A technology of golf head and welding method, which is applied in the field of titanium alloy processing, can solve the problems of welding breakage, welding concave, high proportion of shrinkage cavity and leakage, and achieve good results
Active Publication Date: 2011-12-21
LUOYANG SUNRUI TI PRECISION CASTING
View PDF0 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0007] The technical problem to be solved by the present invention is to provide a welding method of a titanium alloy golf head with a self-fusing edge and its casting, which solves the problem that the existing technology leads to a high proportion of shrinkage cavity leakage after the combined grinding of the Face surface, thus requiring Repair welding again, causing problems such as welding concave, welding breakage and other scrapping
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0022] A welding method for a titanium alloy golf head with a self-fusing edge. When processing the mold, the body part of the golf head mold is reserved with a height of 1.0-1.4mm, a width of 0.2-0.5mm, and a width of R angle of 0.5mm. In this way, the required self-fluxing edge can be formed during pouring; the height of the self-fluxing edge is 1.0-1.4mm, and the width of the self-fluxing edge and the ball head body is 0.3-0.5mm. The width of the R angle where the outer surface meets the self-fusing edge is 0.5mm.
[0023] Take a forged face panel made of titanium alloy, insert it into the face frame of the titanium alloy golf head with self-fusing edge, and then clamp it to the fixture of the MIG / MAG welding machine, use it with the self-fusing edge Welding forgings suitable for the self-fluxing edge of the titanium alloy golf head on the side, adjust the gap between the forged striking surface and the ball head body to make it consistent with the trajectory of the welding...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| height | aaaaa | aaaaa |
| width | aaaaa | aaaaa |
Login to View More
Abstract
The invention introduces a welding method of a titanium alloy golf head with a self-fluxing edge and its casting. A self-fluxing edge with a height of 1.0-1.4 mm is reserved in the body part of the titanium alloy golf head casting, and the self-fluxing edge and The width of the junction of the ball head body is 0.2-0.5mm, the width of the R angle at the junction of the outer surface of the golf head and the self-fluxing edge is 0.5mm, and the welding forgings that are suitable for the self-fluxing edge of the golf head are used for welding, MIG / The width of the weld bead during MAG electric welding is not less than 4mm, and the current is controlled to make the penetration amount reach 1.3-2.5mm. After the application of the present invention, the distance between the shrinkage cavity of the self-fusing edge and the Face frame has changed from about 1.5mm to about 0.5mm. Solder filling, no shrinkage cavity after grinding; popularization and application effect is good.
Description
technical field [0001] The invention relates to a titanium alloy processing technology, in particular to a welding method of a titanium alloy golf head with a self-fusing edge and a casting thereof. Background technique [0002] At present, golf heads are basically made of titanium alloy. The design of golf heads is becoming more and more complicated, and the wall thickness is getting thinner and thinner. This has caused many technical problems for casting technology. [0003] The face of the golf head is also called Face. In the past three years, most titanium alloy golf head face structures have become self-fusing edge structures. This structure replaces the manual feeding action in the welding process, making Standardization of operation has obvious advantages, but this structure has shrinkage cavities of 70% to 100% during grinding after welding, resulting in repair welding, and unevenness and other bad problems during repair welding, resulting in a high scrap rate , th...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Patents(China)
IPC IPC(8): B23K9/173
Inventor 付长浩
Owner LUOYANG SUNRUI TI PRECISION CASTING