A technology of waste ceramics and porcelain clay, which is applied in the field of ceramics, can solve the problems of unused and popularized waste ceramics, and achieve the effects of reducing component types, saving production costs, and good plasticity

Inactive Publication Date: 2010-05-05
广东文化长城集团股份有限公司
View PDF0 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the utilization of waste porcelain in sanitary ceramics and daily-use ceramics has begun, but it has not been popularized in ceramic production areas; and a large number of waste ceramics have not yet been utilized

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing petuntse from waste ceramics
  • Method for producing petuntse from waste ceramics

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] The present invention will be described in detail below through examples.

[0022] Take waste ceramics, crush and ball mill, and then sieve to make waste ceramic particles with a fineness of ≤50 μm for use; by weight of waste ceramics 45%, quartz 8%, feldspar 10%, machine mud 15%, kaolin 22% Percentage Quartz, feldspar, mechanical mud, kaolin and the above-mentioned spare waste ceramic particles are mixed and put into a ball mill, mixed and ball milled for 30 hours to make mud, and the fineness of the ball mill is controlled to be less than 0.2% after passing through a 325 mesh sieve; After the above mud is screened, iron-removed, press-filtered and mud-smelted, porcelain clay is obtained.

[0023] Use the porcelain clay prepared above to produce decorative art ceramics. The porcelain clay has good plasticity, and the cracking and damage of the body formed by grouting is less than 5%; it is fired in the temperature range of 1230-1250 ° C, the firing condition is good, a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for producing petuntse from waste ceramics, which comprises the following producing steps: taking the waste ceramics, pulverizing and ball milling, and then, sieving to obtain waste ceramic particles for standby, wherein the fineness of each ceramic particle is less than or equal to 50mu m; according to the percentage by weight, taking 7-12% of quartz, 8-13% of feldspar, 15-20% of mechanical pounded pug and 20-30% of kaolin to be uniformly mixed with 40-50% of waste ceramic particles for standby, putting the mixture in a ball mill for mixing and ball milling for 25-35 hours to obtain pug, wherein the ball milling fineness is controlled over 325 meshes, and the sieve residue is less than 0.2%; and sieving, de-ironing, filter-pressing and pugging the pug to obtain the petuntse. In the invention, by controlling the fineness of the petuntse, the plasticity of the petuntse is improved to meet the production requirements, the produced petuntse has good plasticity, the component types needed by producing the petuntse are reduced, various ceramic and porcelanic wastes can be recycled, and compared with the traditional method, the production cost of the method of the invention is greatly saved.

Description

technical field [0001] The invention relates to the field of ceramics, in particular to a method for making porcelain clay from waste ceramics. Background technique [0002] my country is a big country producing ceramics in the world, and hundreds of thousands of tons of waste ceramics are produced in production every year. Since waste ceramics have been sintered or fired at high temperatures, they cannot be degraded in natural environmental conditions, and they are discarded in farmland, mountains, roadsides, etc., causing serious pollution to the environment. Prior to this, because the recycling of waste ceramics was only for porcelain waste products, a large number of ceramic waste products were not used, and the technology was not popularized, and the processing cost of waste porcelain was high, resulting in the vast majority of ceramic manufacturers discarding waste ceramics instead of Cause waste of resources and serious environmental pollution. [0003] Due to the a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/02
Inventor 蔡廷祥安鹤芹赵立泉任锋
Owner 广东文化长城集团股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com