Piezoelectric Element and Method for Manufacturing the Piezoelectric Element

Inactive Publication Date: 2008-10-16
MURATA MFG CO LTD
View PDF2 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

[0026]The method according to the present invention produces a piezoelectric element including a piezoelectric ceramic body containing an internal electrode. The method includes the step of preparing a piezoelectric ceramic material mainly containing a perovskite complex oxide containing an alkali metal niobate-based compound and forming the piezoelectric ceramic material into compacts having a predetermined shape, the step of applying an electroconductive paste for forming the

Problems solved by technology

It is difficult to universally give a reduction resistance to PZT compounds, and besides they can be reduced by firing in a reducing atmosphe

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Piezoelectric Element and Method for Manufacturing the Piezoelectric Element
  • Piezoelectric Element and Method for Manufacturing the Piezoelectric Element
  • Piezoelectric Element and Method for Manufacturing the Piezoelectric Element

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0063]K2CO3, Na2CO3, and Nb2O5 were prepared as ceramic raw materials and were weighed out so as to prepare a piezoelectric ceramic composition whose main constituent was expressed by a compositional formula (K0.5Na0.5)NbO3.

[0064]Then, the weighed material was placed together with ethanol in a ball mill containing PSZ and was wet-mixed for about 4 hours. After being dried, the mixture was calcined at a temperature of 700 to 900° C. to yield a calcined material.

[0065]Then, 100 parts by weight of the calcined material, 10 parts by weight of vinyl acetate resin as a binder, and 100 parts by weight of water were placed in a ball mill containing PSZ, and a an appropriate amount of plasticizer was further added. The materials were wet-mixed for 4 hours and thus a ceramic slurry was prepared.

[0066]The ceramic slurry was formed into a compact by a doctor blade method. The compact was cut into a plurality of ceramic green sheets of 10 mm in length, 10 mm in width, and 50 μm in thickness.

[006...

example 2

[0074]A test piece of Example 2 was prepared in the same manner and the same procedure as in Example 1 except that K2CO3, Na2CO3, Li2CO3, and Nb2O5 were prepared as ceramic raw materials and were weighed out so as to prepare a piezoelectric ceramic composition whose main constituent was expressed by a compositional formula (K0.475Na0.475Li0.05)NbO3. The firing was performed at 1050° C. for 2 hours.

example 3

[0075]A test piece of Example 3 was prepared in the same manner and the same procedure as in Example 1 except that K2CO3, Na2CO3, Li2CO3, Nb2O5, and Ta2O5 were prepared as ceramic raw materials and were weighed out so as to prepare a piezoelectric ceramic composition whose main constituent was expressed by a compositional formula (K0.5Na0.5) (Nb0.9Ta0.1)O3. The firing was performed at 1050° C. for 2 hours.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Temperatureaaaaaaaaaa
Temperatureaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

A piezoelectric element includes a piezoelectric ceramic body containing an internal electrode. The piezoelectric ceramic body is mainly made of a perovskite complex oxide containing an alkali metal niobate-based compound containing at least one element selected from among K, Li, and Na. The internal electrode is made of a base metal material, such as Ni or Cu. The piezoelectric element is produced by co-sintering the internal electrode and the piezoelectric ceramic body. Thus, there is provided an inexpensive piezoelectric element that can be properly used in practice even though it has been fired in a reducing atmosphere.

Description

CROSS REFERENCE TO RELATED APPLICATIONS [0001]The present application is a continuation of International Application No. PCT / JP2005 / 023247, filed Dec. 19, 2005, which claims priority to Japanese Patent Application No. JP2005-086102, filed Mar. 24, 2005, the entire contents of each of these applications being incorporated herein by reference in their entirety.FIELD OF THE INVENTION[0002]The present invention relates to piezoelectric elements, and more specifically to a monolithic piezoelectric element including a piezoelectric ceramic body containing an internal electrode and a method for manufacturing the piezoelectric element.BACKGROUND OF THE INVENTION[0003]A variety of piezoelectric elements are increasingly used in electronic apparatuses as the electronic technology is being developed. Among such piezoelectric elements, monolithic piezoelectric elements are manufactured as below.[0004]First, a piezoelectric ceramic raw material is prepared by a known solid-phase synthesis, and c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01L41/187H01L41/24C04B35/00H01L41/09H01L41/273H01L41/39H01L41/43H02N2/18H03H3/02H03H9/17
CPCC01G33/006Y10T29/49163C01P2006/32C01P2006/40C04B35/491C04B35/493C04B35/495C04B2235/3201C04B2235/3203C04B2235/3208C04B2235/3251C04B2235/6025C04B2235/652C04B2235/656C04B2235/6582H01L41/083H01L41/1873H01L41/273H03H9/178Y10T29/42C01P2002/34H10N30/8542H10N30/50H10N30/053
Inventor KIMURA, MASAHIKOSHIRATSUYU, KOSUKETAKEDA, TOSHIKAZUWADA, NOBUYUKI
Owner MURATA MFG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap