Processing method of pressure vessel forgings

A technology of pressure vessel and processing method, which is applied in the field of forging processing, and can solve the problems of multiple fires, uneven deformation of blanks, and difficulty in compaction, etc.

Active Publication Date: 2012-02-15
WUXI HONGDA HEAVY IND
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the forging process uses more firing times, the defects inside the steel ingot are not easy to compact, the internal deformation of the billet is uneven, dead zones are easy to occur, and the qualified rate of the product is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0007] The processing procedure of the pressure vessel forging is described below in conjunction with the examples:

[0008] For example, a pressure vessel with a diameter of 1410 mm and a height of 400 mm is processed. Calculate the weight according to the size of the pressure vessel forging, estimate the weight of the blank according to the weight, and determine the size of the blank according to the length of the blank H / diameter of the blank D≈2.25. , the unit is mm), according to the blanking diameter, it can be calculated that the anvil width is between 566-735, choose 700 mm, and calculate the time from blank forging to blanking according to the reduction amount of each pull length between 15% and 20%. After eight rounds of elongation and the minimum pier diameter of the blank is 1000 mm, the specific processing process is described below: the blank is heated in a heating furnace, and then the blank pier is thickened to a minimum diameter of 1000 mm; then heated, and th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a processing method for a pressure vessel forging. It can minimize the number of forging fires, effectively compact the internal defects of the steel ingot, and have a high pass rate of the workpiece. For the processing method of pressure vessel forgings, the following relationship must be satisfied between the anvil width W0, the blanking diameter D, and the required minimum elongated diameter (pier diameter) D0: anvil width W0=(0.77~1.0)D, the minimum elongated diameter (Pier thick diameter) D0=1.4D×D / W0; it is characterized in that the length H and diameter D of the blanking are calculated according to the volume of the formed forging, where H / D≈2.25, and the anvil width W0 is selected according to the blanking diameter D , when drawing and forging the billet, the reduction of each drawing is between 15% and 20%. The long diameter (thick diameter of the pier) is D0, and then the original blank is elongated, turned over to reach the blanking size, and then unloaded, and the pier is thickened to the required size, and finally rounded and trimmed.

Description

technical field [0001] The invention relates to the technical field of forging processing, in particular to a processing method of a pressure vessel forging. Background technique [0002] At present, the production of forgings in the industry generally adopts several times of compaction and several times of elongation or direct elongation. And this forging process used fire time is more, and the defective of steel ingot interior is difficult for compacting, and blank internal deformation is uneven, easily produces dead zone, and the qualified rate of product is on the low side. Contents of the invention [0003] In view of the above problems, the present invention provides another processing method for pressure vessel forgings, which can minimize the number of forging fires, effectively compact defects inside the steel ingot, and have a high pass rate of workpieces. [0004] Technical scheme of the present invention is such: [0005] Anvil width W 0 , blanking diameter ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B21K21/00B21J5/00B21J5/08
Inventor 张瑞庆张忠明张卫东
Owner WUXI HONGDA HEAVY IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com