Natural travertine-imitated ceramic brick and making method

A porcelain tile, imitation of natural technology, applied in the field of porcelain tile production, can solve the problems of affecting the decorative effect, the effect is not natural enough, and the price is high

Inactive Publication Date: 2008-12-03
霍镰泉
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] On the other hand, the decorative effect of natural stone is generally loved by people. For example, the decorative effect shown by travertine is unique in wall decoration, but natural travertine is expensive and limited in resources, while artificially produced travertine At present, wall tiles can only be manufactured by mold, so the effect is not natural enough, and the holes are too regular, which affects the decorative effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Natural travertine-imitated ceramic brick and making method

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0026] White material formula (No. CB-13):

[0027] Raw material name Proportion (%)

[0028] Ball soil 1# 16

[0029] Ball soil 2# 9

[0030] Albite 1# 10

[0031] Albite 2# 17

[0032] Albite 3# 16

[0033] Potassium feldspar 1# 3

[0034] Potassium feldspar 2# 3

[0035] Potassium feldspar 3# 7

[0036] High temperature sand 1# 9

[0037] High temperature sand 2# 5

[0038] High temperature sand 3# 3

[0039] burnt talc 2

[0040] Total 100

[0041] Foaming material formula (No. QP-01):

[0042] Raw material name Proportion (%)

[0043] Lithium feldspar 38

[0044] limestone 17

[0045] Polishing slag 12

[0046] Albite 2# 22

[0047] Ball soil 1# 10

[0048] burnt talc 1

[0049] Total 100

[0050] The actual chemical composition of the above two formulations is shown in Table 4.

[0051] Table 4 Formula Chemical Composition Table

[0052]

recipe name

SiO 2

al 2 o 3

Fe 2 o 3

TiO 2

...

example 2

[0073] White material formula (No. CB-13).

[0074] Foaming material formula (No. QP-02):

[0075] Raw material name Proportion (%)

[0076] Lithium feldspar 40

[0077] limestone 17

[0078] Polishing slag 5

[0079] Albite 2# 27

[0080] Ball soil 1# 10

[0081] burnt talc 1

[0082] Total 100

[0083] The process parameters of color matching and proportioning are as follows:

[0084] (1), color matching

[0085] Material D: CB-13 (dry material) 100g + 0.6g jade yellow + 3# black material 0.04g + orange red 0.15g

[0086] CB-04 material: CB-13 (dry material) 100 grams + zirconium silicate 2.0 grams

[0087] (two), fabric ratio:

[0088] 1# pipe (1# groove) D material (dark brown material) 10

[0089] 2# pipe (2# groove) D material 20%+CB-0480% (white material) 25

[0090] 3# pipe (3# groove) QP-02 material 5

[0091] 4# pipe (4# tank) D material 70%+CB-0430% (light brown material) 60

[0092] Other parameters are the same as "Example 1".

[0093] It is based ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a ceramic brick to imitate natural cavity stone, which comprises the following parts: 8-15% ball earth, 18-30% sodium feldspar, 30-45% lithium feldspar, 12-20% limestone, 0.5-3% rubber brick material and 0-1% sintered talcum.

Description

technical field [0001] The invention relates to the technical field of porcelain tile production; more specifically, it relates to a porcelain tile with natural travertine style and a preparation method. Background technique [0002] Polished tiles are a very rich category of architectural ceramic products. All products that are sintered and then polished to make their surfaces glossy can be called polished tiles. According to the different production processes before the polishing process, polished tiles can be divided into various types, such as: seepage tiles, magic tiles, micro powder tiles and so on. However, no matter how complicated the changes are, the manufacturing process is not much different, or part of the process is chosen, or multiple processes are mixed. If there are holes and holes in the polished tiles at present, it is generally a substandard product. Therefore, various methods are used to reduce the generation of holes in the existing polished tile produ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/14C04B33/13C04B35/622C04B38/00
Inventor 李深增林斌祝万里
Owner 霍镰泉