylene, polypropylene, ethylene-propylene copolymers, poly(1-hexene), poly(4-methyl-1-pentene), poly(1-butene), poly(3-methyl-1-butene), poly(3-phenyl-1-propene) and poly(vinylcyclohexane). Preferably, the thermoplastic po...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Fractionaaaaaaaaaa
Thicknessaaaaaaaaaa
Percent by massaaaaaaaaaa
Login to View More

Abstract

A container providing effective oxygen-scavenging functionality, while having low haze. The container has at least one wall, wherein the wall comprises a populated area, and wherein the populated area comprises a film-forming polymer; and a population of particles comprising an effective amount of oxygen-scavenging particles, wherein the number of particles of said population does not exceed a concentration of about (6×107 particles÷T) per cubic centimeter of polymer wherein T is the thickness of the populated area in mils; and wherein the wall has a transmission Hunter haze of up to about 1 percent per mil of the container wall.

Description

CROSS-REFERENCE [0001] This application is a continuation of pending application Ser. No. 10 / 195,385 filed Jul. 16, 2002 which is a continuation in part of Ser. No. 09 / 916,671, filed on Jul. 26, 2001 which is now U.S. Pat. No. 6,780,916 all of which are incorporated by reference in their entirety.BACKGROUND OF THE INVENTION [0002] Thermoplastic resins such as polyethylene terephthalate (PET) are commonly used to manufacture packaging materials. PET processed under the right conditions produces high strength articles with excellent gas barrier properties. Foods, beverages, and medicines can deteriorate or spoil if exposed to oxygen. To improve shelf life and flavor retention of products such as foods, beverages, and medicines, therefore, the barrier protection provided by PET is often supplemented with additional layers of packaging material or with the addition of oxygen scavengers. [0003] Adding a layer of gas barrier film is known as passive-barrier packaging. Ethylvinyl alcohol (...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08K3/10B65D1/00B65D1/34B65D1/09B65D30/02B65D65/02B65D65/40B65D81/24B65D81/26C08G63/78C08J3/22C08J5/00C08K3/00C08K3/08C08K3/22C08K3/24C08K3/34C08K5/34C08K9/00C08L67/00C08L67/02
CPCB65D81/266C08J3/226C08J2467/00C08K3/22C08K3/34B29C55/02C08J3/203C08K3/08C08J2367/02C08K2201/005B29C48/288B29C48/023Y10T428/1355Y10T428/1359Y10T428/1397Y10T428/1352C08L67/02
InventorLECKONBY, ROYTUNG, DEBORAH SNELLSISSON, EDWIN A.
OwnerM&G USA