Super-tough nylon alloy

A nylon and alloy technology, applied in the field of engineering plastic modification, can solve the problems of poor low temperature resistance, high water absorption, poor impact resistance, etc.

Inactive Publication Date: 2012-05-23
BEIJING UNIV OF CHEM TECH
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Nylon has outstanding performance in terms of bending strength, wear resistance, creep resistance, electrical properties, etc., but most nylon varieties have poor impact resistance, especially low temperature resistance, and high water absorption. Therefore, it is limited its application in many ways

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Super-tough nylon alloy
  • Super-tough nylon alloy
  • Super-tough nylon alloy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The mass percent is nylon 6665%, itaconic acid grafted ethylene-α-octene copolymer 35%, antioxidant 10100.25%, antioxidant 1680.25%, lubricant TAF0.5%, in a high mixer at room temperature After mixing evenly in the state, put the material into the twin-screw extruder, the extrusion temperature is 260-280°C, the main engine speed is 300r / min, after traction, cooling, pelletizing, the pellets are vacuum dried at 80°C for 8 Hour.

Embodiment 2

[0023] The mass percentage is nylon 66 70%, itaconic acid grafted ethylene-α-octene copolymer 30%, antioxidant 1010 0.25%, antioxidant 168 0.25%, lubricant TAF 0.5%, in the high mixer After mixing evenly at room temperature, put the material into the twin-screw extruder, the extrusion temperature is 260-280°C, the main engine speed is 300r / min, after traction, cooling, pelletizing, the pellets are at 80°C Dry under vacuum for 8 hours.

Embodiment 3

[0025] The mass percent is nylon 66 75%, itaconic acid grafted ethylene-α-octene copolymer 25%, antioxidant 1010 0.25%, antioxidant 168 0.25%, lubricant TAF 0.5%, in the high mixer After mixing evenly at room temperature, put the material into the twin-screw extruder, the extrusion temperature is 260-280°C, the main engine speed is 300r / min, after traction, cooling, pelletizing, the pellets are at 80°C Dry under vacuum for 8 hours.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses a super-tough nylon alloy, which is characterized by comprising raw material by weight percent: 65-90% of nylon, 10-35% of itaconic acid grafting ethylene-alpha-octylene copolymer (POE-g-ITA), 0.1-1% of antioxygen, 0.2-1% of lubricating agent, TAF. A method for preparing the super-tough nylon alloy is characterized by comprising the following steps: placing all raw material into a high mixer and mixing the raw materials for 5-10min; then placing the mixed raw materials into a double screw extrusion machine for extrusion and pelleting; carrying out traction, cooling andgrain-sized dicing, finally drying the grain material; wherein main engine speed is 200-400r / min, temperature is 250-280 DEG C. The invention aims to prepare a novel super-tough nylon material which can be widely applied to the fields such as automobiles, electric products, office appliances and constructional engineering.

Description

technical field [0001] The invention relates to a super-tough nylon alloy blended with itaconic acid grafted ethylene-α-octene copolymer, which can be applied to the fields of automobiles, electronic appliances, office appliances, construction engineering and the like, and belongs to the technical field of engineering plastic modification. Background technique [0002] Polyamide (commonly called nylon) is one of the engineering materials with the largest output, the most varieties, the widest application and excellent comprehensive performance among the five general-purpose engineering plastics. It can be widely used in automobiles, electronic appliances, office appliances, construction projects, etc. . Nylon has outstanding performance in terms of bending strength, wear resistance, creep resistance, electrical properties, etc., but most nylon varieties have poor impact resistance, especially low temperature resistance, and high water absorption. Therefore, it is limited it...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L77/00C08L77/06C08L77/02C08L51/06C08K5/134C08K5/526C08K5/20B29B9/06B29C47/92B29C48/40B29C48/92
CPCB29C48/92B29C2948/92704B29C48/04B29C48/40B29C2948/9259B29C2948/92885B29C2948/92895
Inventor 王克俭王小黎
Owner BEIJING UNIV OF CHEM TECH
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com