Method for processing coloured foreign fiber burnt-out fabric

A processing method and burnt-out technology, applied in the field of knitted fabric processing, can solve the problems of impossibility and single layered feeling, and achieve the effect of ideal warmth retention, clear pattern and good softness

Inactive Publication Date: 2009-05-27
CHANGSHU SHENHUA KNITTING
View PDF2 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although it has the advantages stated in the column of advantages and effects in the last paragraph on page 2 of the specification, the applicant believes that the solution is not enough to make the ready-made fabric full of hazy color effects, and the sense of hierarchy is single, because the formed on the ready-made fabric The patterns and patterns are all made through subsequent additions, that is, produced by artificial processes. More specifically, because the raw materials that make up the garment fabrics do not have the original color, it is impossible to obtain the two colors that people are currently pursuing. Has a sense of layering and has a hazy effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for processing coloured foreign fiber burnt-out fabric
  • Method for processing coloured foreign fiber burnt-out fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] according to figure 1 Process flow shown:

[0032] A) raw material selection, choose 100D / 48F FDY colored polyester filament and 100D / 48F DTY colored polyester network filament as the bottom texture raw material, i.e. bottom yarn, choose 21S ring spinning pure cotton yarn as surface texture raw material, i.e. surface yarn, wherein : The mass percentage that colored polyester filament accounts for is 23%, and the mass percentage that 21S ring-spun pure cotton yarn accounts for is 77%. The pile yarn is located on the two bars of GB1 and GB4, while the GB2 bar uses 100D / 48F

[0033] DTY colored polyester network filaments, 100D / 48F FDY colored polyester filaments for GB3 bar, colored polyester filaments are made of light green, yellow, blue, dark green four colors, the warping machine is warped in strips according to the color needs On the pan head ;

[0034] B) Weaving, put the 100D / 48F FDY colored polyester filament warped by step A), the 100D / 48F DTY colored polyeste...

Embodiment 2

[0044] according to figure 1 Process flow shown.

[0045] A) Raw material selection, choose 100D / 72F FDY colored polyester filament and 150D / 72F DTY colored polyester network filament as the bottom texture raw material, that is, bottom yarn, choose GB1 to use 32S, GB4 to use 16S ring spinning pure cotton yarn as surface texture The raw material is face silk, wherein: the mass percentage that colored polyester filament accounts for is 29%, and the mass percentage that 21S and 16S ring spinning pure cotton yarn accounts for is 71%. 21S ring spun pure cotton yarn is placed on GB1 as raised loop yarn, 16S ring spun pure cotton yarn is placed on GB4 as raised loop yarn, while GB2 uses 150D / 72F DTY colored polyester network filament, and GB3 uses 100D / 72F FDY Colored polyester filaments, colored polyester filaments are made of light green, yellow, blue, orange, and dark green, and are warped on the pan head in strips according to the color requirements of the warping machine;

[0...

Embodiment 3

[0056] according to figure 1 Process flow shown.

[0057] A) Raw material selection, choose 100D / 72F FDY colored polyester filament and 100D / 72F DTY colored polyester network filament as the base material, that is, bottom yarn, choose GB1 to use 16S ring spinning pure cotton yarn, GB4 use 32S ring spinning The pure cotton yarn is used as the raw material of the surface texture, namely the face silk, wherein the mass percentage of colored polyester filament is 24%, and the mass percentage of 21S and 16S ring-spun pure cotton yarn is 76%. Warping machine warping, 16S ring-spun pure cotton yarn is placed on GB1 as a loop yarn, 32S ring-spun pure cotton yarn is placed on GB4 as a loop yarn, and GB2 uses 100D / 72F DTY colored polyester network filament, 100D / 72F FDY colored polyester filaments are used for GB3. The colored polyester filaments are made of dark purple, light purple and pink, and are warped on the pan head in strips according to the color requirements of the warping m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a method for processing color foreign fiber burnt-out fabric. The method comprises the following steps: material selection; first weaving; pile cutting; rinsing; pre-drying; burnt-out print; water washing, softening and dewatering; drying; scalding-shearing; and tailoring. The method is characterized in that: the material selection comprises the selection of covering weave material and the selection of ground weave material; and, the covering weave material is frame spinning purified cotton yarn or viscose glue cotton blended yarn, and the ground weave material is colored terylene filament, wherein the colored terylene filament is 23 to 40 mass percent, and the frame spinning purified cotton yarn or viscose glue cotton blended yarn is 60 to 77 mass percent. The method has the advantages that: because the colored terylene filament is selected as the ground weave, and the frame spinning purified cotton yarn or viscose glue cotton blended yarn is selected as the covering weave, after burnt-out print, the fabrics can achieve the effects of clear pattern, reasonable three dimensional appeal and dusky gentleness; moreover, the fabrics also have good softness and ideal heat insulating ability.

Description

technical field [0001] The invention belongs to the technical field of knitted fabric processing, and in particular relates to a method for processing colored foreign fiber burnt-out fabrics. Background technique [0002] At present, the raw materials adopted for knitted fabrics such as single-sided or double-sided cut pile fabrics mainly contain the following three types, one is all polyester; Colors come in several forms: plain, jacquard or printed. As known in the industry, jacquard and printing belong to a traditional craft, and the clarity and three-dimensional effect of the pattern are lacking, and there is no hazy feeling. [0003] Perhaps based on the above reasons, Chinese Invention Patent Application Publication No. CN1995534A recommends a printing process for all cotton imitation burnt-out fabrics. Flat screen printing, and the temperature of the drying room is controlled at 120-160 during printing. After printing, bake at 150-190 for 2-4min. Yet, because the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D04B21/02D04B21/04D04B35/36D06C13/00D06C13/10D06C23/02D06C15/00D06L3/02D06Q1/02D06L4/12D06L4/13
Inventor 顾宝玉
Owner CHANGSHU SHENHUA KNITTING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap