Multifunctional slagging material findings and method for producing the same

A multi-functional, slag-making technology, applied in the field of metallurgy, can solve problems such as efficient material utilization, and achieve the effects of saving consumption, reducing total amount, and accelerating chemical reactions

Inactive Publication Date: 2008-05-07
攀钢集团成都钢铁有限责任公司
View PDF0 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most of the existing research and reports focus on the primary utilization

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multifunctional slagging material findings and method for producing the same
  • Multifunctional slagging material findings and method for producing the same
  • Multifunctional slagging material findings and method for producing the same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] The auxiliary material for slagging material of the present invention is characterized in that it is composed of the following components by weight ratio: 8.0-9.5 parts of converter steel slag, 0.5-2.0 parts of additives; wherein, the additives are composed of the following components in weight percentage Composition: Na 2 CO 3 5.00~10.00%, FeO 70.00~80.00%, BaCO 3 10.00~20.00%; the prepared slagging material contains the following components in weight percentage: CaO 32.00~45.00%, FeO 20.00~30.00%, BaCO 3 1.00~4.00%, SiO 2 7.00~12.00%, MgO 7.00~9.00%, Na 2 COx 0.5-2.00%.

[0014] Na in the additive of the present invention 2 CO 3 、BaCO 3 It has the function of dephosphorization, FeO provides oxygen sites, and also has the function of dephosphorization. The additive used in the present invention can comprehensively play the functions of dephosphorization and slagging, and is a new high-quality auxiliary material for slagging materials.

[0015] The slagging ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to a plurality of assistant materials of slagging materials and a preparation method, belonging to metallurgy field, which is characterized in comprising the components in the following weight matching: steel slag of converter 8.0 to 9.5 shares and addition agent 0.5 to 2 shares; wherein, the addition agent comprises the components in the following weight percentage: Na2CO3 is 5.00 to 10.00 percent, FeO is 70.00 to 80.00 percent and BaCO3 is 10.00 to 20.00 percent. The assistant materials of slagging materials can be used in slagging and also used as slugging agent and dephosphorizing agent. The invention achieves the recycle utilization of the steel slag of converter, therefore has the advantages of lowering the amount of waste slag during steel-making, saving the dosages of current slagging material: lime and dolomite and improving the slagging performance, and also has the advantages of slagging rapid, sludging rapid and dephosphorizing effectively. The invention provides a new method to recycle the steel slag of converter for people.

Description

technical field [0001] The invention relates to a multifunctional slagging material auxiliary material and a preparation method thereof, belonging to the field of metallurgy. Background technique [0002] Converter steel slag is one of the "three wastes" of the iron and steel industry. It contains a certain amount of steel scrap and useful component resources such as CaO, FeO, SiO2, and MgO. environmental pollution. The recycling of converter steel slag can reduce the total amount of waste slag in steelmaking plants and save a lot of slagging materials. Therefore, the comprehensive utilization of converter steel slag has been incorporated into an important link in the development of circular economy in the iron and steel industry. [0003] At present, the comprehensive utilization rate of converter steel slag in my country is only 36%, which is mainly used for recycling slag iron, metallurgical raw materials, building materials, and pre-desiliconization and dephosphorizatio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C21C7/00C21C5/36
CPCY02P10/20
Inventor 陈坤黄正全张珉
Owner 攀钢集团成都钢铁有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap