Casting blank liquid core length measuring method
A determination method and liquid-phase hole technology are applied in the field of iron and steel continuous casting, which can solve problems such as inability to detect, and achieve the effects of easy operation, favorable promotion and application, and low cost.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0025] Example 1
[0026] The composition of molten steel is (wt%):
[0027] C Si Mn S P Ca [Al]s 0.75 0.21 0.62 0.01 0.009 0.0004 0.0006
[0028] The rest is iron and inevitable impurities.
[0029] The above-mentioned molten steel flows into the mold from the tundish. In the mold, the molten steel is gradually condensed into a primary green shell along the wall of the mould cooled with water around it. Then, the primary solidified shell of the mould is cooled and solidified in the secondary cooling section. And pull it out at a speed of 1.4m / min. At the end of continuous casting, a certain amount of lead tracer was added into the mold while the molten steel in the tundish was stopped. After the tracer fully penetrated to the end of the liquid cavity, the continuous casting billet was pulled out. The billet is a square billet.
[0030] The billet is then inspected. If the problem of difficult operation is not considered, the cross-sectional view o...
Example Embodiment
[0033] Example 2
[0034] The composition of molten steel is: (wt%):
[0035] C Si Mn S P Cu [Al]s 0.143 0.222 0.499 0.015 0.012 0.033 0.0014
[0036] The rest is iron and inevitable impurities.
[0037] The above-mentioned molten steel flows into the mold from the tundish. In the mold, the molten steel is gradually condensed into a primary green shell along the wall of the mould cooled with water around it. Then, the primary solidified shell of the mould is cooled and solidified in the secondary cooling section. And pull it out at a speed of 1.3m / min. At the end of continuous casting, a certain amount of lead tracer was added into the mold while the molten steel in the tundish was stopped. After the tracer fully penetrated to the end of the liquid cavity, the continuous casting billet was pulled out. The billet is a slab.
[0038] The detection method of this embodiment is to intercept a blank sample of a certain length, and cut the blank sample lo...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap